Semiconductor device manufacturing: process – Coating with electrically or thermally conductive material – To form ohmic contact to semiconductive material
Reexamination Certificate
1997-10-08
2001-11-13
Wilczewski, Mary (Department: 2822)
Semiconductor device manufacturing: process
Coating with electrically or thermally conductive material
To form ohmic contact to semiconductive material
C438S664000, C438S655000
Reexamination Certificate
active
06316357
ABSTRACT:
FIELD OF THE INVENTION
The present invention generally relates to a method for forming metal silicide on a silicon surface and more particularly, relates to a method for forming metal silicide on a silicon surface by first depositing a metal layer on top of a silicon surface and then irradiating the metal layer with laser energy for a sufficient length of time such that a layer of metal silicide is formed at the metal/silicon interface.
BACKGROUND OF THE INVENTION
In the fabrication of semiconductor devices, P
−
and N
−
type doped regions in single crystal and polycrystalline silicon are formed as active devices. The doped regions form the basic elements of a semiconductor device which must be connected in a specific configuration to form a desired circuit. The circuit must then be accessible to the outside world through conducting pads for testing with metal probes and for bonding into a packaged chip. While doped silicon and polysilicon conduct electricity, they are not useful in forming contacts or interconnects due to their prohibitively large resistance. As a result, at least one low-resistance contact material such as metal must be deposited and patterned to contact the different regions in a chip.
It is known that when contact is made between two dissimilar materials, a contact potential in the form of a barrier typically develops at an interface between the materials. Such a contact formed between a metal and a semiconductor can be categorized as an ohmic contact which ideally is transparent to current and thus allowing a linear current-voltage characteristic with negligible resistance in both directions across the contact. In order to make sub-micron contacts of sufficiently low resistance, surface dopant concentrations of greater than 10
20
cm
−3
are normally required for achieving a resistance that approaches an ideal ohmic contact so that current may pass with little resistance.
In modern semiconductor devices, specifically those fabricated by the ULSI or the sub-half-micron technology, the depth of the junctions formed in a silicon substrate is reduced when the total dimensions of the device are reduced. One potential problem encountered in reducing the depth of the junctions is the inevitable increase in the sheet and contact resistances of the junctions. A known method for reducing the sheet and contact resistances of junctions, specifically when used in conjunction with a polysilicon contact, is the use of metal silicides for reducing these resistances. Barrier metals are normally deposited on the silicides in order to protect the silicide films and the interfaces with silicon from diffusing species during subsequent processing steps.
Metal silicides can be used in such microelectronic applications by reacting refractory or near noble metals with silicon. Among the more popularly used metal silicides in microelectronics are titanium silicides (TiSi
2
), cobalt silicide (CoSi
2
), tungsten silicide (WiS
2
), platinum silicide (PtSi), molybdenum silicide (MoSi
2
), palladium silicide (PdSi) tantalum silicide (TaSi
2
), and chromium silicide (CrSi). When used in conjunction with a polysilicon layer, the silicide films deposited in parallel with the higher-resistivity junction reduces resistance in the transistor regions. The combined metal silicide/polysilicon metallurgy (sometimes called a polycide) presents a major benefit that it can withstand processing temperatures of higher than 550° C., for instance, a reflow temperature of 850° C. during a planarization process for PSG or BPSG. Such high processing temperatures normally cannot be tolerated by other contact materials. Among the different metal suicides, tungsten silicide, titanium silicide and cobalt silicide are the more commonly used materials based on their low resistivity and their stability in contacts with polysilicon gates and junctions.
Enlarged cross-sectional views of the formation of a metal silicide on a polysilicon gate by a conventional method is illustrated in FIGS.
1
A~
1
C. A conventional self-aligned silicidation process for a post-junction-formation silicide performed on a semiconductor device
10
is shown in FIG.
1
A. Onto a silicon substrate
12
, LOCOS insulators
14
and
16
, lightly doped drain regions
18
and
20
, a polysilicon gate
22
, and gate oxide
24
are first formed by conventional methods. Oxide sidewall spacers
26
,
28
for protecting the polysilicon gate
22
are then formed. An ion implantation process is used to form junctions
32
,
34
for the source/drain regions. The structure formed in
FIG. 1A
is representative of a typical self-aligned TiSi
2
process.
In the next step of the process wherein metal silicide layer is formed, various techniques such as sputtering, evaporation or chemical vapor deposition can be used to first deposit a metal layer
40
over the polysilicon gate
22
and the exposed single crystal silicon regions. In the present example of TiSi
2
, a titanium layer
40
is deposited and then annealed by a two-step furnace or rapid thermal annealing process. In the first step, the titanium film is annealed at a temperature of 650° C. in a nitrogen atmosphere such that titanium nitride is formed at the surface of the metal while titanium reacts with silicon and forms TiSi
2
in those regions where titanium contacts with silicon. At the annealing temperature of 650° C., a high resistivity TiSi
2
forms readily in the exposed silicon regions, while a negligible reaction between titanium and silicon occurs where the metal is in contact with silicon dioxide or silicon nitride insulators. The metal composition in contact with the insulators consists mainly of TiN and unreacted Ti which are then removed by a wet dipping process leaving the metal silicide layer intact. The process results in a self-alignment between the silicide and the exposed silicon regions and therefore, is called a salicide process indicating that silicides formed over polysilicon and single crystal silicon are self aligned to each other. A second annealing step for the TiSi
2
is necessary which is typically conducted at a temperature of 800° C. to further transform the silicide to a lower resistivity phase. The metal silicide region
42
over the polysilicon gate
22
, and the metal silicide regions
44
,
46
formed over the single crystal silicon regions
32
,
34
are shown in an enlarged, cross-sectional view in FIG.
1
C.
The conventional method for forming metal silicide layers over a polysilicon gate and single crystal silicon source/drain regions shown in FIGS.
1
A~
1
C presents several processing problems. The processing problems occurring in the self-aligned silicide formation process are the formation of a bridge between gate and the source/drain regions, the difficulty in forming silicide on thin layer of polysilicon and shallow diffusion regions, and the thermal stability of thin metal silicides formed. Of these problems, the bridging between a gate and source/drain regions is the most serious. For instance, in the formation of TiSi
2
, it is known that silicon is the predominant diffusion species that moves through a growing silicide phase to react with the metal. As a result, TiSi
2
formation is no longer confined to where Ti contacts Si. For instance, TiSi
2
may readily form along the sidewalls of the gate insulators resulting in a short between the gate and the source/drain regions. It has been observed that, under favorable conditions, silicon can diffuse a long distance and thus forming TiSi
2
on the sidewall spacers. The extent of the bridge formation is determined by the temperature and the duration of the sintering process occurring between metal and silicon. Since a high temperature of at least 600° C. is normally required to cause a reaction between Ti and Si for the sintering of TiSi
2
, an extensive diffusion of Si in Ti already occurs at such high temperature. Even though efforts have been made to reduce the bridging problem by utilizing a nitrogen atmosphere and by utilizing a rapid thermal process to reduce the heating ti
Lin Kang-Cheng
Wu Hong-Woei
Industrial Technology Research Institute
Tung & Associates
Wilczewski Mary
LandOfFree
Method for forming metal silicide by laser irradiation does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for forming metal silicide by laser irradiation, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for forming metal silicide by laser irradiation will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2589982