Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
2001-07-06
2003-06-10
Seidleck, James J. (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C525S384000, C524S386000, C424S448000
Reexamination Certificate
active
06576712
ABSTRACT:
TECHNICAL FIELD
This invention relates to preparation of adhesive compositions. More particularly, the invention relates to preparation of hydrophilic pressure sensitive adhesive (PSA) compositions having optimized adhesive properties and that are useful, for example, in transdermal drug delivery systems and other medical, pharmaceutical and cosmetic products that adhere to the skin or other body surface. The invention has utility in a number of fields, including transdermal drug delivery, iontophoretic systems, biomedical electrode fabrication, wound healing, and skin care and cosmetic products.
BACKGROUND
Pressure-sensitive adhesives are well known and have been used for many years in a variety of industrial, consumer and medical applications. Pressure-sensitive adhesives are characterized as being normally tacky and exhibiting instant tack when applied to a substrate. Many polymers have been used to manufacture pressure sensitive adhesives as, for example, acrylic and methacrylic ester homo- or copolymers, butyl rubber-based systems, silicones, urethanes, vinyl esters and amides, olefin copolymer materials, natural or synthetic rubbers, and the like. All the PSAs are elastomers, i.e. they exhibit viscoelastic properties typical of rubbers.
Pressure sensitive adhesives are used extensively in transdermal drug delivery devices, or “patches,” that adhere to the skin or mucosal tissue during use. Adhesive, transport, reservoir and biological properties of polymeric composites constitute a basis for their application in transdermal drug delivery systems, as follows:
Adhesive: High tack coupled with an optimum slip-stick transition point.
Transport: Drug release kinetics controlled in terms of transdermal delivery rate and the functional lifetime of device.
Reservoir: Drug compatibility and ability to be stored in a stable form tailored to the incorporated drug of interest.
Biological: No toxicity, skin irritation and sensitization.
Such diverse requirements are difficult to combine in a single system.
Examples of pressure sensitive adhesives that have been proposed for use in transdermal drug delivery systems include polysiloxanes (e.g., polydimethyl siloxanes, polydiphenyl siloxanes, and siloxane blends), polyisobutylenes, polyacrylates, acrylic acid-acrylate copolymers (e.g., copolymers of acrylic acid copolymers with 2-ethylhexyl acrylate or isooctyl acrylate), and tacky rubbers such as polyisobutene, polybutadiene, polystyrene-isoprene copolymers, polystyrene-butadiene copolymers, and neoprene (polychloroprene). All of these PSAs are hydrophobic polymers and their common disadvantage is a loss in adhesion toward hydrated substrates.
“Bioadhesion” is defined as a pressure sensitive adhesion with respect to highly hydrated biological tissues such as mucosal tissue. In contrast to conventional PSAs (rubber, polysiloxanes and acrylates) that adhere mainly to dry substrates, bioadhesives (BAs) exhibit good tack when adhered to hydrated biological substrates. To be bioadhesive, water should provide a plasticizing effect on a polymer, i.e., the polymer should be hydrophilic. For example, the range of typical BAs includes slightly cross-linked polyacrylic and polymethacrylic acids (EP 0371 421) as well as blends of hydrophilic cellulose derivatives (40-95%) with polyethylene glycol (PEG) (U.S. Pat. No. 4,713,243).
Bioadhesives become tacky as the crosslinked polymer swells in significant quantities of water. The cohesive strength of highly swollen hydrophilic polymers is generally low and the BAs thus differ from the PSAs in this regard.
For a number of practical purposes, it can be highly useful to have a range of PSA and BA polymeric materials of different hydrophilicity and thus different solubilities in water or in the liquids secreted by the skin and mucosa (sweat, mucus, saliva etc.). Attempts to combine the properties of PSAs and BAs have been described by Biegajski et al. in U.S. Pat. No. 5,700,478, where a water-soluble pressure-sensitive mucoadhesive was obtained by blending of 95-40% polyvinylpyrrolidone (PVP) with 0-50% hydroxypropyl cellulose (HPC) and 11-60% glycerol. Other examples of hydrophilic polymer blends coupling the properties of PSAs and BAs involve polyacrylic acid-polyvinyl alcohol (PAA-PVA) interpolymeric complexes formed by hydrogen bonding between the monomer units of the complementary polymers chains and plasticized with PEG-200, glycerol or polypropylene glycol (PPG), molecular weight 425 g/mol (German Patent Application DE 42 19 368).
