Semiconductor device manufacturing: process – Coating with electrically or thermally conductive material – To form ohmic contact to semiconductive material
Reexamination Certificate
2000-10-05
2003-02-18
Smith, Matthew (Department: 2825)
Semiconductor device manufacturing: process
Coating with electrically or thermally conductive material
To form ohmic contact to semiconductive material
C438S664000, C438S184000, C438S265000, C438S647000, C438S649000, C438S656000, C257S382000, C257S384000, C257S755000, C257S768000, C257S900000
Reexamination Certificate
active
06521529
ABSTRACT:
TECHNICAL FIELD
The present invention relates to the fabrication of semiconductor devices, particularly to self-aligned silicide (salicide) technology, and the resulting semiconductor devices. The present invention is particularly applicable to ultra large scale integrated circuit (ULSI) systems having features in the deep sub-micron regime.
BACKGROUND ART
As integrated circuit geometries continue to plunge into the deep sub-micron regime, it becomes increasingly more difficult to accurately form discreet devices on a semiconductor substrate exhibiting the requisite reliability. High performance microprocessor applications require rapid speed of semiconductor circuitry. The speed of semiconductor circuitry varies inversely with the resistance (R) and capacitance (C) of the interconnection system. The higher the value of the R×C product, the more limiting the circuit operating speed. Miniaturization requires long interconnects having small contacts and small cross-sections. Accordingly, continuing reduction in design rules into the deep sub-micron regime requires decreasing the R and C associated with interconnection paths. Thus, low resistivity interconnection paths are critical to fabricating dense, high performance devices.
A common approach to reduce the resistivity of the interconnect to less than that exhibited by polysilicon alone, e.g., less than about 15-300 ohm/sq, comprises forming a multilayer structure consisting of a low resistance material, e.g., a refractory metal silicide, on a doped polycrystalline silicon layer, typically referred to as a polycide. Advantageously, the polycide gate/interconnect structure preserves the known work function of polycrystalline silicon and the highly reliable polycrystalline silicon/silicon oxide interface, since polycrystalline silicon is directly on the gate oxide.
Various metal silicides have been employed in salicide technology, such as titanium, tungsten, and cobalt. Nickel, however, offers particularly advantages vis-à-vis other metals in salicide technology. Nickel requires a lower thermal budget in that nickel silicide and can be formed in a single heating step at a relatively low temperature of about 250° C. to about 600° C. with an attendant reduction in consumption of silicon in the substrate, thereby enabling the formation of ultra-shallow source/drain junctions.
In conventional salicide technology, a layer of the metal is deposited on the gate electrode and on the exposed surfaces of the source/drain regions, followed by heating to react the metal with underlying silicon to form the metal silicide. Unreacted metal is then removed from the dielectric sidewall spacers leaving metal silicide contacts on the upper surface of the gate electrode and on the source/drain regions. In implementing salicide technology, it was also found advantageous to employ silicon nitride sidewall spacers, since silicon nitride is highly conformal and enhances device performance, particularly for p-type transistors. However, although silicon nitride spacers are advantageous from such processing standpoints, it was found extremely difficult to effect nickel silicidation of the gate electrode and source/drain regions without undesirable nickel silicide bridging and, hence, short circuiting, therebetween along the surface of the silicon nitride sidewall spacers.
Accordingly, there exists a need for salicide methodology enabling the implementation of nickel silicide interconnection systems without bridging between the nickel silicide layers on the gate electrode and the source/drain regions, particularly when employing silicon nitride sidewall spacers on the gate electrode.
DISCLOSURE OF THE INVENTION
An advantage of the present invention is a method of manufacturing a semiconductor device having nickel silicide contacts on a gate electrode and associated source/drain regions without bridging therebetween along insulative sidewall spacers, notably silicon nitride sidewall spacers.
Another advantage of the present invention is a semiconductor device having nickel silicide contacts on a gate electrode and associated source/drain regions without bridging therebetween along insulative sidewall spacers, particularly silicon nitride sidewall spacers.
Additional advantages and other features of the present invention will be set forth in part in the description which follows, and in part will become apparent to those having ordinary skill in the art upon examination of the following or may be learned by practice of the present invention. The advantages of the present invention may be realized and obtained as particularly pointed out in the appended claims.
According to the present invention, the foregoing and other advantages are achieved in part by a method of manufacturing a semiconductor device, the method comprising: forming a silicon gate electrode having opposing side surfaces on a substrate with a gate insulating layer therebetween; forming silicon nitride sidewall spacers on the opposing side surfaces of the gate electrode leaving exposed adjacent surfaces of the substrate; depositing a layer of nickel on the gate electrode and on the exposed substrate surfaces; heating to react the layer of nickel with underlying silicon to form a layer of nickel silicide on the gate electrode and layers of nickel silicide on the exposed surfaces of the substrate; removing unreacted nickel from the silicon nitride sidewall spacers; and treating the silicon nitride sidewall spacer with a high density oxygen plasma (HDP) to oxidize any nickel silicide formed on the spacers.
Another aspect of the present invention is a semiocnductor device comprising: a gate electrode, having opposing side surfaces, and an upper surface, on a semiconductor substrate with a gate insulating layer therebetween; silicon nitride sidewall spacers on the opposing side surfaces of the gate electrod; a layer,containing silicon oxide and silicon oxynitride, on a surface of each silicon nitride sidewall spacer; a layer of nickel silicide on the upper surface of the gate electrode; and a layer of nickel silicide on the substrate surface adjacent each silicon nitride sidewall spacer.
Embodiments of the present invention include treating the silicon nitride spacers thereon, thereby forming a layer, comprising silicon oxide and silicon oxynitride and having a refractive index less than about 1.95, on the silicon nitride sidewall spacers. Embodiments of the present invention also include selectively oxidizing the nickel suicide formed on the sidewall spacers, as well as removing any oxidized layer formed on the nickel silicide source/drain contacts Embodiments of the present invention further include forming an oxide liner on the opposing side surfaces of the gate electrode prior to forming the silicon nitride sidewall spacers, and forming the nickel silicide layers at a temperature of about 400° C. to about 600° C.
Additional advantages of the present invention will become readily apparent to those having ordinary skill in the art from the following detailed description, wherein embodiments of the present invention are described simply by way of illustration of the best mode contemplated for carrying out the present invention. As will be realized, the present invention is capable of other and different embodiments, and its several details are capable of modifications in various obvious respects, all without departing from the present invention. Accordingly, the drawings and description are to be regarded as illustrative in nature, and not as restrictive.
REFERENCES:
patent: 5434109 (1995-07-01), Geissler et al.
patent: 5759906 (1998-06-01), Lou
patent: 5804492 (1998-09-01), Shen
patent: 6001721 (1999-12-01), Huang
patent: 6046089 (2000-04-01), Gardner et al.
patent: 6074921 (2000-06-01), Lin
patent: 6127238 (2000-10-01), Liao et al.
patent: 6129819 (2000-10-01), Shan et al.
patent: 6165915 (2000-12-01), Jang
patent: 6211035 (2001-04-01), Moise et al.
patent: 6217658 (2001-04-01), Orczyk et al.
patent: 6218251 (2001-04-01), Kadosh et al.
patent: 6218275 (2001-04-01), Huang et al.
patent:
Adem Ercan
Huertas Robert A.
Mei-Chu Woo Christy
Ngo Minh Van
Lee Jr. Granvill D
Smith Matthew
LandOfFree
HDP treatment for reduced nickel silicide bridging does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with HDP treatment for reduced nickel silicide bridging, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and HDP treatment for reduced nickel silicide bridging will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3125494