Method for increasing filler retention of cellulosic fiber...

Paper making and fiber liberation – Processes and products – Plural fiber containing

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C162S164100, C162S164300, C162S164600, C162S175000, C162S182000

Reexamination Certificate

active

06824649

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to a method for increasing filler retention of cellulosic fiber sheets and, more particularly, to a method for increasing filler retention for cellulosic fiber sheets by incorporating cellulosic fibers having increased anionic sites into the sheet.
BACKGROUND OF THE INVENTION
Fillers are often incorporated into cellulosic fiber sheets to provide paper products having enhanced printability and improved optical properties. However, the improvement provided by filler is limited by the amount of filler that can be retained by the fiber sheet. Accordingly, there exist a need for methods for increasing fiber capacity for filler and for increasing the filler retention of fiber sheets. The present invention seeks to fulfill these needs and provides further related advantages.
SUMMARY OF THE INVENTION
In one aspect, the present invention provides a method for increasing filler retention of cellulosic fiber sheets. In the method, cellulosic fibers with increased anionic sites are treated with either positively charged and/or amphoteric filler particles or a cationic retention aid and negatively charged and/or amphoteric filler particles to provide sheets having increased filler retention.
In another aspect of the invention, cellulosic fiber sheets with retained filler particles are provided. In one embodiment, fiber sheets with retained positively charged and/or amphoteric filler particles are provided and, in another embodiment, the fiber sheets with retained negatively charged and/or amphoteric filler particles are provided.
In a further aspect, a method for increasing drainage from a papermaking furnish is provided. In the method, cellulosic fibers having increased anionic sites are incorporated into the furnish.


REFERENCES:
patent: 4610801 (1986-09-01), Matthews et al.
patent: 5147507 (1992-09-01), Gill
patent: 5201998 (1993-04-01), Töpfl et al.
patent: 5244542 (1993-09-01), Bown et al.
patent: 5514249 (1996-05-01), Cauley et al.
patent: 5522967 (1996-06-01), Shet
patent: 5543014 (1996-08-01), Rushmere et al.
patent: 5611890 (1997-03-01), Vinson et al.
patent: 5667637 (1997-09-01), Jewell et al.
patent: 5755828 (1998-05-01), Westland
patent: 5755930 (1998-05-01), Satterfield
patent: 5827398 (1998-10-01), Depasquale et al.
patent: 5935383 (1999-08-01), Sun et al.
patent: 5958180 (1999-09-01), Hubbe et al.
patent: 0 373 306 (1990-06-01), None
patent: 0 499 448 (1992-08-01), None
patent: WO 93/01353 (1993-01-01), None
patent: WO 95/07303 (1995-03-01), None
patent: WO 98/24974 (1998-05-01), None
Andersson, R., et al., Note: “An N.M.R. Study of the Products of Oxidation of Cellulose and (1→4)-&bgr;-D-xylan with Sodium Nitrite in Orthophosphoric Acid,”Carbohydrate Research, 206:340-346, 1990.
Datye, K.V., et al., “Studies in the Reaction of Formaldehyde with Unmodified, Modified, and Dyed Celluloses Part III: The Reaction of Formaldehyde with Oxycelluloses,”Textile Research Journal, Jul. 1963, pp. 500-510.
“Forming Handsheets for Physical Tests of Pulp,” TAPPI Test T205 os-71.
Fukatsu, K., “Dyeing and Mechanical Properties of Cotton Modified for Cationic Dyes with Hydrophobic and Acidic Groups,”Textile Research Journal, Mar. 1992, pp. 135-139.
Heinze, T.J., et al., Eds., Cellulose Derivatives—Modification, Characterization, and Nanostructures, Besemer, A.C., et al., Chapter 5, “Methods for the Selective Oxidation of Cellulose: Preparation of 2,3-Dicarboxycellulose and 6-Carboxycellulose,”Journal of the American Chemical Society, 212th National Meeting of the American Chemical Society, Aug. 25-29, 1996, pp. 73-82.
Isogai, A., et al., “Preparation of Polyuronic Acid From Cellulose by TEMPO-Mediated Oxidation,”Cellulose, 5:153-164, 1998.
Luner, P., et al., “The Effect of Chemical Modification on The Mechanical Properties of Paper II. Wet Strength of Oxidized Springwood and Summerwood Southern Pine Kraft Fibers,”TAPPI, 50(3):117-120, Mar. 1967.
Luner, P., et al., “The Effect of Chemical Modification on The Mechanical Properties of Paper 3. Dry Strength of Oxidized Springwood and Summerwood Southern Pine Kraft Fibers,”TAPPI, 50(5):227-230, May 1967.
Shenai, V.A., et al., “Hypochlorite Oxidation of Cellulose in the Presence of Cobalt Sulphide,”Textile Dyer&Printer 20:17—22, May 20, 1987.
Shet, R.T., et al., “Crease-Recovery and Tensile-Strength Properties of Unmodified and Modified Cotton Cellulose Treated with Crosslinking Agents,”Textile Research Journal, Nov. 1981, pp. 740—744.
Young, R.A., “Bonding of Oxidized Cellulose Fibers and Interaction with Wet Strength Agents,”Wood and Fiber, 10(2):112—119, Summer 1978.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method for increasing filler retention of cellulosic fiber... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for increasing filler retention of cellulosic fiber..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for increasing filler retention of cellulosic fiber... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3299178

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.