Stock material or miscellaneous articles – Liquid crystal optical display having layer of specified... – Alignment layer of specified composition
Reexamination Certificate
1998-11-02
2001-11-27
Copenheaver, Blaine (Department: 1772)
Stock material or miscellaneous articles
Liquid crystal optical display having layer of specified...
Alignment layer of specified composition
C428S001100, C428S001200, C428S001210, C428S001400, C428S001600, C349S056000, C349S158000
Reexamination Certificate
active
06322860
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to plastic substrates. In particular, the present invention relates to the use of polyglutarimides as substrates for electronic display applications.
Electronic displays are devices used to exhibit electronically generated graphical and textual images. There are many different types of electronic displays, and many more are being developed. Among the more familiar types of electronic displays are: liquid crystal displays (“LCDs”); cathode ray tubes (“CRTs”); arrays of light-emitting diodes (“LEDs”); plasma display panels (“PDP”); field emission displays (“FED”); and electroluminescent (“EL”) displays. As electronics become more and more miniaturized, there has been an increased demand for portable devices. LCDs and EL displays are particularly useful in such portable electronic devices due to their light weight and low power consumption relative to other display technologies.
The basic LCD unit is a cell made of two transparent sheets (referred to in the art as substrates) having conductive coatings, wherein the coated sheets are sandwiched together along the edge with an adhesive cell-sealing material and filled with liquid crystal and spacers. Additional components which may be included in a liquid crystal display cell include, for example, alignment layers used to align the liquid crystal fluid, color filter coatings, active electronic devices such as thin film transistors, and polarizers. EL displays are generally composed of at least one transparent substrate having a conductive coating, and make use of electroluminescent phosphors as the image generating medium. Electronic devices made with these types of displays include other electronic components, such as drivers, which are used to generate the image on the electronic display.
Substrates for display devices have typically been made of optical quality glass or quartz because these materials meet requirements for optical clarity and flatness, and because these materials have good gas and moisture barrier properties and good thermal and chemical resistance. On the other hand, glass and quartz are brittle and subject to breakage, and they are therefore limited in usefulness in thin sheets or films less than 1 mm in thickness.
Various plastics have been proposed as replacement substrates because they are lighter weight, may be formed into thinner sheets or even films, and are more resistant to breakage. High temperature plastics (those having Tg of at least 150° C.) are preferred in order to provide adequate thermal stability during the display manufacturing process. Such materials include, for example, thermoplastic resins such as polyacrylates, polysulfones, polycarbonates and polyimides.
U.S. Pat. No. 4,802,742 (Ichikawa et al) describes the use of certain plastics, such as polyether sulfone and polycarbonate, as plastic substrate materials for LCDs. Polyether sulfone has a Tg of 220° C. and is therefore preferred over other plastics for use as substrate material; however, this resin has an amber color, and is therefore limited in application to thin films. Polycarbonate has less color and a higher white light transmission than polyether sulfone, but its Tg (150° C.) is undesirably low, and it has relatively high stress-optic coefficient (resulting in higher birefringence).
Electronic displays made with these types of plastic substrate materials have been under development for about 20 years, but they have enjoyed only limited commercial success because all of these plastics have limitations which interfere with their performance as substrate materials. These limitations include unsatisfactory: optical quality, flatness, solvent resistance, thermal resistance, and gas barrier properties. Coatings have typically been used to improve some of these deficiencies in the plastic substrates.
EP 770 899 A1 (Paczkowski) discloses a method and composite for double sided processing of plastic substrates useful as plates in liquid crystal displays such that the composite can be separated after processing to form both sides of a liquid crystal cell. The focus of this application is on a method of simultaneously processing two pieces of plastic substrate to minimize the differences in processing conditions between the two plates which form the sides of the LCD cell. There is no discussion in this application of selection of substrate materials except with regard to UV absorption of the material and there is no discussion of coatings for the substrate other than ITO.
There remains a need for a plastic substrate material which has good optical quality, flatness, solvent resistance, thermal resistance, and gas barrier properties.
STATEMENT OF THE INVENTION
The present invention is directed to a plastic substrate for electronic display applications, including a polyglutarimide sheet of 25 mm or less having Tg of at least 150° C.; total white light transmission of at least 88%; and a shrinkage of no more than 0.1%. This substrate further includes optional layers coated on the polyglutarimide sheet, such layers selected independently from crosslinked coatings, barrier coatings, and clear conductive coatings.
The present invention is also directed to a polyglutarimide having an imidization level of at least 95% and an acid level of no more than 1 wt %.
REFERENCES:
patent: 1631805 (1927-06-01), Ferngren
patent: 1753768 (1930-04-01), Blair
patent: 1772448 (1930-08-01), Allen
patent: 1829641 (1931-10-01), Ferngren
patent: 1836394 (1931-12-01), Reece
patent: 1841579 (1932-01-01), Fraser
patent: 1872550 (1932-08-01), Allen
patent: 1891371 (1932-12-01), Danner
patent: 1891373 (1932-12-01), Danner
patent: 3149949 (1964-09-01), Dockerty et al.
patent: 3451798 (1969-06-01), Simon
patent: 3537834 (1970-11-01), Simon
patent: 4727117 (1988-02-01), Hallden-Abberton et al.
patent: 4802742 (1989-02-01), Ichikawa et al.
patent: 5022737 (1991-06-01), Yamamotto et al.
patent: 5076987 (1991-12-01), Wank et al.
patent: 5084517 (1992-01-01), Hallden-Abberton
patent: 5149481 (1992-09-01), Gross et al.
patent: 5242742 (1993-09-01), Funk et al.
patent: 5286436 (1994-02-01), Funk et al.
patent: 5776641 (1998-07-01), Roberts et al.
patent: 5911899 (1999-06-01), Yoshikai et al.
patent: 6183829 (2001-02-01), Daecher et al.
patent: 0 145 355 A2 (1985-06-01), None
patent: 0 232 795 A2 (1987-08-01), None
patent: 0 234 726 A2 (1987-09-01), None
patent: 0 318 197 A2 (1989-05-01), None
patent: 0 570 135 A2 (1993-11-01), None
patent: 0 770 899 A1 (1997-02-01), None
patent: WO 92/04386 (1992-03-01), None
Fields Steven David
Hallden-Abberton Michael Paul
Liss Audrey Brenda
Stein Alan Daniel
Cairns S. Matthew
Chevalier Alicia
Copenheaver Blaine
Frickey Darryl F.
Lemanowicz John L.
LandOfFree
Plastic substrates for electronic display applications does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Plastic substrates for electronic display applications, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Plastic substrates for electronic display applications will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2573999