ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to an integrated circuit having a hydrogen barrier layer to protect elements containing ferroelectric or high-dielectric constant metal oxide materials.
2. Description of the Related Art
Ferroelectric compounds possess favorable characteristics for use in nonvolatile integrated circuit memories. See Miller, U.S. Pat. No. 5,046,043. A ferroelectric device, such as a capacitor, is useful as a nonvolatile memory when it possess desired electronic characteristics, such as high residual polarization, good coercive field, high fatigue resistance, and low leakage current. Lead-containing ABO
3
-type ferroelectric oxides such as PZT (lead titanate zirconate) and PLZT (lanthanum lead titanate zirconate) have been studied for practical use in integrated circuits. Layered superlattice material oxides have also been studied for use in integrated circuits. See Watanabe, U.S. Pat. No. 5,434,102. Layered superlattice material compounds exhibit characteristics in ferroelectric memories that are orders of magnitude superior to those of PZT and PLZT compounds. Integrated circuit devices containing ferroelectric elements are currently being manufactured. Nevertheless, the persistent problem of hydrogen degradation during the manufacturing process hinders the economical production in commercial quantities of ferroelectric memories and other IC devices using the layered superlattice material compounds with the desired electronic characteristics.
A typical ferroelectric memory device in an integrated circuit contains a semiconductor substrate and a metal-oxide semiconductor field-effect transistor (MOSFET) in electrical contact with a ferroelectric device, usually a ferroelectric capacitor. A ferroelectric capacitor typically contains a thin film containing ferroelectric metal oxide located between a first, bottom electrode and a second, top electrode, the electrodes typically containing platinum. During manufacture of the circuit, the MOSFET is subjected to conditions causing defects in the silicon substrate. For example, the CMOS/MOSFET manufacturing process usually includes high energy steps, such as ion-mill etching and plasma etching. Defects also arise during heat treatment for crystallization of the ferroelectric thin film at relatively high temperatures, often in the range 500° C. to 900° C. As a result, numerous defects are generated in the single crystal structure of the semiconductor silicon substrate, leading to deterioration in the electronic characteristics of the MOSFET.
To restore the silicon properties of the MOSFET/CMOS, the manufacturing process typically includes a hydrogen annealing step in which defects, such as dangling bonds, are eliminated by utilizing the reducing property of hydrogen. Various techniques have been developed to effect the hydrogen annealing, such as a forming gas anneal (“FGA”). Conventionally, FGA treatments are conducted under ambient conditions in a H
2
—N
2
gas mixture between 350° C. and 550° C., typically around 400° C. to 450° C., for a time period of about 30 minutes. In addition, the CMOS/MOSFET manufacturing process requires other fabrication steps that expose the integrated circuit to hydrogen, often at elevated temperatures, such as hydrogen-rich plasma CVD processes for depositing metals and dielectrics, growth of silicon dioxide from silane or TEOS sources, and etching processes using hydrogen and hydrogen plasma. During processes that involve hydrogen, the hydrogen diffuses principally through the top electrode to the ferroelectric thin film, but also from the side edges of the capacitor, and reduces the oxides contained in the ferroelectric material. The absorbed hydrogen also metallizes the surface of the ferroelectric thin film by reducing metal oxides. As a result of these effects, the electronic properties of the capacitor are degraded. After the forming-gas anneal (FGA), the remnant polarization of the ferroelectrics is very low and no longer suitable for storing information. An increase in leakage currents also results. In addition, the adhesivity of the ferroelectric thin film to the upper electrode is lowered by the chemical change taking place at the interface. Alternatively, the upper electrode is pushed up by the oxygen gas, water, and other products of the oxidation-reduction reactions taking place. Thus, peeling is likely to take place at the interface between the top electrode and the ferroelectric thin film. In addition, hydrogen also can reach the lower electrode, leading to internal stresses that cause the capacitor to peel off its substrate. These problems are acute in ferroelectric memories containing layered superlattice material compounds because these oxide compounds are particularly complex and prone to degradation by hydrogen-reduction.
A related problem encountered in the fabrication of ferroelectric devices is the stress arising in and between the different circuit layers as a result of the manufacturing processes. The ferroelectric compounds comprise metal oxides. The products of the hydrogen reduction reactions cause an increase in the total volume of the ferroelectric element. As a result, the ferroelectric thin film exerts an upward pressure on the layers above it.
Several methods have been reported in the art to inhibit or reverse hydrogen degradation of desired electronic properties in ferroelectric oxide materials. Oxygen-recovery annealing at high temperature (800° C.) for about one hour results in virtually complete recovery of the ferroelectric properties degraded by hydrogen treatments; but the high-temperature oxygen-anneal itself may generate defects in silicon crystalline structure, and it may offset somewhat the positive effects of any prior forming-gas anneal on the CMOS characteristics. Also, if hydrogen reactions have caused structural damage to the ferroelectric device, such as peeling, then a recovery anneal is not able to reverse effectively the damage.
To reduce the detrimental effects of the hydrogen heat treatment and protect the ferroelectric metal oxide element, the prior art also teaches the application of hydrogen barrier layers to inhibit the diffusion of hydrogen into the ferroelectric material. The barrier layer is typically located over the ferroelectric element, but it can also be located below and laterally to the sides of the element.
Hydrogen degradation is also a problem in complex metal oxides used in nonferroelectric, high-dielectric constant applications in integrated circuits. Hydrogen reactions cause structural damage, as described above for ferroelectric oxides, and cause degradation of dielectric properties. Examples of metal oxides subject to hydrogen degradation include barium strontium titanate (“BST”), barium strontium niobate (“BSN”), certain ABO
3
-type perovskites, and certain layered superlattice materials. Hydrogen barrier layers are, therefore, used also to protect nonferroelectric, high-dielectric constant metal oxides.
It is known in the art to use a hydrogen barrier layer comprising a nitride of aluminum, silicon or titanium, that is, AlN, Si
3
N
4
, or Ti
3
N
4
.
Typically, hydrogen barrier layers known in the art are not completely effective in preventing hydrogen diffusion and the resulting hydrogen degradation of metal oxides. Thus, even when a diffusion barrier is used, it is not uncommon for structural damage to arise in the ferroelectric or dielectric device and for hydrogen to reach the metal oxide layer and degrade the desired ferroelectric or dielectric properties of the metal oxide material. Therefore, it would be useful to have new materials different from those known in the art to obtain the benefits of a hydrogen barrier layer in protecting ferroelectric and dielectric oxide materials, in particular, ferroelectric layered superlattice materials, from hydrogen degradation.
BRIEF SUMMARY OF THE INVENTION
The invention solves the above problem by disclosing novel compositions of material for a hydrogen diffusion barrier.
A feature of the invention is a hydrogen barrier lay
Cuchiaro Joseph D.
McMillan Larry D.
Paz de Araujo Carlos A.
Nelms David
Nhu David
Patton & Boggs LLP
Symetrix Corporation
LandOfFree
Ferroelectric integrated circuit having hydrogen barrier layer does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Ferroelectric integrated circuit having hydrogen barrier layer, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Ferroelectric integrated circuit having hydrogen barrier layer will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2930700