Paper making and fiber liberation – Processes and products – Non-fiber additive
Reexamination Certificate
1999-08-27
2001-02-13
Silverman, Stanley S. (Department: 1731)
Paper making and fiber liberation
Processes and products
Non-fiber additive
C162S180000, C162S181100, C162S143000, C162S183000, C106S238000
Reexamination Certificate
active
06187143
ABSTRACT:
The present invention relates to a process for the manufacture of hydrophobic paper or hydrophobic board by using rosin sizing. The invention also relates to a sizing composition which contains rosin size.
Rosin and rosin-based sizes have long been used for the sizing of board and paper when the stock is acidic or almost neutral. Size is used by adding it to the fiber stock from which a web is later formed on the wire. The purpose of the use of size is to increase the hydrophobicity of the paper or board.
Rosin sizing is based on the forming of electrostatic bonds between the size and the cellulose or other fibers or solids in the stock or the paper web. With the present-day reaction products of anhydrides and rosinous substances a better sizing result is obtained than with products which contain only rosinous substances. Such reaction products are called reinforced rosin sizes. In general, an aqueous dispersion is formed of the sizes in order to facilitate dosing. Stable dispersions of rosin or rosin-based products are well known.
Rosin is a solid substance present in the pitch of pine trees, Its principal component is abietic acid, which can react with fumaric acid, maleic acid or its anhydride, whereby the active agent of reinforced sizes is formed. These reinforced sizes can be treated further with formaldehyde and alcohols.
The preparation of rosin sizes is generally known technology.
The preparation and formulation of a rosin size is described in, for example, patent FI-C-77884.
Rosin sizes are in general stabilized with substances which form a shielding colloid around the resin particles. Usually there is used for this purpose a modified starch or natural polymers or synthetic polymers, such as polyvinyl alcohols, polyvinyl pyrrolidone or cellulose derivatives, such as carboxymethyl cellulose. The use of rosin size stabilization agents is generally known technology.
Aluminum salts, which may be of any type which is commonly known to be usable for the sizing and hydrophobification of cellulose and other fibers, such as aluminum sulfate, aluminum chloride, polyaluminum chloride, polyaluminum sulfate, and mixtures thereof, are essential for the use and performance of a rosin size. It is generally known that the amount of alum required in rosin sizing is approx. 1.5 times that of the rosinous substance (W. F. Reynolds, The Sizing of Paper, second edition, 1989, pages 1-31), and the highest possible cationic charge is obtained when 1-1.5 equivalents of the Al
3+
ion are neutralized with the OH ion. In this case the pH is 4-5. It is known that Ca
2+
and Mg
2+
ions weaken the sizing effect by decreasing the negative charge of the rosin size and by forming disadvantageous precipitates. Problems appear in particular when the pulps are prepared in hard water or when calcium carbonate is used as a filler. Calcium carbonate buffers the pulp within a pH range of 7-8. Efforts have been made to improve the performance of rosin size in this environment by using dispersion sizes of very small particle size. By means thereof, rosin sizes can be caused to react with aluminum only in the drying section, where water no longer serves as the continuous phase and the size is no longer in contact with carbonate. On the other hand, efforts have been made to increase the interaction between aluminum and rosin size by dosing them at the same location into the short cycle of diluted pulp.
The quality properties of board for the packaging of liquids include not only hydrophobicity of the board, which is generally defined as Cobb numbers, but also resistance to the penetration of lactic acid from the edge of the board (lactic acid REP) and resistance to the penetration of hydrogen peroxide (peroxide REP). The numbers illustrate the penetration of the said solutions from the board edge towards its cross-sectional area.
Resistance to peroxide is necessary since the board is treated in a hot hydrogen peroxide bath before the manufacture of packaging. Resistance to lactic acid is necessary or the packaging being resistant to the milk and other liquid food products to be stored therein. In general, in order to achieve effective sizing, an AKD (alkyl ketene dimer) size is also used in the manufacture of liquid packaging board. An AKD size which can be used together with a rosin size is usually an aqueous dispersion.
The concentration of AKD in the products may be 0.5-30% by weight. In general there are used for the formulation of AKD various starches, which are generally cationated either with quaternary amines, in which case the starch retains its cationic charge even in alkaline conditions, or with primary, secondary or tertiary amines, the charge of which is dependent on the pH. The amount of starch may be 0.1-10 times the proportion of AKD. In general there are used for the dispersing of an AKD wax various anionic compounds, such as lignosulfates, aliphatic or aromatic sulfonates, nonionic surfactants such as fatty acid or fatty alcohol ethoxylates, or cationic surfactants such as fatty acid amines or imidazolines. It is also possible to use, for the stabilization of an AKD dispersion, polymers such as polyethylene irine, polyepiamine, polydimethyldiallyl or dicyandiamide compounds, polyacrylamide or polyacrylic acid and its salts. It is generally known that the amount of stabilization chemicals is 1-200% by weight of the amount of AKD. By the use of polymers it is possible not only to improve the stability of the product but also to affect the performance of the product in paper or board. The adding of stabilizing chemicals is prior art commonly used in the formulation of AKD products.
It is generally known that rosin sizing is used specifically for affecting the peroxide resistance of board, whereas alkyl ketene dimer (AKD) primarily affects its lactic acid resistance. AKD size can be dosed to the pulp in the board machine before, after or simultaneously with resin size, depending on the manner in which the board machine is run. The dosing order does not affect the performance of the invention.
It has been observed, surprisingly, that peroxide resistance specifically derived from rosin sizing can be increased by using complexing agents which are dosed together with the rosin size or are incorporated into the product. Complexing agents suitable for this purpose include agents which react slowly with aluminum compounds and rapidly with alkaline earth metal ions.
According to the invention there is thus provided a process for the manufacture of hydrophobic paper or board by using rosin sizing, the process being characterized in that an organic complexing agent is used together with the rosin size.
The term chelating agent is also used for complexing agents.
According to the invention, the organic complexing agent can be incorporated into the rosin size or it can be dosed at the same location in the paper or board machine as the rosin size.
The process according to the invention is especially suitable for sizing together with an aluminum compound, such as aluminum sulfate, aluminum chloride, polyaluminum chloride, polyaluminum sulfate or mixtures of these.
Suitable complexing agents which can be used in accordance with the invention include
a) aminopolycarboxylic acids
b) N-bis- or tris-[(1,2-dicarboxylethoxy)ethyl]amines and
c) phosphonic acids.
The complexing agents cited above may be in the form of an acid or a salt. Suitable salts include alkali metal salts and ammonium salt. Sodium and potassium salts are preferred salts.
Preferred complexing agents of group a) include amino polycarboxylic acids having the following general Formula I.
where
A is —CH
2
COOH,
B is —CH
2
COOH or —CH
2
CH
2
OH,
x is 0-6, preferably 0-3,
y is 0-6, preferably 0-2,
a is 2-10, preferably 2-4, and
b is 2-10, preferably 2-6.
Especially preferable compounds according to Formula I include
ethylene diamine tetra-acetic acid, i.e. EDTA (B=A, x=0, b=2 and y=1),
diethylene triamine penta-acetic acid, i.e. DTPA (B=A, x=1, a=2, b=2 and y=1),
Juppo Ari
Paren Aarto
Greenberg & Traurig, LLP
Halpern Mark
Kemira Chemicals Oy
Manak Joseph M.
Silverman Stanley S.
LandOfFree
Process for the manufacture of hydrophobic paper or... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for the manufacture of hydrophobic paper or..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the manufacture of hydrophobic paper or... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2589505