MOSFET gate insulating films with oxynitride and oxide

Active solid-state devices (e.g. – transistors – solid-state diode – Field effect device – Having insulated electrode

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C257S392000, C257S369000

Reexamination Certificate

active

06333541

ABSTRACT:

BACKGROUND OF THE INVENTION
This invention relates to a semiconductor device and a method of manufacturing the same, and more particularly to a MOSFET gate insulating film in a semiconductor device using two types of power supply voltage in a single chip and a method of manufacturing the same.
As integrated circuits are being required to operate much faster, the gate electrode length of a MOSFET grows finer at an increasingly rapid pace. By 2000, the advent of an integrated circuit using MOSFETs with a gate electrode length on the order of about 0.15 &mgr;m to 0.1 &mgr;m is expected. In such a fine MOSFET, it is expected that the power supply voltage to bring out the optimum performance might more frequently differ from the power supply voltage determined by the interface with another device on the outside. For example, this corresponds to the following case: use of a power supply voltage of 2.5 V is preferable to the interface with an external device, whereas use of a power supply voltage of about 1.8 V is preferable to operating the relevant integrated circuit at high speed.
Another problem in miniaturizing MOSFETs arises from making the gate insulating film thinner. Specifically, the gate insulating film must be made thinner as the gate electrode length grows finer. In this case, when the electric field applied to the thin gate insulating film has reached 5 MV/cm or higher, the insulating film is more liable to be broken, decreasing the reliability.
For this reason, a semiconductor device required to operate at higher speed has employed such a structure including MOSFETs with different gate insulating films formed in a single chip and selectively using the MOSFETs with the gate insulating film thickness suitable for each power supply voltage.
Still another problem in making the gate insulating film thinner arises from: when p-type polysilicon is used for the gate electrode of a p-channel MOSFET with a fine gate length, p-type impurities, such as boron, included in the polysilicon pass through the thinner gate insulating film in various thermal processes carried out in the manufacturing process and diffuse throughout the substrate, which degrades the controllability of the threshold voltage. It is known that use of material including a trace of nitrogen for the gate insulating film is effective in dealing with the problem. For example, it is desirable that oxynitride should be used for a gate insulating film whose thickness is 6 nm or less.
Next, using FIG.
1
and
FIGS. 2A
to
2
D, a conventional semiconductor device and a method of manufacturing the semiconductor device will be explained. As shown in
FIG. 1
, element isolating regions
12
have been formed at the main surface of a silicon (Si) substrate
11
. In the element regions electrically separated by the element isolating regions
12
, diffused layers
13
and
14
acting as source/drain regions are formed. A gate insulating film
15
is formed on the silicon substrate
11
between the source/drain regions
13
. On the gate insulating film
15
, a gate electrode
16
is formed, thereby constructing a MOSFET Q
1
. A gate insulating film
17
is formed on the silicon substrate
11
between the source/drain regions
14
. A gate electrode
18
is formed on the gate insulating film
17
, thereby constructing a MOSFET Q
2
.
The MOSFET Q
1
constitutes an internal circuit. In the p-channel MOSFET in area A in which the MOSFET Q
1
has been formed, p-type material, such as boron-doped polysilicon, is used for the gate electrode
16
. In contrast, the MOSFET Q
2
formed in area B constitutes a circuit for exchanging signals and data with an external device. The MOSFET Q
1
formed in area A operates on about 1.8 V lower than MOSFET Q
2
formed in area B and the dimension (gate length) of, for example, the gate electrode is 180 nm. In the MOSFET Q
1
, the gate insulating film
15
requires a thickness of about 4 nm to provide the optimum performance. In contrast, because an external power supply voltage of 2.5 V is applied to the MOSFET Q
2
formed in area B, the gate insulating film
17
needs a thickness of about 6 nm. An oxynitride film is used as the gate insulating films
15
and
17
.
The semiconductor device of
FIG. 1
is formed by the processes shown in
FIGS. 2A
to
2
D. First, as shown in
FIG. 2A
, element isolating regions
12
are formed in a silicon substrate
11
. Then, impurities for controlling the threshold voltage of a MOSFET are introduced into the main surface of the silicon substrate
11
.
Thereafter, as shown in
FIG. 2B
, to become a gate insulating film
17
, oxynitride is deposited on the main surface of the silicon substrate
11
. The oxynitride film has a thickness of, for example, about 5 nm. Following that, a resist pattern
19
is formed as a mask on the oxynitride film
17
in area B by, for example, photoetching techniques.
Next, after the oxynitride film
17
on area A has been removed, another oxynitride layer is deposited as a gate insulating film
15
to a thickness of, for example, 4 nm. In this case, the oxynitride film
17
on area B is subjected to another oxidation, which forms a gate insulating film
17
of about 6 nm in thickness (see FIG.
2
C).
Thereafter, as shown in
FIG. 2D
, polysilicon
20
is deposited on the gate insulating films
15
and
17
to a thickness of, for example, about 200 nm. The polysilicon film is patterned by photoetching techniques, thereby forming gate electrodes
16
and
18
.
Then, impurity ions are implanted into the silicon substrate
11
. The resulting silicon substrate is then activated by rapid thermal annealing at about 1000° C., thereby forming a diffused layer to act as the source/drain regions
13
and
14
of each of the MOSFETs Q
1
and Q
2
. This completes a semiconductor device as shown in FIG.
1
.
In the semiconductor device formed as described above, use of an oxynitride film for the internal circuit MOSFET Q
1
using the gate insulating film as thin as about 4 nm prevents p-type impurities from diffusing from the gate electrode
16
into the silicon substrate
11
. In the manufacturing processes, however, the MOSFET Q
2
interfacing with an external device using the gate insulating film
17
as thick as about 6 nm has also a structure using an oxynitride film. In heat treatment at about 1000° C., the gate insulating film of about 6 nm in thickness does not necessarily need oxynitride from the viewpoint of the diffusion of p-type impurities from the gate electrode
18
into the silicon substrate
11
. Conversely, use of oxynitride causes the problem of decreasing the current driving capability of the MOSFET Q
2
due to the appearance of an interface level. Therefore, use of oxynitride is unfavorable from the standpoint of making the operation speed of the semiconductor device faster.
In the conventional semiconductor device and the method of manufacturing the semiconductor device, since an oxynitride film has been used as all the gate insulating films in an LSI requiring two or more types of power supply, this has caused the problems of decreasing the current driving capability and operation speed of the MOSFET.
BRIEF SUMMARY OF THE INVENTION
A first embodiment of the present invention is to provide a semiconductor device capable of not only minimizing a decrease in the current driving capability of a MOSFET but also making its operation speed faster in an LSI requiring two or more types of power supply.
A second embodiment of the present invention is to provide a method of manufacturing a semiconductor device capable of not only minimizing a decrease in the current driving capability of a MOSFET but also making its operation speed faster in an LSI requiring two or more types of power supply.
The first object of the invention is accomplished by providing a semiconductor device comprising: a first circuit which is integrated in a semiconductor chip and operates on a first voltage and which includes a transistor whose gate insulating film is made of SiO
2
; and a second circuit which is integrated in the semiconductor chip and operates

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

MOSFET gate insulating films with oxynitride and oxide does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with MOSFET gate insulating films with oxynitride and oxide, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and MOSFET gate insulating films with oxynitride and oxide will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2597002

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.