Radiation imagery chemistry: process – composition – or product th – Imaging affecting physical property of radiation sensitive... – Radiation sensitive composition or product or process of making
Reexamination Certificate
2000-06-22
2002-07-02
Hamilton, Cynthia (Department: 1752)
Radiation imagery chemistry: process, composition, or product th
Imaging affecting physical property of radiation sensitive...
Radiation sensitive composition or product or process of making
C430S269000, C522S092000, C522S096000, C522S090000, C522S109000, C522S142000, C522S146000, C522S170000, C264S401000
Reexamination Certificate
active
06413696
ABSTRACT:
The present invention relates to a liquid, radiation-curable composition which is particularly suitable for the production of three-dimensional shaped articles by means of stereolithography, to a process for the production of a cured product and, in particular, for the stereolithographic production of a three-dimensional shaped article from this composition having a high heat deflection temperature.
BACKGROUND
The production of three-dimensional articles of complex shape by means of stereolithography has been known for a relatively long time. In this technique the desired shaped article is built up from a liquid, radiation-curable composition with the aid of a recurring, alternating sequence of two steps (a) and (b); in step (a), a layer of the liquid, radiation-curable composition, one boundary of which is the surface of the composition, is cured with the aid of appropriate radiation, generally radiation produced by a preferably computer-controlled laser source, within a surface region which corresponds to the desired cross-sectional area of the shaped article to be formed, at the height of this layer, and in step (b) the cured layer is covered with a new layer of the liquid, radiation-curable composition, and the sequence of steps (a) and (b) is repeated until a so-called green model of the desired shape is finished. This green model is, in general, not yet fully cured and must therefore, normally, be subjected to post-curing.
The mechanical strength of the green model (modulus of elasticity, fracture strength), also referred to as green strength, constitutes an important property of the green model and is determined essentially by the nature of the stereolithographic-resin composition employed. Other important properties of a stereolithographic-resin composition include a high sensitivity for the radiation employed in the course of curing and a minimum curl factor, permitting high shape definition of the green model. In addition, for example, the precured material layers should be readily wettable by the liquid stereolithographic-resin composition, and of course not only the green model but also the ultimately cured shaped article should have optimum mechanical properties.
Another requirement that has recently become a high priority for stereolithography users is the high temperature performance of cured articles produced by stereolithography. It is usually measured by the Heat Deflection Temperature (HDT) or Glass Transition Temperature (T
g
). The HDT value is determined by the ASTM method D648 applying a load of 66 psi.
For several years, high temperature performance for stereolithography produced articles has been achieved by the use of (meth)acrylate chemistry. This approach primarily entails the use of various commercially available urethane acrylate derivatives. EP-802455 of Teijin Seiki Corp. (Oct. 22, 1997) and JP 08323866 of Takemoto Oil & Fat Co Ltd (Dec. 10, 1996) describe acrylate urethane compositions for achieving good heat resistance and strength. However, a major disadvantage of such acrylate urethane compositions is that polymerization is hindered by atmospheric oxygen because polymerization is of a radical nature, that the cure shrinkage is unacceptably large, that the resins are irritant to the skin, particularly when the viscosity is low (low viscosity is highly preferred for stereolithography applications). Thus, acrylate urethane-based compositions show poor practicality for stereolithography.
Liquid, radiation-curable compositions for stereolithography which overcome the abovementioned problems of the acrylate chemistry are described, for example, in U.S. Pat. No. 5,476,748, which is incoporated herein by reference. These compositions are so-called hybrid systems, comprising free-radically and cationically photopolymerizable components. Such hybrid compositions comprise at least:
(A) a liquid difunctional or more highly functional epoxy resin or a liquid mixture consisting of difunctional or more highly functional epoxy resins;
(B) a cationic photoinitiator or a mixture of cationic photoinitiators;
(C) a free-radical photoinitiator or a mixture of free-radical photoinitiators; and
(D) at least one liquid poly(meth)acrylate having a (meth)acrylate functionality of more than 2,
(E) at least one liquid cycloaliphatic or aromatic diacrylate, and
(F) a certain hydroxy compound that is selected from the group consisting of OH-terminated polyethers, polyesters and polyurethanes. Such hybrid systems can optionally further contain vinyl ether-based resins or other cationically cured components such as oxetanes, spiro-ortho esters.
A drawback of commercial cationic or hybrid cationic-radical stereolithographic compositions is that their cured articles show HDT values that are much lower than those based on acrylate chemistry, usually between 40 and 100° C.
Many hybrid compositions have been developed by companies for use in stereolithography process systems. For example, U.S. Pat. No. 5,434,196, assigned on its face to Asahi Denka Kogyo K.K., discloses resin compositions for so-called optical molding containing a mixture of epoxy resins and vinylethers, a cationic initiator, and a mixture of an acrylate compound and a triacrylate compound.
To date, there is no scientifically published or universally accepted term for defining the high temperature hybrid stereolithography resins. Through marketing brochures of stereolithography resin maufacturers and presentations in trade organizations, high temperature hybrid stereolithography resins are defined as those wherein their cured articles have HDT values over 80 and about 100° C. The highest HDT value ever reported for commercial hybrid stereolithography resins is about 100° C.
Despite all previous attempts, there exists a need for hybrid stereolithography compositions capable of producing high temperature performance cured articles for which the photospeed, accuracy, water resistance are commercially acceptable. Such hybrid compositions should possess HDT values over those of the existing ones, especially over 110° C.
SUMMARY OF THE INVENTION
The present invention relates to novel resin compositions containing at least one solid or liquid actinic radiation-curable and cationically polymerizable organic substance, an actinic radiation-sensitive initiator for cationic polymerization and an actinic radiation-curable and radical-polymerizable organic substance. The compositions contain an actinic radiation-sensitive initiator for radical polymerization. The actinic radiation-curable and cationically polymerizable organic substance is at least one glycidylether of a polyhydric aliphatic, alicyclic or aromatic alcohol having at least three epoxy groups with epoxy equivalent weight between 90 and 700 grams per equivalent and at least one solid or liquid alicyclic epoxide with an epoxy equivalent weight between 80 and 330 grams per equivalent having at least two epoxy groups, or mixtures thereof having a monomer purity greater than about 80% by weight.
The composition preferably contains 55-90%, more preferably 20 and 75% by weight, of the at least one solid or liquid actinic radiation-curable and cationically polymerizable organic substance, 0.05 to 12% by weight an actinic radiation-sensitive initiator for cationic polymerization, 5% to 25% by weight of an actinic radiation-curable and radical-polymerizable organic substance, and 0.02 to 10% by weight, with the sum total of components being 100 percent by weight.
The actinic radiation-curable and cationically polymerizable organic substance can contain not more than 20% by weight of at least one liquid or solid vinylether compound having at least two cationically-reactive groups in the molecule or a hydroxy-functionalized mono(poly)vinylether or mixtures thereof.
The actinic radiation-curable and cationically polymerizable organic substance can further contain at least one liquid or solid epoxy cresol novolac, epoxy phenol novolac, oxetane or spiro-ortho ester compound having at least two cationically-reactive groups in the molecule, or mixtures thereof.
The at least o
Fong John W.
Melisaris Anastasios P.
Pang Thomas H.
Renyi Wang
Hamilton Cynthia
Lyon & Lyon LLP
Vantico Inc.
LandOfFree
Liquid, radiation-curable composition, especially for... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Liquid, radiation-curable composition, especially for..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Liquid, radiation-curable composition, especially for... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2834767