Double LDD devices for improved DRAM refresh

Semiconductor device manufacturing: process – Making field effect device having pair of active regions... – Having junction gate

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C438S289000

Reexamination Certificate

active

06759288

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to the field of integrated circuits and, more particularly, to semiconductor devices having double lightly doped regions for improved DRAM refresh characteristics and methods for their manufacture.
2. Description of the Related Art
Metal oxide semiconductor (MOS) structures are basic electronic devices used in many integrated circuits. One such structure is the MOS field effect transistor (MOSFET), which is typically formed in a semiconductor substrate by providing a gate structure over the substrate to define a channel region, and by forming source and drain regions on opposing sides of the channel region.
MOSFETs are often used in the formation of memory circuits, including dynamic random access memory (DRAM) circuits. DRAM circuits are composed of an array of individual memory cells, each cell including a capacitor for holding a charge and an access transistor for accessing the charge held in the capacitor.
In a typical DRAM cell using a MOSFET access transistor, after a charge is stored the charge does not remain in the capacitor indefinitely, but instead slowly leaks out of the p-n junction of the access transistor for the cell. This phenomenon is known as “junction leakage.” To avoid losing the cell contents, the charge must be periodically re-stored in the capacitor through a process known as “refresh.”Increased junction leakage leads to premature depletion of the capacitor's stored charge, necessitating more frequent refresh operations. Refresh operations consume device resources and it is therefore desirable to reduce junction leakage as much as possible and thus reduce the frequency of required refresh operations.
Several factors are known to contribute to junction leakage, including (a) the electric field (E) generated at the p-n junction, (b) surface- or bulk-defect-induced recombination/generation current, and (c) gated diode assisted band-to-band tunneling leakage, such as gate-induced drain-leakage (GIDL) current. In particular, factor (a), the electric field (E) generated at the p-n junction, is proportional to the gradient of the doping concentration of either side of the junction. Because junction leakage varies directly with this electric field (i.e. higher E leads to higher junction leakage), it is desirable to control the doping concentration on both sides of the p-n junction. By controlling the doping concentration on both sides of the junction to reduce the gradient of the doping concentration, the p-n junction electric field (E) can be reduced and hence junction leakage.
The gradient of the doping concentration at the p-n junction of a MOSFET in a DRAM array depends on the doping concentration of the channel region and the doping concentration of the ion-implanted regions adjacent the channel serving as source/drain regions for a cell access transistor. For example, in an NMOS transistor, the channel is doped with p-type impurities, the source and drain regions are doped with n-type impurities, and as the boundary between the p-type channel and the n-type drain region is approached, the rate of change in impurity concentration defines the gradient of the doping concentration. An abrupt change in impurity concentration from p-type to n-type doping at the boundary creates a high gradient, high electric field (E) and hence increases junction leakage. A more gradual change from p-type to n-type doping concentration, for example using lightly doped drain (LDD) regions, creates a relatively lower gradient, lower electric field (E) and hence decreases junction leakage.
There are several tradeoffs that must be taken into account when formulating the doping concentrations on either side of the p-n junction. For example, in an NMOS transistor, the p-type doping concentration of the channel should be sufficiently high to turn off the transistor when the gate is off (i.e., low subthreshold leakage). On the other hand, the channel doping concentration should not be so high that a full potential of charge is prevented from being transferred from source to drain when the gate is on.
Likewise, the n-type doping concentration of the source and drain regions should be sufficiently high to obtain satisfactorily low series resistance and threshold voltage. If the n-type doping concentration is too low, transistor current drive may be degraded and a wider depletion width may result, possibly leading to undesirable levels of reverse bias current. On the other hand, if the n-type doping concentration is too high, undesirable junction leakage effects can result as discussed above. Thus, it would be desirable to form the memory array taking the above considerations into account and produce memory cells in which the electric field generated at the p-n junction is reduced for each cell and hence reduce junction leakage.
Another problem associated with the electric field generated at the p-n junction is the “hot carrier” or “hot electron” effect wherein energetic charge carriers, typically electrons and/or holes, are accelerated by a strong electric field, such as that created at the p-n junction. Such high strength electric fields accelerate the energetic carriers, known as “hot carriers,” toward the gate electrode and the underlying gate oxide. These hot carriers are thus injected into the thin dielectric layer of the gate structure and into the adjacent thicker dielectric gate spacer structure, resulting in damage to the gate oxide as well as to the gate spacer structure. Over time, these hot electrons create a permanent charge in the thin dielectric layer and the dielectric spacers, degrading or destroying the performance of the associated MOSFET device. This is typically more of a problem with N-channel MOSFETS (which have electrons as the primary carrier species) than P-channel MOSFETS (which have “holes” as the primary carrier species).
The above problems are well known in the art and have resulted in the widely practiced remedy of forming lightly doped drain (LDD) regions between the source/drain regions and the channel region in the semiconductor substrate. This LDD region reduces the gradient of the doping concentration at the boundary (p-n junction) between the source/drain regions and the channel region to thereby lower the strength of the electric field (E) generated at the p-n junction. This reduction in the electric field (E) results in decreased junction leakage and reduces the hot carrier effect.
For example, U.S. Pat. No. 4,366,613 to Ogura et al. (“Ogura”) discloses the formation of LDD regions in a RAM MOSFET. Referring to
FIG. 1
, MOSFET device
5
includes a gate structure comprising an access gate conductor
16
and a gate top insulator
20
formed over an oxide layer
18
that is formed on a substrate
12
. Insulating spacers
32
,
34
are formed on sidewalls of the gate structure. The device also includes source/drain regions
36
,
38
and two lightly doped regions
22
and
24
, one of which is provided proximate to each of the source/drain regions
36
,
38
. A channel
15
extends between the LDD regions
22
and
24
. By providing the LDD regions
22
and
24
, the electric field at the p-n junction between the channel
15
and the source/drain regions
36
,
38
is reduced, thereby reducing the junction leakage and the hot carrier effect.
The prior art LDD structure of
FIG. 1
can be made by a variety of processes, but is typically made by providing a low-density ion implant of the LDD regions
22
,
24
before adding oxide spacers
32
,
34
to the gate structure (see U.S. Pat. No. 4,366,613 to Ogura). After the spacers
32
,
34
have been added to the gate structure, a higher-density ion implant is made to form the source and drain regions
36
,
38
. Since the source and drain regions
36
,
38
were implanted after the formation of the spacers
32
,
34
, they are offset further from the channel
15
than the LDD regions
22
,
24
. The resulting structure exhibits a decreased electric field at the p-n junction.
Although LDD structures have helped advanc

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Double LDD devices for improved DRAM refresh does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Double LDD devices for improved DRAM refresh, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Double LDD devices for improved DRAM refresh will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3233477