Semiconductor device manufacturing: process – Coating with electrically or thermally conductive material – Insulated gate formation
Reexamination Certificate
1999-08-02
2002-11-05
Chaudhuri, Olik (Department: 2813)
Semiconductor device manufacturing: process
Coating with electrically or thermally conductive material
Insulated gate formation
C438S652000, C438S657000, C438S614000
Reexamination Certificate
active
06475892
ABSTRACT:
TECHNICAL FIELD
The present invention relates to a method of manufacturing a semiconductor device having accurate and uniform polysilicon gates and underlying gate oxides. The present invention is applicable to manufacturing high speed integrated circuits having submicron design features and high conductivity reliable interconnect structures.
BACKGROUND ART
Current demands for high density and performance associated with ultra large scale integration require design rules of about 0.18 microns and under, increased transistor and circuit speeds and improved reliability. As device scaling plunges into the deep sub-micron ranges, it becomes increasingly difficult to maintain performance and reliability.
Devices built on the semiconductor substrate of a wafer must be isolated. Isolation is important in the manufacture of integrated circuits which contain a plethora of devices in a single chip because improper isolation of transistors causes current leakage which, in turn, causes increased power consumption leading to increased noise between devices.
In the manufacture of conventional complementary metal oxide semiconductor (CMOS) devices, isolation regions, called field dielectric regions, e.g., field oxide regions, are formed in a semiconductor substrate of silicon dioxide by local oxidation of silicon (LOCOS) or by shallow trench isolation (STI). A conductive gate, such as polysilicon, is also formed on the substrate, with a gate oxide layer in between.
A polysilicon layer is deposited on gate oxide. Thereafter, a patterned photoresist mask is formed on the polysilicon layer and the polysilicon layer—oxide layer is etched to form conductive gates with a gate oxide layer in between. Dielectric spacers are formed on sidewalls of the gate, and source/drain regions are formed on either side of the gate by implantation of impurities.
Photolithography is conventionally employed to transform complex circuit diagrams into patterns which are defined on the wafer in a succession of exposure and processing steps to form a number of superimposed layers of insulator, conductor and semiconductor materials. Scaling devices to smaller geometries increases the density of bits/chip and also increases circuit speed. The minimum feature size, i.e., the minimum line-width or line-to-line separation that can be printed on the surface, controls the number of circuits that can be placed on the chip and directly impacts circuit speed. Accordingly, the evolution of integrated circuits is closely related to and limited by photolithographic capabilities.
An optical photolithographic tool includes an ultraviolet (UV) light source, a photomask and an optical system. A wafer is covered with a photosensitive layer. The mask is flooded with UV light and the mask pattern is imaged onto the resist by the optical system. Photoresists are organic compounds whose solubility changes when exposed to light of a certain wavelength or x-rays. The exposed regions become either more soluble or less soluble in a developer solvent.
There are, however, significant problems attendant upon the use of conventional methodology to form conductive gates with gate oxide layers in between on in a semiconductor substrate. For example, when a photoresist is formed on a highly textured surface such as polysilicon, and exposed to monochromatic radiation, undesirable standing waves are produced as a result of interference between the reflected wave and the incoming radiation wave. In particular, standing waves are caused when the light waves propagate through a photoresist layer down to the polysilicon layer, where they are reflected back up through the photoresist.
These standing waves cause the light intensity to vary periodically in a direction normal to the photoresist, thereby creating variations in the development rate along the edges of the resist and degrading image resolution. These irregular rejections make it difficult to control critical dimensions (CDs) such as linewidth and spacing of the photoresist and have a corresponding negative impact on the CD control of the conductive gates and gate oxide layers.
There are further disadvantages attendant upon the use of conventional methodologies. For example, distortions in the photoresist are further created during passage of reflected light through the highly reflective polysilicon layer which is typically used as a hardmask for etching. Specifically, normal fluctuations in the thickness of the polysilicon layer cause a wide range of varying reflectivity characteristics across the polysilicon layer, further adversely affecting the ability to maintain tight CD control of the photoresist pattern and the resulting conductive gates and gate oxide layers.
Highly reflective substrates accentuate the standing wave effects, and thus one approach to addressing the problems associated with the high reflectivity of the silicon nitride layer has been to attempt to suppress such effects through the use of dyes and anti-reflective coatings below the photoresist layer. For example, an anti-reflective coating (ARC),.such as a polymer film, has been formed directly on the polysilicon layer. The ARC serves to absorb most of the radiation that penetrates the photoresist thereby reducing the negative effects stemming from the underlying reflective materials during photoresist patterning. Unfortunately, use of an ARC adds significant drawbacks with respect to process complexity. To utilize an organic or inorganic ARC, the process of manufacturing the semiconductor chip must include a process step for depositing the ARC material, and also a step for prebaking the ARC before spinning the photoresist.
There exists a need for a cost effective, simplified processes enabling the formation of an ARC prevent the negative effects stemming from the underlying reflective materials during photoresist patterning.
The present invention addresses and solves the problems attendant upon conventional multi-step, time-consuming and complicated processes for manufacturing semiconductor devices utilizing an ARC.
DISCLOSURE OF THE INVENTION
An advantage of the present invention is an efficient cost-effective method of manufacturing a semiconductor device with accurately formed conductive gates and gate oxide layers.
Additional advantages of the present invention will be set forth in the description which follows, and in part, will become apparent to those having ordinary skill in the art upon examination of the following or may be learned from the practice of the present invention. The advantages of the present invention may be realized and obtained as particularly pointed out in the appended claims.
According to the present invention, the foregoing and other advantages are achieved in part by a method of manufacturing a semiconductor device, which method comprises:
forming an oxide-layer on a semiconductor substrate;
forming a polysilicon layer on the oxide layer in a chamber;
forming a silicon carbide coating on the polysilicon layer in the chamber; and
forming a photoresist mask on the silicon carbide coating.
Additional advantages of the present invention will become readily apparent to those skilled in this art from the following detailed description, wherein embodiments of the present invention are described, simply by way of illustration of the best mode contemplated for carrying out the present invention. As will be realized, the present invention is capable of other and different embodiments, and its several details are capable of modifications in various obvious respects, all without departing from the present invention. Accordingly, the drawings and description are to be regarded as illustrative in nature, and not as restrictive.
REFERENCES:
patent: 5710067 (1998-01-01), Foote et al.
patent: 5846859 (1998-12-01), Lee
patent: 6130102 (2000-10-01), White et al.
patent: 6218292 (2001-04-01), Foote
AAdvanced Micro Devices, Inc.
Chaudhuri Olik
Huynh Yennhu B.
LandOfFree
Simplified method of patterning polysilicon gate in a... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Simplified method of patterning polysilicon gate in a..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Simplified method of patterning polysilicon gate in a... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2954392