Specialized metallurgical processes – compositions for use therei – Processes – Producing or treating free metal
Reexamination Certificate
1998-08-17
2001-02-20
Andrews, Melvyn (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Processes
Producing or treating free metal
C075S512000
Reexamination Certificate
active
06190435
ABSTRACT:
TECHNICAL FIELD
The present invention relates to a method and apparatus for vacuum decarburization refining a molten steel and, more particularly, to a method and apparatus, for refining a molten steel, that can inhibit the deposition of a splash onto the inner wall of a vacuum tank and an oxygen lance and at the same time can prevent oxidation loss of metal in the molten steel.
BACKGROUND ART
Conventional methods for additional decarburization refining of a molten steel which has been once subjected to decarburization refining in an electric furnace or a converter to provide a molten steel having a carbon concentration of not more than 0.01% by weight include: (1) a VOD (vacuum oxygen decarburization) method, typified by the one disclosed in Japanese Unexamined Patent Publication (Kokai) No. 57-43924, wherein an oxygen gas is blown onto the surface of a molten steel in a ladle while holding the molten steel surface in vacuo; and (2) a straight barrel type snorkel method wherein an oxygen gas is blown onto the surface of a molten steel within a snorkel submerged in molten steel to carry out vacuum refining.
In the method (1), VOD, a satisfactory space cannot be ensured above the molten steel surface. This causes a splash of molten steel, scattered during oxygen blowing decarburization refining, to be deposited onto a top-blown lance and a cover of a vacuum vessel, adversely affecting the operation.
The method (2), straight barrel type snorkel method, unlike the method (1), has no significant limitation on equipment, and an example of this method is disclosed in Japanese Unexamined Patent Publication (Kokai) No. 61-37912. The method disclosed in this publication is shown in FIG.
35
. Specifically, in this method for vacuum refining of molten steel, a molten steel
71
contained in a ladle
70
is sucked through a snorkel
72
into a vacuum tank
73
. An inert gas is blown into the molten steel within the snorkel
72
through under the plane of projection of the snorkel
72
within the ladle
70
, and, at the same time, an oxidizing gas is blown through a top lance
74
onto the surface of the molten steel within the vacuum tank
73
. In this case, the inner diameter of the snorkel
72
is determined so that the ratio of the inner diameter (D
1
) of the snorkel
72
to the inner diameter (D
0
) of the ladle
70
, that is, D
1
/D
0
, is 0.4 to 0.8. In addition, the depth of blowing of the inert gas is determined so that the ratio of the depth (H
1
) of blowing of the inert gas as measured from the surface of the molten steel to the depth (H
0
) of the molten steel within the ladle
70
, that is, H
1
/H
0
, is 0.5 to 1.0. The above method for vacuum refining of molten steel aims to efficiently carry out decarburization without the deposition of the metal, slag and the like within the tank.
Japanese Unexamined Patent Publication (Kokai) No. 2-133510 proposes a vacuum treatment apparatus comprising: a ladle for placing therein a molten metal; a vacuum tank having a snorkel, submerged in the molten metal, provided at the lower end of the vacuum tank; an evacuation pipe connected to a vacuum source for evacuating the interior of the vacuum tank; and a shield disposed in the interior of the vacuum tank, wherein the shield is kept at a height of 2 to 5 m above the molten steel surface within the snorkel.
The method proposed in Japanese Unexamined Patent Publication (Kokai) No. 61-37912, however, had the following problems (i) to (iv).
(i) Conditions for decarburization refining, such as the flow rate of the oxygen gas blown onto the molten steel, the flow rate of the argon gas for agitation, and the degree of vacuum within the vacuum tank
73
, are not properly specified. This causes excessive fluctuation of the molten steel surface and splashing, leading to operation troubles attributable to deposition of the metal.
(ii) In the oxygen blowing decarburization refining of chromium-containing molten steel, such as stainless steel, the chromium component contained in the molten steel is oxidized with the blown oxygen. A part of the chromium oxide produced by the oxidation is reduced with carbon contained in the molten steel in the course of descending through the molten steel. Most part of the chromium oxide, however, undergoes the convection due to the inert gas blown from below the molten steel and floats, without being reduced, on the surface of the molten steel between the snorkel and the inner wall of the ladle to form slag
75
which is then discharged from the molten steel, increasing the loss of the chromium component.
(iii) The presence of the slag
75
containing chromium oxide causes the surface of the molten steel present between the snorkel
72
and the inner wall of the ladle to come into contact with air and to be cooled. This increases the viscosity of the molten steel surface. In addition, the slag
75
, the metal or the like is deposited around the above inner wall of the ladle, making it difficult to conduct sampling of the molten steel in the course of and at the end of the refining, or making it difficult to move the snorkel
72
from the position of the ladle
70
at the end of the refining, which is an obstacle to refining.
(iv) The oxygen efficiency in the decarburization, defined as the ratio of the amount of the oxygen gas contributed to the decarburization of the molten steel to the total amount of the oxygen gas blown onto the molten steel, is influenced by refining conditions, such as the degree of vacuum in the vacuum tank
73
, the state of agitation of the molten steel, and the flow rate of the oxygen gas blown. These refining conditions are not proper, making it difficult to maintain the oxygen efficiency in decarburization at a high level.
The method described in Japanese Unexamined Patent Publication (Kokai) No. 2-133510, wherein a shield is provided within a vacuum tank (a snorkel) to prevent splash of the molten steel created by oxygen blowing, thereby preventing deposition and accumulation of a metal caused by solidification of the splash deposited onto an oxygen lance, a vacuum tank, an evacuation pipe, had the following problems.
(i) When an exhaust gas is passes between shields within the vacuum tank, the molten steel splash in the exhaust gas or dust produced by solidification of the splash is deposited and accumulated onto the shields, increasing the flow resistance of the exhaust gas, which in turn increases the pressure loss within the vacuum tank.
(ii) Since the spacing, between the shields, serving as a passage for the exhaust gas becomes narrow, a high-power evacuation apparatus is necessary to provide a high degree of vacuum.
(iii) When a metal or the like scattered by splashing or spitting is once deposited and accumulated onto the passage for the exhaust gas between the shields, removal of the deposited and accumulated metal cannot be achieved without difficulty due to the complicated structure and requires a lot of time and labor.
In the method disclosed in Japanese Unexamined Patent Publication (Kokai) No. 61-37912, when the oxygen blowing refining is carried out at a high speed in order to increase the productivity of vacuum refining, the splashing is remarkably increased, posing the following problems which will be described with reference to FIG.
35
.
(i) Although the creation of the splash of the molten steel
71
per se can be inhibited, dust is still contained in the exhaust gas. Therefore, the dust is gradually deposited within the evacuation duct
76
particularly around its duct inlet section to form a deposit
77
, clogging the passage or increasing the air-flow resistance, which lowers the attainable level of the degree of vacuum within the vacuum tank
73
.
(ii) Dust is introduced into a gas cooler
78
and damages the gas cooler. This results in suspension of equipment and increased maintenance cost. Further, a dust deposit is formed within the gas cooler
78
, which causes a markedly lowered cooling efficiency.
(iii) Once a dust deposit
77
is formed within an evacuation duct
76
, the dust is strongly united and must b
Hayakawa Ryuzou
Ishimatsu Hiroyuki
Kaneyasu Takayuki
Katahira Keiichi
Kato Katsuhiko
Andrews Melvyn
Kenyon & Kenyon
Nippon Steel Corporation
LandOfFree
Method of vacuum decarburization/refining of molten steel does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of vacuum decarburization/refining of molten steel, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of vacuum decarburization/refining of molten steel will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2611701