ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention generally relates to the fabrication of integrated circuits and, more particularly, to a system and method for forming polysilicon (p-Si) films from the sputter deposition of amorphous Si (a-Si) using an Argon (Ar)-Hydrogen (H
2
) gas mixture.
2. Description of the Related Art
Amorphous Si thin films are used in the fabrication of polycrystalline silicon thin film transistors (TFTs), which in turn are a key element in active matrix (AM) type liquid crystal displays (LCDs).
Sputtering is a well-known conventional process suited to the formation of the various Si-based, TFT layers because:
1. It is a safe and environmentally benign technique;
2. It can be used even at room temperature. Hence, it is compatible with any kind of substrate;
3. Silicon films with very low H
2
content can be deposited by this method. Hence, there is no need for dehydrogenation to release excessive hydrogen. Alternatively, hydrogen can be incorporated into the film if, and when, necessary; and
4. It is a simpler and a more easily scaled method than comparable methods that rely upon chemistry.
For improved electrical performance it is desirable that the deposited amorphous silicon film be converted, typically by annealing, into a microcrystalline or polycrystalline Si film. There are many processes known in the art to form polycrystalline silicon (polysilicon) from amorphous silicon.
It is known to use a large amount of hydrogen in the Ar gas in the sputtering deposition process for applications such as deposition of hydrogenated a-Si:H films used in amorphous silicon solar cells or amorphous silicon LCDs. In these films, H
2
termination of Si dangling bonds is necessary to achieve desired film characteristics. However, the use of hydrogen in the sputtering deposition process is not conventionally known to improve the electrical characteristics of the polycrystalline silicon film formed by this method.
FIGS. 1
a
through
1
e
are partial cross-sectional diagrams illustrating the fabrication of a conventional top-gate TFT structure (prior art). Poly-Si (polycrystalline-Si) TFTs are made by a plurality of processes. In the majority of polycrystalline silicon TFT LCD applications, the so-called top-gate, polycrystalline silicon TFT structure is used. Typically, Plasma-Enhanced Chemical Vapor Deposition (PE-CVD) or Low-Pressure CVD (LPCVD) is used to deposit the amorphous silicon precursor. However, there are several advantages in using physical vapor deposition (PVD) or sputtering to form the silicon film. Such advantages are a reduction in process steps, since there is no need for dehydrogenation, a reduction in equipment costs, and improved process safety, since no toxic/pyrophoric gases are necessary.
In
FIG. 1
a
a barrier layer
10
is deposited over a substrate
12
. Amorphous Si
14
is deposited over barrier layer
10
.
In
FIG. 1
b
the silicon layer
14
is annealed, using an Excimer Laser for example, to form polycrystalline silicon layer
14
. Then, the polycrystalline silicon layer
14
is patterned and dry etched.
In
FIG. 1
c
a gate isolation layer
16
is formed over the polycrystalline silicon layer
14
. A gate
18
is formed over gate isolation layer
16
, and the source region
20
and drain region
22
are implanted with P material.
In
FIG. 1
d
an interlayer dielectric
24
is isotropically deposited.
In
FIG. 1
e
the interlayer dielectric
24
is selectively etched to form vias to the source/drain regions
20
/
22
. A source contact
26
and a drain contact
28
are deposited and patterned. The present invention is concerned with the sputter deposition of the amorphous silicon used to form polycrystalline silicon layer
14
(
FIG. 1
a
).
FIG. 2
is a partial cross-sectional diagram of a typical DC magnetron sputtering chamber (prior art). One of the key aspects of the Si-sputtering process is the ‘target’ component. The target is a block of the material to be deposited, mounted on an appropriate metal backing plate, and placed opposite to the substrate where the film is to be deposited. Plasma strikes in the gap between the target and the substrate. The magnet that is scanning above the target backing plate is used to intensify the plasma and confine it in the region defined by the magnetic field. By scanning the magnet, the plasma is swept across the surface of the target, resulting in deposition of the film on the substrate opposite to the target. The plasma is generated by applying high voltage to an inert gas (typically Ar, but alternately He, Ne, Kr or mixtures) that flows in the region between the target and the substrate. For certain applications, other gases may be mixed to the sputtering gas, such as H
2
, O
2
, N
2
, etc., to alter the composition and/or the properties of the sputtered film.
It would be advantageous if a process existed for improving the electrical characteristics associated with an amorphous silicon film deposited by sputtering.
It would be advantageous if a process existed for improving the sheet resistance of polycrystalline silicon film, annealed from a sputter deposited amorphous silicon film.
It would be advantageous if the above-mentioned polycrystalline silicon film could be fabricated using easily controlled process steps and inert materials.
SUMMARY OF THE INVENTION
Accordingly, a method is provided for forming a polycrystalline silicon (p-Si) film in an integrated circuit (IC) fabrication process. The method comprises: sputtering amorphous silicon (a-Si) material on a substrate; supplying an Ar gas mixture including a hydrogen content of no more than 4% volume (in the gas feed); forming an amorphous silicon film incorporating hydrogen; annealing the amorphous silicon film using a rapid thermal annealing or Excimer laser process; and, forming a polycrystalline silicon film having a crystalline content in the range from 95 percent (%) to 100%, as measured by Raman Spectroscopy or equivalent measurement means, and a hydrogen content in the range from 1% atomic weight (at %) to 3 at %.
Also provided is a polysilicon (p-Si) film, such as might be used in the fabrication of a thin film transistor (TFT). The polycrystalline silicon film comprises a pre-anneal amorphous silicon (a-Si) film having a content of no more than 4% hydrogen, by atomic weight, and a post-anneal polycrystalline silicon film having a crystalline content in the range from 95% to 100%, and a hydrogen content in the range from 1 at % to 3 at %.
Additional details of the polycrystalline silicon film, polycrystalline silicon film fabrication process, and a pre-anneal film are provided below.
REFERENCES:
patent: 5723034 (1998-03-01), Ohmi
patent: 6261877 (2001-07-01), Yamazaki et al.
patent: 63-031175 (1988-02-01), None
Article entitled, “Low-Temperature Polysilicon Thin-Film Transistors Fabricated from Laser-Processed Sputtered-Silicon Films”, by Gary K. Giust et al., published in IEEE Electron Device Letters, vol. 19, No. 9, Sep. 1998, pp. 343-344.
Article entitled, “Laser-Processed Thin-Film Transistors Fabricated from Sputtered Amorphous-Silicon Films”, by G. K. Giust & T. W. Sigmon, published in IEEE Transactions on Electron Devices, vol. 47, No. Jan. 1, 2000, pp. 207-213.
Article entitled, “Characteristics of Hydrogenated Amorphous Silicon Thin Film Transistors Fabricated by D.C. Magnetron Sputtering”, by A. Kolodziej and S. Nowak, published in Thin Solid Films, 175 (1989) pp. 37-42.
Krieger Scott C.
Rabdau Matthew D.
Ripma David C.
Sharp Laboratories of America Inc.
LandOfFree
System and method for sputtering silicon films using... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with System and method for sputtering silicon films using..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and System and method for sputtering silicon films using... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3152789