The present invention relates to a method for forming a Chemical Vapor Deposition (CVD) film and an apparatus for manufacturing a semiconductor device with formation of an interlevel insulator in the semiconductor device.
There are a variety of CVD systems for forming an insulating film, but a plasma CVD method and a thermal CVD method have been principally used in recent years. However, an insulating film formed by the plasma CVD method is not suitable for a highly dense and fine pattern such as a very large scale integrated circuit (VLSI), in particular a dynamic random access memory (DRAM), since such insulating film has poor step coverage and contains impurities such as carbon (C).
Accordingly, attention has focused on application of the thermal CVD method because of its superior step coverage, in particular the thermal CVD method which enables film formation at such a low temperature that no thermal influence is exerted upon other components in forming a VLSI such as a DRAM.
Conventional methods include (a) a method involving oxidizing SiH.sub.4 or oxidizing SiH.sub.4 after mixing PH.sub.3 and B.sub.2 H.sub.4 therewith, and (b) a method involving pyrolyzing or oxidizing alkoxysilane Si(OR).sub.4 or oxidizing Si(OR).sub.4 after mixing B(OR).sub.3 and PO(OR).sub.3 therewith. Both (a) and (b) are conventional thermal CVD methods for forming a SiO.sub.2 film or an insulating film with a SiO.sub.2 film as the base.
Interlevel insulators are formed between Al and a gate and between Al and Al.
(1) For an interlevel isolator between Al and Al, the following are the criteria:
(2) For an interlevel insulator between Al and a gate, the following are the criteria:
Accordingly, a conventional plasma CVD method or atmospheric pressure CVD method may be used for forming an interlevel insulator between Al and Al, a complicated process wherein three types of a CVD film I 35, CVD film II 36 and a CVD film III 37 are formed on interconnection metals 34 on a substrate 33, as shown in FIG. 8. Optionally, a glass film may be applied midway therebetween for flattening and etch-back as shown in FIG. 9.
The following methods have been proposed for forming an interlevel insulator between Al and a gate:
(1) Formation of an arsenic silicate glass film using SiH.sub.4 -A.sub.S H.sub.3 -O.sub.2.
(2) Formation of a boron silicate glass film using SiH.sub.4 -B.sub.2 H.sub.6 -PH.sub.3 -O.sub.2.
(3) Formation of a boron arsenic silicate glass film using TEOS-Tri Methyl Borate (TMB)-Tri Methyl Phosphate (TMOP)-O.sub.3.
(4) Formation of a boron arsenic silicate glass film using TEOS-TMB-TMOP-O.sub.2.
(5) Formation of a germanium silicate glass film using SiH.sub.4 -GeH.sub.4 -PH.sub.3 -O.sub.2.
However, since reflow of the interlevel insulator can be performed at a temperature of approximately 800.degree. C. to 900.degree. C. in (1) to (5), it is possible to lower the reflow temperature, which, however, is not sufficient. In particular, the reflow temperature is lowered in (2) to (4) by adding arsenic or boron, but the film quality becomes unstable with the increase of the concentration of arsenic or boron.
Furthermore, according to the method for forming a germanium silicate glass film using SiH.sub.4 -GeH.sub.4 -PH.sub.3 -O.sub.2 in (5), there is the problem that the respective compounds are hydrides which are very active and very difficult to handle in practice and, thus, the method is unsuitable for mass production.
The present invention was created to address such various conventional problems, and has for its object provision of an improved method for forming a CVD film And apparatus for manufacturing a semiconductor device suitable for both formation of an interlevel insulator between Al and Al and formation of an interlevel insulator between Al and a gate and also suitable for mass production.


SUMMARY OF THE INVENTION

According to a first embodiment of the method for forming a CVD film of the present invention, an organic silane compound containing siloxane or alkoxysilane and an alkoxy compound o

REFERENCES:
patent: 4791005 (1988-12-01), Becker et al.
patent: 4845054 (1989-07-01), Mitchener
patent: 5028566 (1991-07-01), Lagendijk
Yamaguchi et al, "Superconducting properties of Ba.sub.2 YCu.sub.3 O.sub.7-x thin films prepared by chemical vapor deposition on SrTiO.sub.3 and metal substrate," Appl. Phys. Lett. vol. 55, No. 15, Oct. 1989 pp. 1581-1582.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method for forming CVD thin glass films does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for forming CVD thin glass films, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for forming CVD thin glass films will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2376358

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.