Method for forming multi-layer metal line of semiconductor...

Semiconductor device manufacturing: process – Coating with electrically or thermally conductive material – To form ohmic contact to semiconductive material

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C438S622000

Reexamination Certificate

active

06777326

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method for forming a multi-layer metal line of a semiconductor device, and in particular to an improved method for forming a multi-layer metal line of a semiconductor device wherein an insulating film having a low dielectric constant is used in a formation process of an interlayer insulating film of the multi-layer metal line to improve characteristics and reliability of the device.
2. Description of the Background Art
In general, a line of a semiconductor device for electrically connecting devices or device to an external circuit is formed by filling a contact hole and a via hole for interconnection with a line material to form a line layer, and performing subsequent processes. In particular, a metal line is used in a region where a low resistance is required.
The metal line is formed by filling the contact hole and the via hole with the line material, such as an aluminum alloy containing aluminum and a small amount of silicon and/or copper which has a low resistance and excellent processing characteristics according to sputtering of physical vapor deposition (PVD).
Due to a high integration tendency of the semiconductor device, in a process formation of a metal line, a low-K material layer having a low dielectric constant is formed as an interlayer insulating material to reduce resistance capacitance delay by spin coating, and a via hole for connecting an upper line to a lower line is formed, and filled the via hole to form a tungsten contact plug.
Here, since the insulating film is non-uniformly coated on the metal line by the spin-coating process, the thickness of the insulating film depends on a width and density of the metal line therebelow.
An inter-capacitance value between the upper metal line and the lower metal line varies due to non-uniform thickness according to the width and density of the metal line, which deteriorates characteristics of the device.
Moreover, bowing phenomenon occurs during a dry etching process of the via hole, which complicates etching conditions, and the bowing on the sidewalls of the via hole makes deposition of an adhesive film and a diffusion barrier film difficult, which complicates a subsequent process, namely a formation process of a tungsten contact plug.
Furthermore, the end of the metal line is shorted and rounded due to a proximate effect during the patterning process of the metal line, which reduces process margin in a via contact etching process. As a result, the characteristics of the device are deteriorated.
FIGS. 1
a
to
1
e
are cross-sectional views illustrating a conventional method for forming a multi-layer metal line of a semiconductor device.
Referring to
FIG. 1
a
, a lower metal line
13
is formed on a semiconductor substrate
11
. Here, the lower metal line
13
is composed of an aluminum alloy, and has Ti or Ti/TiN stacked layer at the upper and lower portions of the lower metal line
13
.
Reference numeral
100
denotes a region where the area of the lower metal line varies, and reference numeral
200
denotes a region where the density of the lower metal line varies. That is, a metal line having a large area is formed at the left side of region
100
, and a metal line having a small area is formed at the right side thereof. A density of the metal line at the left side of the region
200
is relatively higher than that of the right side thereof.
Thereafter, an insulating film
15
having a low dielectric constant is formed on the entire surface. Here, the insulating film
15
is formed according to spin coating using a material having a dielectric constant of about 3.
Although the insulating film
15
has an excellent filling property between metals, namely high step coverage, it is not uniformly coated on the metal line due to its adhesiveness, but unevenly coated on the metal line depending on a width and density of the metal line.
In general, the insulating film
15
is coated thicker on the metal line having the larger area than on the metal line having the smaller area, and in the region having high metal line density than the region having low metal line density.
Thereafter, an oxide film
17
is deposited on the insulating film
15
according to plasma enhanced chemical vapor deposition (PECVD).
Here, the oxide film
17
is formed using a material having a dielectric constant of about 4 at a thickness ranging from 5000 to 12000 Å.
A chemical mechanical polishing (CMP) is performed on the oxide film
17
to form an interlayer insulating film having a stacked structure of the insulating film
15
and the oxide film
17
.
As shown in
FIG. 1
b
, a photosensitive film pattern
19
is formed on the interlayer insulating films
15
and
17
.
Here, the photosensitive film pattern
19
is formed according to exposure and development processes using a via contact mask (not shown).
As illustrated in
FIG. 1
c
, a via contact hole
21
exposing the lower metal line
13
is formed by etching the interlayer insulating films
17
and
15
using the photosensitive film pattern
19
as a mask.
Since an etch selectivity ratio of the insulating film
15
is at least 1.5 times higher than the etch selectivity ratio of the oxide film
17
, the insulating film
15
which is thicker is laterally etched.
The residual photosensitive film pattern
19
is removed after the etching process, and a Ti/TiN film
23
which is an adhesive layer/diffusion barrier film is formed on the entire surface of the resulting structure including the via contact hole
21
.
As depicted in
FIG. 1
d
, a tungsten layer
25
for contact plug is formed on the entire surface of the resulting structure according to the PECVD to contact the lower metal line
13
through the via contact hole
21
.
Here, bowing is generated in the laterally-etched portion of the insulating film
15
as shown in @.
As described above, in the conventional method for forming the multi-layer metal line of the semiconductor device a bowing phenomenon in the subsequent process because the insulating film having the high etch selectivity ratio is laterally etched during the via contact etching process, thereby deteriorating the property and reliability of the device.
SUMMARY OF THE INVENTION
Accordingly, it is an object of the present invention to provide a method for forming a multi-layer metal line of a semiconductor device which can easily form the sufficient multi-layer metal line for high integration of the semiconductor device by forming a presumed via contact plug without generating bowing.
In order to achieve the above-described object of the invention, there is provided a method for forming a multi-layer metal line of a semiconductor device, including the steps of: (a) forming a first insulating film having a low dielectric constant on a semiconductor substrate having a lower metal line thereon; (b) forming and planarizing a first oxide film on the first insulating film; (c) etching back the first oxide film and the first insulating film until a predetermined thickness of first insulating film remains on the lower metal line; (d) forming and planarizing a second insulating film having a low dielectric constant on the entire surface of the resulting structure; (e) forming a second oxide film on the second insulating film; (f) selectively etching the second oxide film and the first and the second insulating films to form a via contact hole exposing the lower metal line; (g) forming an adhesive film/diffusion harrier film on the entire surface of the resulting structure; and (i) forming a contact plug filling the via contact hole, and forming an upper metal line contacting the contact plug.
On the other hand, the principle of the present invention will now be explained.
An insulating film having a low dielectric constant is coated, an oxide film is deposited low thereon and then planarized according to CMP, an etch back process is performed thereon by using an etch speed difference, a thickness of the insulating film non-uniformly formed on the metal line according to a width a

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method for forming multi-layer metal line of semiconductor... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for forming multi-layer metal line of semiconductor..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for forming multi-layer metal line of semiconductor... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3287343