Semiconductor device manufacturing: process – Introduction of conductivity modifying dopant into... – Ion implantation of dopant into semiconductor region
Reexamination Certificate
1999-08-10
2001-02-06
Nelms, David (Department: 2818)
Semiconductor device manufacturing: process
Introduction of conductivity modifying dopant into...
Ion implantation of dopant into semiconductor region
C438S526000
Reexamination Certificate
active
06184111
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to the manufacture of substrates. More particularly, the invention provides a technique including a method and device for cleaving a substrate in the fabrication of a multi-layered substrate for semiconductor integrated circuits, for example. But it will be recognized that the invention has a wider range of applicability; it can also be applied to other substrates for multi-layered integrated circuit devices, three-dimensional packaging of integrated semiconductor devices, photonic devices, piezoelectronic devices, microelectromechanical systems (“MEMS”), sensors, actuators, solar cells, flat panel displays (e.g., LCD, AMLCD), biological and biomedical devices, and the like.
Craftsmen or more properly crafts-people have been building useful articles, tools, or devices using less useful materials for numerous years. In some cases, articles are assembled by way of smaller elements or building blocks. Alternatively, less useful articles are separated into smaller pieces to improve their utility. A common example of these articles to be separated include substrate structures such as a glass plate, a diamond, a semiconductor substrate, and others.
These substrate structures are often cleaved or separated using a variety of techniques. In some cases, the substrates can be cleaved using a saw operation. The saw operation generally relies upon a rotating blade or tool, which cuts through the substrate material to separate the substrate material into two pieces. This technique, however, is often extremely “rough” and cannot generally be used for providing precision separations in the substrate for the manufacture of fine tools and assemblies. Additionally, the saw operation often has difficulty separating or cutting extremely hard and/or brittle materials such as diamond or glass.
Accordingly, techniques have been developed to separate these hard and/or brittle materials using cleaving approaches. In diamond cutting, for example, an intense directional thermal/mechanical impulse is directed preferentially along a crystallographic plane of a diamond material. This thermal/mechanical impulse generally causes a cleave front to propagate along major crystallographic planes, where cleaving occurs when an energy level from the thermal/mechanical impulse exceeds the fracture energy level along the chosen crystallographic plane.
In glass cutting, a scribe line using a tool is often impressed in a preferred direction on the glass material, which is generally amorphous in character. The scribe line causes a higher stress area surrounding the amorphous glass material. Mechanical force is placed on each side of the scribe line, which increases stress along the scribe line until the glass material fractures, preferably along the scribe line. This fracture completes the cleaving process of the glass, which can be used in a variety of applications including households.
Although the techniques described above are satisfactory, for the most part, as applied to cutting diamonds or household glass, they have severe limitations in the fabrication of small complex structures or precision workpieces. For instance, the above techniques are often “rough” and cannot be used with great precision in fabrication of small and delicate machine tools, electronic devices, or the like. Additionally, the above techniques may be useful for separating one large plane of glass from another, but are often ineffective for splitting off, shaving, or stripping a thin film of material from a larger substrate. Furthermore, the above techniques may often cause more than one cleave front, which join along slightly different planes, which is highly undesirable for precision cutting applications.
From the above, it is seen that a technique for separating a thin film of material from a substrate which is cost effective and efficient is often desirable.
SUMMARY OF THE INVENTION
According to the present invention, an improved technique for removing a thin film of material including devices (e.g., transistors, capacitors, resistors, inductors) from a substrate using a controlled cleaving action is provided. This technique allows an initiation of a cleaving process on a substrate using a single or multiple cleave region(s) through the use of controlled energy (e.g., spatial distribution) and selected conditions to allow an initiation of a cleave front(s) and to allow it to propagate through the substrate to remove a thin film of material from the substrate.
In a specific embodiment, the present invention provides a method for fabricating electronic devices. The method includes providing a substrate. The substrate comprises a stressed layer at a selected depth underneath a surface of the substrate. The stressed layer is at the selected depth to define a substrate material to be removed above the selected depth. The stressed layer comprises a deposited layer and an implanted region. The material layer comprises a device layer overlying the stressed layer. The method also includes forming a plurality of integrated circuit devices on the substrate material. The forming comprises a thermal treatment process at a temperature greater than about 400 degrees Celsius, while maintaining a substantially microbubble free implanted region in the stressed layer. A step of providing energy to a selected region of the substrate to initiate a controlled cleaving action at the selected depth in the substrate is also included. The cleaving action is made using a propagating cleave front to free a portion of the material to be removed from the substrate.
Numerous benefits are achieved over pre-existing techniques using the present invention. In particular, the present invention uses controlled energy and selected conditions to preferentially cleave a thin film of material from a donor substrate which includes multi-material sandwiched films. This cleaving process selectively removes the thin film of material from the substrate while preventing a possibility of damage to the film or a remaining portion of the substrate. Accordingly, the remaining substrate portion can be re-used repeatedly for other applications.
Additionally, the present invention uses a relatively low temperature during the controlled cleaving process of the thin film to reduce temperature excursions of the separated film, donor substrate, or multi-material films according to other embodiments. In most cases, the controlled cleaving process can occur at, for example, room temperature, as well as others. This lower temperature approach allows for more material and process latitude such as, for example, cleaving and bonding of materials having substantially different thermal expansion coefficients. In other embodiments, the present invention limits energy or stress in the substrate to a value below a cleave initiation energy, which generally removes a possibility of creating random cleave initiation sites or fronts. This reduces cleave damage (e.g., pits, crystalline defects, breakage, cracks, steps, voids, excessive roughness) often caused in pre-existing techniques. Moreover, the present invention reduces damage caused by higher than necessary stress or pressure effects and nucleation sites caused by the energetic particles as compared to pre-existing techniques.
The present invention achieves these benefits and others in the context of known process technology. However, a further understanding of the nature and advantages of the present invention may be realized by reference to the latter portions of the specification and attached drawings.
REFERENCES:
patent: 3770499 (1973-10-01), Crowe et al.
patent: 3901423 (1975-08-01), Hillberry et al.
patent: 4244348 (1981-01-01), Wilkes
patent: 4539050 (1985-09-01), Kramler et al.
patent: 4727047 (1988-02-01), Bozler et al.
patent: 5213451 (1993-05-01), Frank
patent: 5585304 (1996-12-01), Hayashi et al.
patent: 5611855 (1997-03-01), Wijaranakula
patent: 5643834 (1997-07-01), Harada et al.
patent: 5705421 (1998-01-01), Matsushita et al.
patent: 5714395 (1998-02-01), Bruel
patent: 5755914 (
Cheung Nathan W.
Henley Francois J.
Le Dung
Nelms David
Silicon Genesis Corporation
Townsend and Townsend / and Crew LLP
LandOfFree
Pre-semiconductor process implant and post-process film... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Pre-semiconductor process implant and post-process film..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Pre-semiconductor process implant and post-process film... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2597824