ABSTRACT:
TECHNICAL FIELD
This invention relates to physical vapor deposition targets, to conductive integrated circuit metal alloy interconnections, and to electroplating anodes.
BACKGROUND OF THE INVENTION
Aluminum and its alloys are common metal materials used in metal interconnects in the fabrication of integrated circuitry on semiconductor wafers. Yet as circuitry density increases and operating speed increases, aluminum's electrical resistance is expected to prevent its use in many next generation circuits. Copper has been proposed as a strong candidate to replace aluminum and its alloys due to copper's low bulk resistivity of 1.7 microohms.cm at near 100% purity (i.e., greater than 99.999% copper). Further, it has electromigration resistance compared to that of aluminum and its alloys of about 10 times or greater.
One problem associated with pure copper interconnects concerns abnormal grain growth or thermal stability in the deposited film. Further, such abnormal and undesired grain growth can reduce the film's electromigration resistance. Low thermal stability is defined as, and abnormal grain growth is characterized by, a tendency of the individual crystal grains within copper to grow when exposed to a certain temperature. The higher the temperature at which a material recrystallizes or starts to grow larger grains, the higher the thermal stability of the material.
Elemental copper and its alloys can be deposited in integrated circuitry fabrication using a number of techniques, including chemical vapor deposition, physical vapor deposition and electrochemical deposition, such as electroplating. Ideally when deposited, the copper comprising sputtering target will have substantially uniform microstructure, a fine grain size, and preferred crystal orientation in order to achieve desired sputtering performance and resultant thin film formation and properties.
SUMMARY
The invention includes conductive integrated circuit metal alloy interconnections, physical vapor deposition targets and electroplating anodes. In one implementation, a physical vapor deposition target includes an alloy of copper and silver, with the silver being present in the alloy at from less than 1.0 at % to 0.001 at %. In one implementation, a physical vapor deposition target includes an alloy of copper and silver, with the silver being present in the alloy at from 50 at % to 70 at %. In one implementation, a physical vapor deposition target includes an alloy of copper and tin, with tin being present in the alloy at from less than 1.0 at % to 0.001 at %.
In one implementation, a conductive integrated circuit metal alloy interconnection includes an alloy of copper and silver, with the silver being present in the alloy at from less than 1.0 at % to 0.001 at %. In one implementation, a conductive integrated circuit metal alloy interconnection includes an alloy of copper and silver, with the silver being present in the alloy at from 50 at % to 70 at %. In one implementation, a conductive integrated circuit metal alloy interconnection includes an alloy of copper and tin, with tin being present in the alloy at from less than 1.0 at % to 0.001 at %.
In one implementation, an electroplating anode includes an alloy of copper and silver, with the silver being present in the alloy at from less than 1.0 at % to 0.001 at %. In one implementation, an electroplating anode includes an alloy of copper and silver, with the silver being present in the alloy at from 50 at % to 70 at %. In one implementation, an electroplating anode includes an alloy of copper and tin, with tin being present in the alloy at from less than 1.0 at % to 0.001 at %.
In other implementations, other useable copper alloys in physical vapor deposition targets, conductive integrated circuit metal alloy interconnections, and electroplating anodes include an alloy of copper and one or more other elements, the one or more other elements being present in the alloy at a total concentration from less than 1.0 at % to 0.001 at % and being selected from the group consisting of Be, Ca, Sr, Ba, Sc, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Ti, Zr, Hf, Zn, Cd, B, Ga, In, C, Se, Te, V, Nb, Ta, Cr, Mo, W, Mn, Tc, Re, Fe, Ru, Os, Co, Rh, Ni, Pd, Pt, Au, Tl, and Pb. An electroplating anode is formed to comprise one or more of the above alloys.
In other implementations, the invention contemplates metal alloys for use as a conductive interconnection in an integrated circuit.
REFERENCES:
patent: 4786469 (1988-11-01), Weber et al.
patent: 5023698 (1991-06-01), Kobayashi et al.
patent: 5590389 (1996-12-01), Dunlop et al.
patent: 5719447 (1998-02-01), Gardner
patent: 5833820 (1998-11-01), Dubin
patent: 5895562 (1999-04-01), Dubin
patent: 5972192 (1999-10-01), Dubin et al.
patent: 6162726 (2000-12-01), Dubin
patent: 0 335 383 (1989-03-01), None
patent: 0 626 722 (1993-02-01), None
patent: 49007777 (1974-02-01), None
patent: WO 00/73531 (2000-12-01), None
Massalski, 18 Binary Alloy Phase Diagrams 18-19, 928-929, 936-937, 964-965 (1986).
Electromigration Properties of Copper-Zirconium alloy Interconnects, Y. Igarashi et al.,J. Vac. Sci. Technol. B 16(5), Sep./Oct. 1998, p. 2745-2750.
Directional and Preferential Sputtering-Based Physical Vapor Deposition, S.M. Rossnagel,1995 Elsevier Science S.A., p. 1-12.
Excellent Electro/Stress-Migration-Resistance Surface-Silicide Passivated Giant-Grain Cu-Mg alloy Interconnect Technology for Giga Scale Integration (GSI), T. Takewaki et al., 1995 IEEE, p. 95-253-95-256.
Materials Issues in Copper Interconnections, J.M.E. Harper, et al.,MRS Bulletin/Aug. 1994, p. 23-29.
Preparation of Low Resistivity Cu-1 at. %Cr Thin Films by Magnetron, C. Cabral, Jr., et al.,Journal of the Institute of Metals, Jun. 1951, p. 185-208.
International Critical Tables of Numerical Data, Physics, Chemistry and Technology,National Research Council of the United States of America, vol. I-VII, 1933, 6 pages.
Buehler Jane
Hargarter Hinrich
Li Jianxing
Nagano Shozo
Honeywell International , Inc.
Ip Sikyin
Wells St. John P.S.
LandOfFree
Physical vapor deposition target does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Physical vapor deposition target, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Physical vapor deposition target will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3246623