Semiconductor device manufacturing: process – Making field effect device having pair of active regions... – Having insulated gate
Reexamination Certificate
2000-07-28
2002-06-11
Pham, Long (Department: 2823)
Semiconductor device manufacturing: process
Making field effect device having pair of active regions...
Having insulated gate
C438S257000, C438S264000, C438S514000
Reexamination Certificate
active
06403420
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates generally to flash memory devices and more particularly to a method of fabricating flash memory devices having an ONO layer which contains a silicon nitride layer sandwiched between two silicon oxide layers.
2. Description of the Related Art
A flash memory having an ONO layer is illustrated in FIG.
1
. It includes an ONO layer
60
disposed on top of a silicon substrate
10
, and a control gate
71
, typically of polysilicon, disposed on top of the ONO layer
60
. The ONO layer
60
comprises a lower layer
61
made of silicon oxide, a middle layer
62
made of silicon nitride, and an upper layer
63
made of silicon oxide.
FIGS. 2A-2I
illustrate the conventional process for fabricating a flash memory device having an ONO layer. First, a silicon oxide layer
20
is thermally grown on the silicon substrate
10
to form the structure of FIG.
2
A. Then, as shown in
FIG. 2B
, nitrogen atoms (N or N
2
) are implanted into the silicon oxide layer
20
.
The nitrogen implanting step is followed by heating to anneal out the implant damage and to diffuse the implanted nitrogen to the Si/SiO
2
interface
21
and cause SiN bonds to be formed at the Si/SiO
2
interface
21
. The heating is performed in a furnace and the entire heating process takes several hours because the process requires a long time to ramp up and ramp down.
Subsequently, a silicon nitride layer
30
is deposited on top of the silicon oxide layer
20
by chemical vapor deposition (CVD).
FIG. 2C
shows the silicon nitride layer
30
deposited on top of the silicon oxide layer
20
. A second layer of silicon oxide
40
is then formed on top of the silicon nitride layer
30
and the resulting structure is shown in FIG.
2
D. Thereafter, as shown in FIG.
2
E, a photoresist
50
is formed on top of the second silicon oxide layer
40
, and this semiconductor structure is etched until an upper surface of the silicon substrate
10
is exposed. The resulting structure, shown in
FIG. 2F
, is subsequently implanted with arsenic and boron ions using the remaining photoresist
50
as a mask and heated to diffuse the implanted ions.
The remaining photoresist
50
is stripped away and, as shown in
FIG. 2G
, a polysilicon layer
70
is deposited on top of the exposed surface of the silicon substrate
10
and on top and sidewalls of the ONO layer
60
. The polysilicon layer
70
is then patterned using conventional lithography techniques and a control gate
71
remains on top of the ONO layer
60
.
FIG. 2H
shows the resulting gate structure
75
including the control gate
71
and the ONO layer
60
.
Oxide spacers
81
,
82
, shown in
FIG. 2I
, are formed on the sidewalls of the gate structure
75
by (i) depositing a conformal layer of silicon oxide
80
by CVD on the exposed surface of the silicon substrate
10
and on top and sidewalls of the gate structure
75
(FIG.
2
I), and (ii) anisotropically etching the deposited silicon oxide.
SUMMARY OF THE INVENTION
The invention provides a process for forming an ONO flash memory device that improves the Si/SiO
2
interface robustness against hot carrier degradation by carrying out the step of nitrogen implantation after bit-line formation.
The invention produces a gate structure for an ONO flash memory device that includes a first layer of silicon oxide on top of a semiconductor substrate, a second layer of silicon oxide, a layer of silicon nitride sandwiched between the two silicon oxide layers, and a control gate on top of the second layer of silicon oxide.
In the process according to the invention, the ONO layer is first formed and patterned, and junction areas are formed in the substrate. Thereafter, nitrogen is implanted into the patterned ONO layer and the entire semiconductor structure is heated to anneal out the nitrogen implant damage and to diffuse or drive the implanted nitrogen into the substrate and silicon oxide interface to form strong SiN bonds at that interface. The SiN bonds is desirable because they improve the bonding strength at the interface and the nitrogen remaining in the silicon oxide layer increases the oxide bulk reliability.
By implanting nitrogen into the ONO stack, instead of a single silicon oxide layer, damage to the underlying silicon substrate is reduced.- If the nitrogen was implanted into only the single silicon oxide layer, the damage to the underlying silicon substrate would be larger. This results in better isolation between adjacent bit lines and suppresses leakages between adjacent bit lines.
Additional objects, features and advantages of the invention will be set forth in the description of preferred embodiments which follows.
REFERENCES:
patent: 5966603 (1999-10-01), Eitan et al.
patent: 6130095 (2000-10-01), Eitan et al.
patent: 6168993 (2001-01-01), Foote et al.
Ramsbey Mark
Sun Yu
Wu Yider
Yang Jean
Advanced Micro Devices , Inc.
Foley & Lardner
Pham Long
LandOfFree
Nitrogen implant after bit-line formation for ONO flash... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Nitrogen implant after bit-line formation for ONO flash..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Nitrogen implant after bit-line formation for ONO flash... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2954651