Using a carbon film as an etch hardmask for hard-to-etch...

Details Using a carbon film as an etch hardmask for hard-to-etch... Using a carbon film as an etch hardmask for hard-to-etch...

2001-08-02

2003-06-03

Nelms, David (Department: 2812)

Semiconductor device manufacturing: process

Introduction of conductivity modifying dopant into...

Diffusing a dopant

C438S639000

Reexamination Certificate

active

06573167

ABSTRACT:

FIELD OF THE INVENTION
The invention is generally related to the field of semiconductor processing and more specifically to hardmasks for etching hard-to-etch materials in a semiconductor process.
BACKGROUND OF THE INVENTION
Many materials, such as Pt, Ir, Ru, IrO
2
, RuO
2
, BST (Barium-strontium-titanate), PZT (Lead Zirconate Titanate), SBT (Bismuth Strontium Tantalunate), FeNi, FeNiCo, and others used in making DRAMs, FeRAMs (ferroelectric random access memories), or magnetic storage devices, are very difficult to etch due to the lack of volatile etch by products under normal plasma etch conditions. The etch of these materials is typically accomplished by physical sputtering or chemically assisted sputtering. As a result, photoresist, silicon oxide, or silicon nitride masks do not offer enough etch selectivity. Therefore, masking for these etches is very difficult.
One masking approach uses a TiAlN based hardmask. Under the proper etch conditions, TiAlN and TiN have enough selectivity to serve as a hardmask when etching these hard-to-etch materials. The proper etch conditions include a gas mixture of oxygen and Cl- or F-bearing gases at specific concentrations. The restrictions on the etch conditions imposed by the hardmask limit the process window and process optimizations. Furthermore, removing the TiAlN hardmask has a tendency to etch the capacitor dielectric and bottom barrier materials.
SUMMARY OF THE INVENTION
The invention uses a carbon hardmask for etching hard-to-etch materials such as Pt, Ir, Ru, IrO
2
, RuO
2
, BST (Barium-strontium-titanate), PZT (Lead Zirconate Titanate), SBT (Bismuth Strontium Tantalunate), FeNi, and FeNiCo.
An advantage of the invention is providing a hardmask for etching hard-to-etch materials that expands the process chemistries available for etching the hard-to-etch materials.
This and other advantages will be apparent to those of ordinary skill in the art having reference to the specification in conjunction with the drawings.


REFERENCES:
patent: 3646527 (1972-02-01), Wada et al.
patent: 5445710 (1995-08-01), Hori et al.
patent: 5888593 (1999-03-01), Petrmichl et al.
patent: 5981398 (1999-11-01), Tsai et al.
patent: 5998100 (1999-12-01), Azuma et al.
patent: 6211035 (2001-04-01), Moise et al.
patent: 07-297170 (1995-11-01), None

Affiliated with

Also associated with

Rating

Using a carbon film as an etch hardmask for hard-to-etch... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Using a carbon film as an etch hardmask for hard-to-etch..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Using a carbon film as an etch hardmask for hard-to-etch... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3114676