Method for formation of patterned resist layer

Radiation imagery chemistry: process – composition – or product th – Imaging affecting physical property of radiation sensitive... – Forming nonplanar surface

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C430S270100, C430S330000

Reexamination Certificate

active

06255041

ABSTRACT:

BACKGROUND OF THE INVENTION
The present invention relates to a method for the formation of a patterned resist layer or, more particularly, to an efficient method for the formation of a very finely patterned resist layer of high fidelity to the photomask pattern having an excellently orthogonal cross sectional profile with high photosensitivity on a substrate surface by using a positive-working chemical-amplification photoresist composition.
As a trend in the manufacturing technology of semiconductor devices and liquid crystal display panels in recent years, extensive investigations are now under way to establish a photolithographic patterning process of a resist layer having a pattern resolution of as fine as 0.25 &mgr;m or even finer by the use of a positive-working chemical-amplification photoresist composition. Turning now to the problem of the light source for the pattern-wise exposure of the photoresist layer to comply with the requirement in the manufacture of semiconductor devices to accomplish finer and finer patterning, a photolithographic patterning technology for obtaining a patterned resist layer of 0.15 to 0.22 &mgr;m fineness by using a KrF excimer laser beam is the current target of the development works.
With an object to comply with the above mentioned requirements, a proposal is made in Japanese Patent Kokai 7-209868 for a positive-working chemical-amplification photoresist composition containing, as the film-forming resinous ingredient, a copolymeric resin consisting of hydroxyl group-containing styrene units, styrene units and tert-butyl (meth)acrylate units in a molar ratio of 40:20:40 or 33:17:50. The there proposed photoresist composition using a copolymeric resin with a relatively small amount of the hydroxyl group-containing styrene units or a relatively large amount of the tert-butyl (meth)acrylate units is not quite satisfactory when an extremely fine patterned resist layer of 0.15 to 0.22 &mgr;m fineness is formed therewith because the cross sectional profile of the patterned resist layer is not fully orthogonal as desired.
In the photolithographic patterning technology, studies have been made on the temperatures in the drying heat treatment or, namely, pre-exposure baking treatment of the coating layer of the photoresist composition as applied to the substrate surface and the post-exposure baking treatment after pattern-wise exposure of the resist layer to light. It is known that the pre-exposure baking treatment is undertaken preferably at a temperature higher than the temperature in the post-exposure baking treatment (see, for example, Journal of Vacuum Science and Technology, 278, March/April, 1991). This teaching, however, is not applicable to various types of photoresist compositions because the studies reported there were conducted by using a positive-working photoresist composition comprising a novolak resin and a polyhydroxystyrene resin of which a part of the hydroxy groups were substituted by tetrahydropyranyl groups, which necessarily had low transmissivity to ultraviolet light giving only a limited critical pattern resolution.
Japanese Patent No. 2688188 teaches a photolithographic patterning method in which the pre-exposure baking treatment is conducted at a temperature not lower than the glass transition temperature of the resinous ingredient by more than about 20° C. but not exceeding the scission temperature of the acid-labile groups and the post-exposure baking treatment is conducted at a temperature of about 110° C. or higher. In this method, however, the temperature of the post-exposure baking treatment is not necessarily lower than the temperature of the pre-exposure baking treatment so as not to attain a pattern resolution of 0.22 &mgr;m or finer.
In recent years, on the other hand, onium salts or, in particular, those containing sulfonate ions as the anion are highlighted as an acid-generating agent used in positive-working chemical-amplification photoresist compositions. Examples of such an onium salt as the acid-generating agent in a positive-working chemical-amplification photoresist composition heretofore proposed include onium salts containing a fluoroalkyl sulfonate ion and having at least one acid-instabilizable group on the phenyl group in the molecule such as 2,2,2-trifluoroethane sulfonic acid (4-tert-butoxyphenyl) diphenyl sulfonium as disclosed in Japanese Patent Kokai 10-7650.
The onium salts having an acid-instabilizable group in the molecule, however, are defective due to their low solubility in the organic solvent of the photoresist solutions to limit the amount thereof in the photoresist solution resulting in a decreased photosensitivity and low storage stability of the photoresist solution. In addition, the acid-instabilizable group is liable to be decomposed when the pre-exposure baking treatment or, namely, heat-drying of the photoresist layer formed by coating is performed at 120° C. or higher eventually to lose the activity as an acid-generating agent.
SUMMARY OF THE INVENTION
The present invention accordingly has an object to provide an efficient method capable of forming a very finely patterned resist layer of high fidelity to the photomask pattern having an excellently orthogonal cross sectional profile by using a positive-working chemical-amplification photoresist composition with high photosensitivity.
Thus, the method of the present invention for the formation of a patterned resist layer on a substrate surface comprises the steps of:
(1) forming, on the surface of a substrate, a coating layer of a positive-working chemical-amplification photoresist composition comprising, as a uniform solution in an organic solvent:
(A) 100 parts by weight of a copolymeric resin consisting of (a) from 50 to 85% by moles of hydroxyl group-containing styrene units, (b) from 15 to 35% by moles of styrene units and (c) from 2 to 20% by moles of acrylate or methacrylate ester units each having a solubility-reducing group capable of being eliminated in the presence of an acid, the total of the molar fractions of the monomeric units (a), (b) and (c) being 100%; and
(B) from 1 to 20 parts by weight of a radiation-sensitive acid-generating agent which is an onium salt containing a fluoroalkyl sulfonate ion having 1 to 10 carbon atoms as the anion;
(2) subjecting the coating layer to a first baking treatment at a temperature in the range from 120° C. to 140° C. for 30 to 150 seconds;
(3) exposing the coating layer pattern-wise to actinic rays;
(4) subjecting the coating layer to a second baking treatment for 30 to 150 seconds at a temperature in the range from 110° C. to 130° C. but lower, by at least 10° C., than the temperature of the first baking treatment in step (2); and
(5) subjecting the coating layer to a development treatment.
In particular, the above mentioned solubility-reducing group capable of being eliminated by interacting with an acid forming the (meth)acrylate ester units in the component (A) is selected preferably from the group consisting of tertiary alkyl groups, 1-alkoxyalkyl groups and acetal groups. Further, the anion forming the onium salt as the component (B) is preferably a nonafluorobutane sulfonate ion.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The base ingredient as the component (A) in the photo-resist composition used in the inventive method is a ternary copolymeric resin consisting of three kinds of the monomeric units including (a) from 50 to 85% by moles of hydroxyl group-containing styrene units, (b) from 15 to 35% by moles of styrene units and (c) from 2 to 20% by moles of acrylate or methacrylate ester units each having a solubility-reducing group capable of being eliminated in the presence of an acid, the total of the molar fractions of the monomeric units (a), (b) and (c) being 100%. In this ternary copolymeric resin as the component (A), the monomeric unit of the first type (a) is a unit derived from a styrene monomer having at least one hydroxyl group in the molecule in order to impart the copolymeric resin with good solubility in an aqueous alkaline solution as the developer

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method for formation of patterned resist layer does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for formation of patterned resist layer, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for formation of patterned resist layer will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2557141

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.