Chemistry: electrical and wave energy – Processes and products – Coating – forming or etching by sputtering
Reexamination Certificate
1995-07-28
2002-07-30
McDonald, Rodney G. (Department: 1753)
Chemistry: electrical and wave energy
Processes and products
Coating, forming or etching by sputtering
C204S192130, C204S192150
Reexamination Certificate
active
06425990
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method for fabricating a transparent conductive ITO (Indium Tin Oxide) film, and, more particularly, to a method for fabricating transparent conductive ITO film which is utilized as an electrode of a liquid crystal display device, a solar battery, or the like by using a sputtering process.
2. Description of the Prior Art
A transparent conductive ITO film has been known which contains indium (In) and oxygen (O) as the basic component elements and tin (Sn) is added as a donor. Conventional methods for fabricating the transparent conductive ITO film include chemical film formation processes such as a spray process, a chemical vapor deposition (CVD) process, and a wet dip process, and physical film formation processes such as a vacuum evaporation process, and a sputtering process.
Among the above thin film fabricating methods, the sputtering process is superior to the others in that it can provide a transparent conductive ITO film with a relatively low resistance, and uniformly form a transparent conductive ITO film on a large substrate such as a glass plate.
There are direct current (DC) discharge-type sputtering processes and radio frequency (RF) discharge-type sputtering processes. The direct current discharge sputtering process (called the “DC sputtering process”) is conventionally used because it is inexpensive, provides stable discharge and has excellent controllability. A magnetron sputtering process is also conventionally used. This process converges plasma on the surface of a target with closed magnetic field generated by one or more magnets located behind the target. Because it has a high film formation rate, the magnetron sputtering process has excellent mass production capability. In view of the foregoing, a DC magnetron sputtering process which combines the direct current discharge process and the magnetron process is commonly currently used as the mass production apparatus for forming transparent conductive ITO films. Recently, a DC magnetron sputtering apparatus has been further developed to perform sputtering over the entire surface of the target by reciprocating (rocking) or eccentrically rotating the magnet located behind the target.
The sputtering process is known to have substrate temperature and oxygen partial pressure as factors affecting the resistivity of the resulting transparent conductive ITO film. As for the substrate temperature, a higher temperature provided a lower resistivity. For the oxygen partial pressure, on one hand the carrier density of the formed ITO film becomes higher in a region formed under a lower partial pressure because many oxygen vacancies exist in the film, while the mobility of the carriers becomes low. On the other hand, the carrier density of the ITO film formed in a region under higher partial pressure becomes lower as the number of oxygen vacancies decreases, while the mobility of carrier becomes higher. Because the resistivity is the inverse of the product of the carrier density and the mobility, there is optimal oxygen partial pressure where the resistivity is minimized in balancing between the carrier density and the mobility. Conventional sputtering processes have been used to fabricate a transparent conductive ITO film with low resistivity by adjusting the substrate temperature and the oxygen partial pressure as parameters. A sputtering process is disclosed in Japanese patent publication HEI 2-47255, herein incorporated by reference, wherein an oxide thin film is manufactured in a period in which only an inert gas (argon) is introduced and in other periods only oxygen gas is introduced.
SUMMARY OF THE INVENTION
In the conventional sputtering process, there is a problem that the resistivity of the transparent conductive ITO film formed on each substrate gradually increases as the number of the substrates on which the ITO film is formed increases. In a continuous sputtering process, a transparent conductive ITO film having the same resistivity cannot be formed on each sequentially processed substrate. That is, the continuous sputtering process causes a problem in that the resistivity increases as sputtering proceeds to sequentially form the ITO film on substrates.
FIG. 2
shows a graph of the characteristics of the change in the films resistivity to cumulative power supplied to the target when transparent conductive ITO films are formed on a plurality of substrates by the continuous DC magnetron sputtering process. In the example, the target was a disk-shaped mixed sintered material (density of 95%) of In
2
O
3
to which 10 wt % of SnO
2
is added and having a diameter of 8 inches (&phgr; 8″). The ITO film was formed on a substrate heated to 200° C. at a power of 300 W and under a pressure of 3×10
−3
Torr. The sputtering gas was a mixture of argon (Ar) and oxygen (O
2
) gases. The partial pressure of the oxygen in the sputtering gas was adjusted to be within a range of from 6×10
−5
to 1.5×10
−4
to minimize resistivity every time a constant power (3 kWh) is cumulated. As clearly seen from
FIG. 2
, the resistivity of the film increased as the cumulative power increased.
When transparent conductive ITO films are formed on a number of substrates by the continuous DC magnetron sputtering process, the conventional sputtering process cannot provide uniform resistivity for each substrate, as shown in FIG.
2
. In conventional film formation processes, to maintain the resistivity of each substrate to within a range where the performance of the device is guaranteed, it is necessary to grind the surface of the target, or to replace the target itself before the potential end of its life. This prevents the productivity from being improved, so that the manufacturing cost is increased.
Although
FIG. 2
shows that the resistivity increases as the cumulative power increases in a case where transparent conductive ITO films are formed on a plurality of substrates by continuous sputtering, strictly speaking, such increase of the resistivity of the film for the cumulative power may occur even when forming a film on one substrate. That is, the resistivity gradually increases in the direction of film thickness even on a transparent conductive ITO film formed on one substrate. Therefore, when it is intended to form a film with considerable thickness on a substrate, there also arises a problem that the resistivity of entire film increases as the film becomes thicker.
An object of the present invention is to provide a method capable of fabricating a transparent conductive ITO film with resistivity within a predetermined range until the end of the life of the target when transparent conductive ITO films are continuously formed on a plurality of substrates by continuous sputtering, and capable of fabricating a transparent conductive ITO film with resistivity being within a predetermined range even when the film becomes thicker in forming it on a single substrate.
To attain the above object, the method for fabricating a transparent conductive ITO film according to the first feature of the present invention is a method for fabricating a transparent conductive ITO film which has In and O as basic component elements and which is added with Sn as a donor, in an atmosphere of a mixture of rare gas and oxygen gas by a sputtering process using a mixture of oxides of In and Sn as a target wherein it comprises a first step of forming a transparent conductive ITO film on a substrate, and a second step of interrupting the first step and performing discharge in a state with a partial pressure of oxygen higher than that in the first step to compensate for the oxygen deficiency in the target, the first and second steps being repeated alternately.
The method according to the second feature of the present invention is a method according to the first feature wherein a transparent conductive ITO film is continuously formed on each of a plurality of substrates by the first step, and then the second step is performed.
The method accordin
Anelva Corporation
McDonald Rodney G.
LandOfFree
Method for fabricating transparent conductive ITO film does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for fabricating transparent conductive ITO film, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for fabricating transparent conductive ITO film will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2918206