The ideal performance characteristics of an adhesive intended for use on human skin and/or mucosal tissue present difficult and conflicting technical requirements. Initially, of course, the pressure sensitive adhesive should be suitable for long-term skin contact, and permeable to and physically and chemically compatible with the active agent and any permeation enhancers or other vehicles or additives that are present. The ideal adhesive should also be nonirritating, noncomedogenic and nonsensitizing, yet bond quickly to skin or mucosal tissue at the intended site of use with only very slight pressure. The adhesive should maintain its bond for as long a period of time as necessary and be resistant to inadvertent removal, yet be easily removed without removing any skin or leaving a residue (a suitable strength of an adhesive joint with the skin ranges from about 200 to 400 N/m under the 180 degree peel test). High tack (i.e., greater than about 50 g/cm
2
) should be coupled with an optimum transition point from adhesive to cohesive failure. Furthermore, the adhesive should not be weakened or destroyed by exposure to moisture or high humidity. Finally, in order to protect a wound or maintain the integrity of placement of an electrode or other device, the adhesive should resist skin movement and be able to transfer a mechanical load from the adhesive backing to the skin.
For many pharmaceuticals, the solubility of the active agent in the reservoir of a transdermal drug delivery device is of decisive importance. With higher solubility, it is possible to increase the rate of transdermal delivery (i.e., the rate at which the active agent migrates from the device and into the skin or mucosal tissue). Because many therapeutic agents are ionogenic organic substances having a higher solubility in hydrophilic media than in lipophilic media, adhesive reservoirs based on hydrophilic polymers would be more versatile than adhesive reservoirs based on hydrophobic polymers. Furthermore, as noted above, pressure sensitive adhesives for application to mucosal tissue should adhere well to hydrated substrates, and hydrophilic adhesives would therefore be ideal.
General advantages of hydrophilic adhesives are as follows:
1. Hydrophilic adhesives can provide greater adhesion compared with hydrophobic adhesives, because the surface energy of hydrophilic adhesives is typically higher and closer to that of biological substrates such as skin and mucosal membranes.
2. Hydrophilic adhesives are compatible with a wide variety of drugs, excipients and additives.
3. The plasticizing effect of water sorbed by hydrophilic adhesives from hydrated skin or mucosal tissues enhances adhesion, in contrast to hydrophobic adhesives.
4. The enhanced solubility of drugs in hydrophilic adhesives facilitates control over drug release kinetics.
5. With hydrophilic adhesives, based on hydrophilic polymers, there is an expanded capability to control and manipulate the adhesive-cohesive balance.
6. The adhesive properties of hydrophilic polymers are considerably less sensitive to their molecular weight than those of hydrophobic polymers, as a result of specific intramolecular and intermolecular interaction within hydrophilic adhesives.
In order to increase the hydrophilicity of an adhesive composition, hydrophobic PSAs have been “hydrophilized” by incorporation of non-tacky hydrophilic polymers and fillers into a hydrophobic adhesive. Thus, polyisobutylene (PIB) PSA has been hydrophilized by incorporation of cellulose and cellulose derivatives (U.S. Pat. No. 4,231,369)
Chalykh Anatoly E.
Cleary Gary W.
Feldstein Mikhail M.
Plate Nicolai A.
A. V. Topchiev Institute of Petrochemical Synthesis
Canaan Karen
Reed Dianne E.
Reed & Eberle LLP
LandOfFree
Preparation of hydrophilic pressure sensitive adhesives... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Preparation of hydrophilic pressure sensitive adhesives..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Preparation of hydrophilic pressure sensitive adhesives... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3104351