Superconductive transition metal carbonitride fibers and method

Details Superconductive transition metal carbonitride fibers and method Superconductive transition metal carbonitride fibers and method

1973-09-13

1976-04-20

Sebastian, Leland A.

Compositions

Electrically conductive or emissive compositions

Elemental carbon containing

29599, 252516, 423364, 423371, H01B 106

Patent

active

039518701

ABSTRACT:
Fine diameter continuous multifilament superconductor yarns comprising niobium carbonitride may be prepared. The fibers of which the yarn is composed possess a very high transition temperature (T.sub.c of 17.degree.K) combined with a good upper critical field (H.sub.c2 of 125 kG) and critical current density (J.sub.c of 10.sup.5 amps/cm.sup.2 at 40 kG). This invention provides excellent superconductor materials in the form of continuous fine diameter multifilament yarn.

REFERENCES:
patent: 3364099 (1968-01-01), Forshey et al.
patent: 3380935 (1968-04-01), Ring
"Superconductivity of Cubic Niobium Carbo-Nitrides", J. Phys. Chem. Solids, Pergamon Press 1967, Vol. 28, pp. 333-341.
Chemical Abstracts, Vol. 78, 1973, 7260d, "Development on Process for Producing Continuous Fine Diameter Filaments of Superconductors".

Affiliated with

Also associated with

Rating

Superconductive transition metal carbonitride fibers and method does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Superconductive transition metal carbonitride fibers and method , we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Superconductive transition metal carbonitride fibers and method will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-1586251