Semiconductor device manufacturing: process – Formation of semiconductive active region on any substrate – Amorphous semiconductor
Patent
1998-06-10
2000-04-11
Elms, Richard T.
Semiconductor device manufacturing: process
Formation of semiconductive active region on any substrate
Amorphous semiconductor
438487, 438505, H01L 2120
Patent
active
06048781&
ABSTRACT:
A semiconductor processing method of providing a polysilicon layer atop a semiconductor wafer comprises the following sequential steps: a) depositing a first layer of arsenic atop a semiconductor wafer; b) depositing a second layer of silicon over the arsenic layer, the second layer having an outer surface; c) first annealing the wafer at a temperature of at least about 600.degree. C. for a time period sufficient to impart growth of polycrystalline silicon grains in the second layer and providing a predominately polysilicon second layer, the first annealing step imparting diffusion of arsenic within the second layer to promote growth of large polysilicon grains; and d) with the second layer outer surface being outwardly exposed, second annealing the wafer at a temperature effectively higher than the first annealing temperature for a time period sufficient to outgas arsenic from the polysilicon layer. As an alternate consideration, the layer of silicon could be in situ provided with an effective quantity of As during deposition.
REFERENCES:
patent: 5183777 (1993-02-01), Doki et al.
patent: 5242507 (1993-09-01), Iverson
patent: 5310698 (1994-05-01), Wild
patent: 5491107 (1996-02-01), Turner et al.
patent: 5529937 (1996-06-01), Zhang et al.
patent: 5531182 (1996-07-01), Yonehara
patent: 5532183 (1996-07-01), Sugawara
patent: 5597741 (1997-01-01), Sakamoto et al.
patent: 5923997 (1999-07-01), Mitanga et al.
patent: 5930658 (1999-07-01), Ibok
patent: 5960323 (1999-09-01), Wakita et al.
patent: 5976918 (1999-11-01), Matsuoka et al.
patent: 5985741 (1999-11-01), Yamazaki et al.
patent: 5994164 (1999-11-01), Fonash et al.
T. Noguchi et al. Jpn. J. Appl. Phys., 24(6)(1985)L434 "Grain growth . . . of super thin polysilicon films . . . ", Jun. 1985.
G. Chaussemy et al., Phys. Stat. Sol. A124 (1991) 103 "RTA of arsenic implanted monocrystalline silicon: dopant redistribution and outdiffusion", 1991 month unknown.
H. Kerkow et al., Phys. Stat. Sol. A76 (1983) K203 "Kinetics of furnace annealing of As-implanted Si", 1983 month unknown.
C.V. Thomoson, "Grain Growth in Polycrysatalline Silicon Films", Dept. of Materials Science and Engineering Massachusetts Institute of Technology, Cambridge, MA. Mat.Res. Soc. Symp. Proc. vol. 106, 1988.
Gorkum et al., "Controlled Atomic Layer Doping and ALD MOSFET Fabrication in Si", Japanese Journal of Applied Physics, vol. 26, No. 12, pp. L1933-1935, Dec. 1987.
Gong et al., "A Metal-Oxide-Silicon Field-Effect Transistor Made by Means of Solid-Phase Doping", J. Appl. Phy., 65 (11), pp. 4435-4437, Jun. 1989.
Aoyama et al., "Leakage Currents Reduction of Poly-Si TFT's by Two Step Annealing", Extended Abstracts of the 22nd (1990 International) Conference on Sol. St. Dev. and Materials, pp. 389-392.
Translation of JP5-129204, May 1993.
Manning Monte
Turner Charles L.
Elms Richard T.
Lebentritt Michael S.
Micro)n Technology, Inc.
LandOfFree
Semiconductor processing method for providing large grain polysi does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Semiconductor processing method for providing large grain polysi, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Semiconductor processing method for providing large grain polysi will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1176137