NH3 plasma descumming and resist stripping in semiconductor...

Semiconductor device manufacturing: process – Chemical etching – Combined with the removal of material by nonchemical means

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C438S710000

Reexamination Certificate

active

06455431

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
In general, the present invention relates to a method for removing photoresist from locations on a semiconductor structure where its presence is undesired. One embodiment pertains to a method of removing residual photoresist (descumming) from a surface underlying the photoresist layer after patterning (opening) the photoresist. Another embodiment pertains to a method of removing a patterned photoresist layer from an underlying surface when the patterned photoresist is misaligned from its desired location on the underlying surface.
2. Brief Description of the Background Art
A patterned photoresist layer is often used as a template for pattern etching an underlying layer which functions as a hard mask during the etching of layers which underlie the hard mask. Frequently, the hard mask is formed from an inorganic material such as silicon oxide or silicon nitride (or a combination thereof).
FIG. 1
shows a typical prior art semiconductor structure
100
which includes, from bottom to top, a silicon substrate
102
, overlaid with a layer
104
of an organic-based dielectric material, overlaid with a hard mask layer
106
, and a patterned photoresist layer
108
. After patterning of the photoresist layer
108
, there are often “feet”
110
remaining at the interface between the patterned photoresist layer
108
and the hard mask layer
106
, as shown in FIG.
1
. The presence of these “feet” makes it difficult to maintain control of the critical dimensions of a pattern etched in the hard mask layer
106
(and the critical dimensions of features etched in the organic dielectric layer
104
underlying hard mask layer
106
).
FIG. 2
shows a second prior art semiconductor structure
200
, which may occur as an intermediate structure in a dual damascene process. This structure
200
includes, from bottom to top, a substrate layer
202
, a contact via
210
etched in an organic dielectric layer
204
, a patterned hard mask layer
206
, and a second, patterned photoresist layer photoresist
214
, which was deposited after etching of contact via
210
. Any residual material from the first patterned layer of photoresist (not shown) which was used to pattern hard mask
206
was removed after etching of contact via
210
. Then, an additional layer
214
of photoresist was deposited and patterned in order to provide a template for pattern etching the hard mask layer
206
to provide trenches which connect between contact vias (for example, and not by way of limitation). However, as illustrated in
FIG. 2
, an error occurred during patterning of second photoresist layer
214
, and the opening
216
in second patterned photoresist layer
214
, which was intended to be centered over contact via
210
is misaligned. By this time, considerable expense has been incurred in the formation of the structure
200
shown in
FIG. 2
, and rather than discard the structure
200
, it is desired to remove the misaligned second patterned photoresist layer
214
and to reapply a new photoresist layer.
In the past, since most photoresists are comprised of organic materials, a plasma formed from oxygen (O
2
) gas has been used to remove the “feet”
110
of the kind shown in
FIG. 1
(descumming) and to strip misaligned photoresist from a semiconductor structure of the kind shown in
FIG. 2
(reworking). However, even when a bias voltage is applied to the substrate, etching with O
2
is isotropic. With respect to the structure illustrated in
FIG. 1
, this may cause a change in the critical dimension (an enlargement) of the pattern in patterned photoresist layer
108
by the time the feet
110
are removed. With respect to the structure illustrated in
FIG. 2
, this may cause undercutting of the organic dielectric layer
204
toward its base, as illustrated by the broken lines indicating areas
218
. Also, etching with O
2
is very fast, making it difficult to maintain good control over the amount of photoresist which is removed (or organic dielectric layer which is inadvertently removed).
It would be desirable to provide an effective process for descumming that would not result in a change in the critical dimension of the patterned photoresist. It would also be desirable to provide a method for removal of misaligned patterned photoresist that would not disturb an underlying organic dielectric material.
SUMMARY OF THE INVENTION
We have discovered a method of residual photoresist descumming which does not impact the critical photoresist pattern dimensions. In addition, basically the same etch chemistry can be used to strip misaligned patterned photoresist layers during a rework process without causing significant harm to layers of organic dielectric material which are separated from the misaligned patterned resist layer by an inorganic hard mask layer, or by an organic hard mask layer which is resistant to the etch chemistry of the method. These methods utilize a plasma etch where the plasma is generated from a source gas which is primarily (at least 50%) comprised of NH
3
. In many instances, the plasma source gas is preferably solely NH
3
. A relatively high substrate bias voltage (typically about −100 V to about −1,000 V) is applied; the result is vertically directed anisotropic etching, where ionized nitrogen and hydrogen species, for example, are more active at the base of an opening in the substrate structure than at the lateral sidewalls of the opening. This avoids undercutting of the patterned photoresist layer during descumming. In the case of reworking, the hard mask layer shields the underlying organic dielectric layer at the top of the opening, and this, combined with the anisotropic direction of etch, reduces damage to the previously etched dielectric layer underlying the hard mask layer.


REFERENCES:
patent: 5674357 (1997-10-01), Sun et al.
patent: 5980768 (1999-11-01), Abraham
patent: 6153530 (2000-11-01), Ye et al.
patent: 6207583 (2001-03-01), Dunne et al.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

NH3 plasma descumming and resist stripping in semiconductor... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with NH3 plasma descumming and resist stripping in semiconductor..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and NH3 plasma descumming and resist stripping in semiconductor... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2859619

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.