ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method of patterning a transparent electrode of Indium Tin Oxide (ITO) and, more particularly, to a method of crystallizing the transparent electrode of ITO.
2. Description of the Related Art
A transparent conductive layer of Indium Tin Oxide (ITO) is practically applied to the fabrication of a contact of contact panel, an electrode of liquid crystal display (LCD), a thermal reflective coating, a gas-sensing sensor, a static electricity-resistance coating, and an abrasion-resistance coating of glass. The ITO layer may be formed by a chemical film-forming method, such as spray, chemical evaporation, or dipping. Alternatively, the ITO layer may be formed by a physical film-forming method, such as vacuum evaporation or sputtering. Generally, sputtering can form an ITO layer of a low resistance and a uniform thickness on a substrate. However, when the ITO layer is then patterned by conventional photolithography and etching with oxalic acid, the patterned ITO layer cannot fit in with the requirements for product properties.
FIG. 1
is a flow chart of a conventional method of patterning an ITO layer. First, at step
10
of sputtering, an amorphous ITO layer is deposited on a substrate. Then, conventional photolithography, which comprises a step
12
of photoresist coating, a step
14
of soft baking, a step
16
of exposure, a step
18
of developing, a step
20
of hard baking, a step
22
of etching by oxalic acid, and a step
22
of photoresist stripping, is carried out on the amorphous ITO layer. The step
14
of soft baking drives out the solvents existing in the photoresist. The step
16
of exposure makes the photoresist absorb appropriate energy so as to proceed with photochemical transformation. The step
18
of developing forms the potential pattern that is transferred to the photoresist. The step
20
of hard baking is used to further reduce the solvent remaining in the photoresist and fix the profile of the patterned photoresist. The step
22
of etching by oxalic acid removes the amorphous ITO layer not covered by the patterned photoresist, thus forming the pattern of the amorphous ITO layer. Finally, at step
26
, annealing is performed in an oven to turn the amorphous ITO layer into a crystallized ITO layer. Thus the ITO layer can achieve the expected resistance and transparency.
However, at the step
10
of sputtering with H
2
O, when the amorphous ITO layer is continuously deposited to reach a thickness of more than 800 Å, the process temperature is lower than the process temperature in the subsequent step
20
of hard baking. Thus, the higher temperature in the step
20
of hard baking causes a microcrystalline phenomenon on the surface of the amorphous ITO layer. Also, when the process temperature is improperly controlled in sputtering or photolithography, the microcrystalline phenomenon can be formed. Since oxalic acid is not the excellent etchant for etching crystallized materials, the step
22
of etching cannot completely remove the crystalline area of the ITO layer and this decreases the accuracy of patterning the ITO layer.
In addition, in the series of steps
12
~
24
,exposured photoresist and developer solution are easily remained on the substrate, thus effecting the properties of the subsequent etching or deposition. Also, the complicated steps
12
~
26
have high production costs and may cause the substrate to be bended, damaged or contaminated if man-made carelessness and improper process control occur.
Thus, a method of patterning an ITO layer solving the aforementioned problems is called for (desired).
SUMMARY OF THE INVENTION
The present invention provides a method of patterning an ITO layer to pattern and crystallize the amorphous ITO layer at the same time so as to simplify the procedure.
The method of patterning an indium tin oxide (ITO) layer is performed on a glass substrate. First, using sputtering, an amorphous ITO layer is deposited on the glass substrate. Then, using excimer laser annealing (ELA), the amorphous ITO layer within a predetermined pattern is turned into a crystalline ITO layer. Finally, using an etch solution, the amorphous ITO layer outside the predetermine pattern is removed.
Accordingly, it is a principle object of the invention to provide excimer laser annealing for replacing the conventional photolithography process.
It is another object of the invention to use excimer laser annealing to pattern and crystallize the amorphous ITO layer at the same time.
Yet another object of the invention is to simply the method of patterning the ITO layer.
It is a further object of the invention to accurately pattern the ITO layer.
REFERENCES:
patent: 5574293 (1996-11-01), Arai et al.
patent: 5766989 (1998-06-01), Maegawa et al.
patent: 5827773 (1998-10-01), Voutsas
patent: 5938839 (1999-08-01), Zhang
patent: 6071796 (2000-06-01), Voutsas
patent: 6169013 (2001-01-01), Voutsas
patent: 6184068 (2001-02-01), Ohtani et al.
patent: 6225197 (2001-05-01), Maekawa
patent: 6297086 (2001-10-01), Hegde et al.
patent: 6329229 (2001-12-01), Yamazaki et al.
Hsieh In-Cha
Peng Chih-Yu
Darby & Darby
Hannstar Display Corp.
Le Thao P.
Nelms David
LandOfFree
Method of patterning an ITO layer does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of patterning an ITO layer, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of patterning an ITO layer will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2831381