Treatment to eliminate polysilicon defects induced by...

Cleaning and liquid contact with solids – Processes – Including application of electrical radiant or wave energy...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C134S001200, C134S021000

Reexamination Certificate

active

06715497

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates generally to a method and apparatus for fabricating semiconductor devices and, in particular, to a method and apparatus for cleaning a substrate surface by, for example, eliminating polysilicon defects induced by metallic contaminants.
2. Description of Related Art
In the production of semiconductor devices, a semiconductor substrate, such as a silicon substrate, may be formed comprising a number of varying block levels or layers whereby such block levels may include various structures formed over the semiconductor substrate. For example, block levels may include varying structures over the silicon substrate which define the semiconductor devices such as resistors, PFET wells and NFET wells in CMOS technology, and the like.
As will be recognized, the varying structures, or varying block levels, may be made by processes including photolithography, ion implant, resist strip, wet cleaning processes, and the like. An inherent problem of these block levels, and the processes used to define them over the silicon substrate, is that they produce contaminants including, for example, metallic contaminants and hydrocarbon-containing contaminants over the substrate which remain thereon to contaminate the surface. During the semiconductor manufacturing process, contaminants including metallic contaminants and hydrocarbon-containing contaminants may be deposited on both the substrate front-side (chip side) and back-side. Front-side contaminants are typically introduced from trace metallics in the photoresist while backside contaminants are typically introduced from the semiconductor processing equipment such as, for example, automated substrate handlers and chucks. This invention addresses both substrate front-side and back-side metallic removal.
As will be further recognized, if the metallic contaminants are not removed from the substrate front-side or back-side prior to either the gate oxidation or the polysilicon deposition processes, a gross defect may be induced. It is preferable to remove the contaminants prior to gate oxidation to reduce the potential for gate oxide “pinholes”. These “pinholes” can render the device either non-functional or unreliable due to poor gate oxide integrity. Additionally, removal of the metallic contaminants will prevent the formation of polysilicon defects, herein referred to as “peppery polysilicon”, which can result in shorts between polysilicon lines.
The microelectronics industry has faced problems with peppery polysilicon since it first started using polysilicon as a gate conductor. Several techniques are aimed at controlling peppery polysilicon including, for example, reducing the metallics within the deposited photoresist, and improving both the dry steps and wet clean steps used to define the various block levels. However, such prior art techniques do not completely eliminate the metallic contaminants over the substrate surface, and thus do not prevent the occurrence of peppery polysilicon. Therefore, known techniques can still lead to semiconductor failure in the field.
Prior art is also directed to controlling contaminants within the deposition tools used for gate formation. For instance, in U.S. Pat. No. 3,279,946, a process is disclosed wherein a reactor chamber, or a conventional semiconductor deposition tool, is preconditioned prior to a semiconductor material deposition. The tool is preconditioned by heating the reactor in the presence of a reactant gas, preferably HCl or chlorine, which reacts with donor impurities on the walls of the chamber to merely remove impurities in the reactor prior to a semiconductor material deposition on a clean wafer. This approach is problematic as the chlorine eventually induces corrosion of the deposition tooling in the reactor whereby the corrosion can actually increase metallic contamination during the semiconductor material deposition. Since the prior art does not describe any in-situ cleaning of metal contaminants from a substrate surface, or cleaning of the corroded deposition tooling, peppery polysilicon will likely result and the semiconductor may fail.
Furthermore, as semiconductor technologies, such as CMOS technologies, continue to decrease in size, and thus require thinner transfer gate oxides, the known cleaning and/or metallic contamination removal processes do not completely clean the substrate surface and/or eliminate metallic contaminants from the substrate surface. For example, the process of removing metallic contaminants from a substrate surface using a chlorinated environment during gate oxidation transfer processes is used for thick gate oxide depositions. In such processes, the metallics are removed as a result of the substrate being exposed to the chlorinated environment for the extended period of time it takes to deposit the thick gate oxide. However, such techniques are not effective or efficient in removing metallic contaminants from substrates having thin gate oxide. To produce the thinner gate oxide the substrate will be exposed to the chlorinated environment for a limited time since the gate oxide deposition time is reduced to produce the thinner gate oxide. Thus, metallic contaminants may remain on the thin gate oxide resulting in peppery polysilicon, as well as pinholes in the thinner gate oxide, whereby gate oxide integrity may be compromised, and polysilicon shorts and semiconductor failure may occur.
Bearing in mind the problems and deficiencies of the prior art, it is therefore an object of the present invention to provide a method and apparatus which cleans and/or removes contaminants, including metallic contaminants and hydrocarbon-containing contaminants, form a surface of a substrate to provide the substrate with a clean surface for uniform gate formation.
It is another object of the present invention to provide a method and apparatus to clean and/or reduce residual metallic contamination on a surface of a semiconductor substrate after completion of all block levels.
A further object of the present invention is to provide a method and apparatus to clean and/or reduce residual metallic contamination on a surface of a semiconductor substrate prior to sacrificial oxide removal.
Another object of the present invention is to provide a method and apparatus of preventing oxides formed on a semiconductor substrate surface prior to gate formation.
Still another object of the present invention is to provide a method and apparatus of forming a clean surface on a semiconductor substrate to provide for a high quality gate oxide transfer.
It is also an object of the present invention to provide a method and apparatus for the uniform formation of a gate oxide layer across the surface of a semiconductor substrate.
Still other objects and advantages of the invention will in part be obvious and will in part be apparent from the specification.
SUMMARY OF THE INVENTION
The above and other objects and advantages, which will be apparent to one of skill in the art, are achieved in the present invention which is directed to, in a first aspect, a method of eliminating metal contaminants on a surface of a semiconductor substrate. The method comprises the steps of providing a semiconductor substrate which may have metallic contaminants and/or hydrocarbon-containing contaminants on a surface thereof into a mainframe. The pressure and atmosphere of the mainframe is then evacuated to an oxygen-free environment at a pressure of less than about 1 Torr. Subsequently, the semiconductor substrate is heated to an elevated temperature, preferably to a temperature ranging from about 500° C. to about 700° C. for a time ranging from about 5 minutes to about 30 minutes, within the mainframe. While heating the substrate, the substrate is simultaneously purged and a surface thereof contacted with a chlorine-containing gas, preferably HCl or Cl
2
by a chemical vapor deposition process, which may form volatile metallic byproducts with metallic contaminants and/or volatile byproducts with the hydrocarbon-containing contaminants the

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Treatment to eliminate polysilicon defects induced by... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Treatment to eliminate polysilicon defects induced by..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Treatment to eliminate polysilicon defects induced by... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3271488

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.