Semiconductor device manufacturing: process – Coating with electrically or thermally conductive material – To form ohmic contact to semiconductive material
Reexamination Certificate
2001-06-15
2003-02-18
Lee, Eddie (Department: 2815)
Semiconductor device manufacturing: process
Coating with electrically or thermally conductive material
To form ohmic contact to semiconductive material
C438S628000, C438S644000, C438S654000, C438S687000, C438S692000, C438S759000
Reexamination Certificate
active
06521523
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to the fabrication of semiconductor structures, and more particularly, to a method for forming selective protection layers over copper interconnects in the manufacture of integrated circuits.
2. Description of the Related Arts
As integrated circuit feature sizes continue to decrease, it has become advantageous to construct metal connections out of copper instead of aluminum. Copper has a lower resistivity than aluminum, and therefore can form higher speed connections for a given line width.
Copper has disadvantages when compared to aluminum that must be overcome. For example, copper is much more susceptible to oxidation during processing. Copper also tends to diffuse into adjacent materials, including dielectrics. To use copper for interconnections, therefore, it is necessary to encapsulate the copper in barrier materials.
Where a low resistive interface between a copper interconnect and an underlying metal conductor must be completed, it is common in the art to deposit a barrier of a metal material, such as titanium, tungsten, tantalum, or tantalum nitride before the copper layer is deposited.
After the copper layer is deposited, another barrier layer, typically called a sealing layer is deposited overlying the copper. Typically in the art, this sealing layer (also called a cap layer, or an encapsulation layer) is composed of silicon nitride, though other materials are used.
Referring to
FIG. 1
, a cross-section of a prior art damascene wiring is shown. A dielectric layer
102
and a substrate
100
are depicted. The substrate
100
encompasses all underlying layers, devices, junctions, and other features that have been formed prior to the deposition of dielectric layer
102
.
Interconnection trenches are formed in the dielectric layer
102
, and a barrier layer
104
is deposited overlying the dielectric layer
102
and in the trenches. The purpose of the barrier layer
104
is to prevent diffusion of the subsequently deposited copper. A copper layer
106
has been deposited overlying the dielectric layer
102
and filling the trenches. The excess copper layer
106
and the excess barrier layer
104
are then typically polished down to the dielectric layer
102
by a chemical mechanical polishing (CMP) process.
Following the definition of the copper interconnects
106
by the CMP, a sealing layer
108
is deposited. This sealing layer
108
serves as a barrier to diffusion of the copper layer
106
into any overlying layers. In addition, by encapsulating the copper completely in the barrier layer
104
and the sealing layer
108
, oxidation during subsequent processes is eliminated.
The sealing layer
108
is typically silicon nitride. Due to the need for low temperature processing after the copper is deposited, the silicon nitride layer
108
cannot be deposited at temperatures in excess of 450° C. Accordingly, silicon-nitride deposition is typically performed using plasma enhanced chemical vapor deposition (PECVD) where temperatures generally range from 200° C. to 425° C. PECVD silicon-nitride has been used in other applications in semiconductor devices. However, in using a silicon nitride cap for copper interconnects, conventional PECVD silicon nitride creates reliability problems. In particular, silicon nitride films deposited using conventional PECVD processes have poor adhesion to copper surfaces. As an example, some nitride films can be peeled from the copper surfaces simply by scratching the film or by removing the film using an adhesive tape. These results are indicative of how the silicon nitride film might adhere to the copper in an actual fabrication process. After being deposited onto the copper surface, additional insulating layers will be deposited over the silicon nitride film. However, subsequent deposition of insulating layers onto the nitride film will produce stresses which can cause the silicon nitride layer to peel from the copper surface. Despite that other layers have been deposited onto the semiconductor device, the peeling of the silicon nitride film creates a path for copper to diffuse outward and for moisture or other contaminates to diffuse inward.
Several prior art approaches deal with copper sealing methods. U.S. Pat. No. 5,403,779 to Joshi et al teaches a process to form damascene metal lines and vias. After copper deposition, tungsten is deposited by CVD. A CMP step is performed to planarize the structures. U.S. Pat. No. 5,447,887 to Filipiak et al discloses a process to form copper interconnects where a copper silicide layer is formed overlying the copper traces. A silicon nitride layer is deposited overlying the copper silicide to complete the encapsulation layer. U.S. Pat. No. 5,814,557 to Venkatraman et al discloses a process to form a copper-containing aluminum film overlying an aluminum conductor. An annealing operation is performed to diffuse the copper into the aluminum conductor.
SUMMARY OF THE INVENTION
An object of the invention is to provide a process for implementing copper damascene wiring within an integrated circuit.
A further object of the invention is to provide a method of fabricating copper interconnects with selective protection layers that are selectively formed only overlying the copper interconnects.
A still further object of the invention is to provide a method of fabricating copper interconnects with selective sealing layers that effectively prevent copper oxidation and diffusion.
A yet further object of the invention is to provide a method of fabricating copper interconnects with selective adhesion layers that increase the adhesion between the nitride and copper.
The above and other objects are achieved by polishing the excess copper layer with a slurry comprising an aluminum organic substance. The aluminum organic substance reacts with copper via annealing to selectively form aluminum-copper alloys on the copper interconnects. The aluminum-copper alloys are then oxidized to form aluminum oxide protection layers capping the copper interconnects. The aluminum oxide protection layers can function as a conventional sealing layer to prevent copper diffusion and oxidation, or they can function as an adhesion layer to improve the adhesion between the copper interconnects and a later sealing layer.
According to one aspect of this invention, there is provided a method for making copper interconnects in the fabrication of a semiconductor device comprising the steps of providing a semiconductor substrate; forming a dielectric layer overlying the substrate, the dielectric layer having interconnect trenches formed therein; depositing a copper layer overlying the dielectric layer and filling the interconnect trenches; chemical-mechanical polishing the copper layer to the top surface of the dielectric layer and thereby defining copper interconnects, said polishing leaving an aluminum organic substance on said copper interconnects which can react with copper via annealing to form an aluminum-copper alloy; annealing the substrate to form aluminum-copper alloys overlying said copper interconnects; and oxidizing the aluminum-copper alloys to form aluminum oxide protection layers capping said copper interconnects.
According to another aspect of this invention, there is provided a method for making copper interconnects in the fabrication of a semiconductor device comprising the steps of providing a semiconductor substrate; forming a dielectric layer overlying the substrate, the dielectric layer having interconnect trenches formed therein; depositing a copper layer overlying the dielectric layer and filling the interconnect trenches; first chemical-mechanical polishing the copper layer with a first slurry to remove most of the copper layer overlying the dielectric layer; second chemical-mechanical polishing the copper layer with a second slurry to the top surface of the dielectric layer and thereby defining copper interconnects, said second slurry comprising an aluminum organic substance which can react with copper via annealing to form an aluminum-cop
Hsue Chen-Chiu
Lee Shyh-Dar
Lee Eddie
Richards N. Drew
Silicon Integrated Systems Corp.
LandOfFree
Method for forming selective protection layers on copper... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for forming selective protection layers on copper..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for forming selective protection layers on copper... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3148808