Semiconductor device manufacturing: process – Making field effect device having pair of active regions... – On insulating substrate or layer
Reexamination Certificate
1998-02-02
2003-07-22
Wilczewski, Mary (Department: 2822)
Semiconductor device manufacturing: process
Making field effect device having pair of active regions...
On insulating substrate or layer
C438S486000, C438S487000
Reexamination Certificate
active
06596572
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a semiconductor formed of a polycrystal silicon thin film, which is formed by crystallizing an amorphous silicon thin film on an insulator, and a thin-film transistor using that semiconductor.
2. Description of the Related Art
In recent years, a technique has been popularly researched where an amorphous silicon thin film is formed on an insulator such as a quartz substrate, allowed to grow into a solid-phase crystal (SPC) through a heating treatment or an annealing process due to the irradiation of a laser beam or an intense light to form a polycrystal silicon thin film.
A conventional general technique for obtaining a polycrystal silicon thin-film by allowing an amorphous silicon thin film to grow in a solid phase will be described below.
First, an amorphous silicon thin film having a thickness of 500 to 5000 Å is formed on a quartz substrate.
Thereafter, the amorphous silicon thin film thus formed is heated to 400 to 1100° C. and subjected to an annealing process to make the amorphous silicon thin film grow into crystal. In this situation, a heater, infrared rays or the like is used as heating means.
The annealing process may be conducted by the irradiation of a laser beam or an intense light other than heating.
In the above-mentioned manner, a polycrystal silicon thin film is obtained.
The polycrystal silicon thin film thus obtained is used as an active silicon layer of the thin-film transistor (TFT), to thereby provide a thin-film transistor. As a result, a liquid-crystal display unit, image sensor or the like which is high in operation speed and in image quality is obtained using the above thin film transistor.
Up to now, the polycrystal silicon thin film obtained by annealing the amorphous silicon thin film has difficulty in lowering a defect density in crystal.
The thin-film transistor using the polycrystal silicon thin film thus formed as the active silicon film is hindered from realizing an improvement in various characteristics of the thin-film transistor, for example, the lowering of a threshold voltage (V
th
), an increase in mobility, a decrease in a leak current (I
off
), etc., because the defect density in the active silicon layer is high.
SUMMARY OF THE INVENTION
The present invention has been made in view of the above circumstances, and therefore an object of this invention is to make a polycrystal silicon thin film obtained by annealing an amorphous silicon thin film low in defect density and high in quality.
Another object of the invention is to provide a thin-film transistor using a polycrystal silicon thin film obtained through an annealing process with a lowered threshold voltage (V
th
) and leak current (I
off
) and an increased mobility.
In order to solve the above-mentioned problem, according to one aspect of the present invention, there is provided a method of manufacturing a semiconductor characterized in that, in polycrystallizing an amorphous silicon thin film formed on a substrate through an annealing process, said amorphous silicon thin film has a plane area of 1000 &mgr;m
2
or less.
In the above-mentioned method, the amorphous silicon thin film is preferably 1000 Å or more, more preferably 2000 Å to 10000 Å in thickness.
Also, according to another aspect of the present invention, there is provided a thin-film transistor having an active silicon film which is formed of a plurality of island-like regions arranged in parallel to each other, each of said island-like regions being formed of a polycrystal silicon thin film having a plane area of 1000 &mgr;m
2
or less.
In the thin-film transistor thus constituted, the island-like regions are formed of a polycrystal silicon thin film which is preferably 1000 Å or more, more preferably 2000 Å to 10000 Å in thickness.
Also, according to another aspect of the present invention, there is provided a method of manufacturing a thin-film transistor comprising the steps of: forming an amorphous silicon thin film on a substrate; processing said amorphous silicon thin film into a plurality of island-like regions having a plane area of 1000 &mgr;m
2
or less; polycrystallizing an amorphous silicon thin film that forms said island-like regions through an annealing process; and forming a thin-film transistor having at least one of said plurality of island-like regions as an active silicon layer.
In the above-mentioned method, the amorphous silicon thin film is preferably 1000 Å or more, more preferably 2000 Å to 10000 Å in thickness.
The present applicant has found that after the amorphous silicon thin film has been formed as island-like regions each has a plane area (an area viewed from an upper surface of the substrate) of 1000 &mgr;m
2
or less, it is subjected to an annealing process by heating or the irradiation of a laser light beam or an intense light to form a polycrystal silicon thin film with the result that a polycrystal silicon thin film which is low in defect density and high in quality is obtained.
FIG. 1
is a graph showing a relationship between a threshold voltage (V
th
) and an area of the island-like regions of the polycrystal silicon thin-film transistor, in which each of the island-like regions is 1250 Å in thickness.
As shown in
FIG. 1
, it has been found that as the area of the island-like regions is small, the threshold voltage approaches 0 (zero) more in both of a p-channel and an n-channel so that the defect density is lowered.
In
FIG. 1
, there has been found that an extremely excellent crystalline property is obtained when the plane area of each of the island-like regions is 1000 &mgr;m
2
or less.
Also, when the plane area of each of the island-like regions is 1000 &mgr;m
2
or less, the island-like regions may be of a square, a rectangle or other shapes.
Further, when the island-like regions are 1 &mgr;m
2
or more in plane area, the semiconductor is satisfactorily available as a device, and also it can be readily manufactured by a usual technique.
On the other hand, in the case where the polycrystal silicon thin film is provided as the active silicon layer of the thin-film transistor, because an area of the island-like regions is limited in size, the thin-film transistor using that polycrystal thin film is also limited in size, which causes a limit to the performance of the thin-film transistor.
Under the above circumstances, the applicant has found that a plurality of each of the island-like regions, a plane area of which is 1000 &mgr;m
2
or less is arranged in parallel to each other as active silicon layers that constitute the source region, the drain region and the channel formation region of a thin-film transistor so as to increase a substantial channel width, thereby being capable of obtaining a polycrystal thin-film transistor which allows a sufficient amount of current to flow therein, which has the channel formation region low in defect density, and which is high in performance.
FIG. 3
shows an example of a plane shape of a thin-film transistor using a plurality of island-like regions as an active silicon layer.
In
FIG. 3
, a plurality of island-like regions
301
are arranged in parallel to each other to form an active silicon layer
305
of a thin-film transistor. On the island-like regions
301
are disposed a gate electrode
302
, a source electrode
303
and a drain electrode
304
to form one thin-film transistor. Appropriate intervals between the respective island regions is several to several tens &mgr;m. As the intervals are small, the plane area of the active silicon layer can be reduced more.
In the island-like region, as its plane area is reduced, the defect density is reduced more in a polycrystallized state, thereby being capable of reducing a leak current.
Also, the applicant has found that the amorphous silicon thin film is set to preferably 1000 Å or more, more preferably 2000 Å to 10000 Å in thickness, thereby lowering the defect density of the polycrystal silicon thin film obtained by
Arai Michio
Kobori Isamu
Fish & Richardson P.C.
Semiconductor Energy Laboratory Co. Ltd
Wilczewski Mary
LandOfFree
Method of fabricating a thin-film transistor having a... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of fabricating a thin-film transistor having a..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of fabricating a thin-film transistor having a... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3029397