Semiconductor device manufacturing: process – Formation of semiconductive active region on any substrate – On insulating substrate or layer
Reexamination Certificate
2002-12-12
2004-06-15
Mulpuri, Savitri (Department: 2812)
Semiconductor device manufacturing: process
Formation of semiconductive active region on any substrate
On insulating substrate or layer
C438S483000, C117S104000, C427S255340
Reexamination Certificate
active
06750120
ABSTRACT:
FIELD OF THE INVENTION
The invention relates to the field of semiconductor processing. More specifically, the invention relates to forming a nitrogen containing group III-arsenide compound semiconductor using ammonia as a precursor.
BACKGROUND OF THE INVENTION
Long wavelength lasers, lasers that emit light in wavelengths between 1.3 micrometers and 1.6 micrometers, are highly desirable for telecommunication system use because at these “telecom wavelengths”, a “wavelength window” exists where light absorption in optical fibers is minimized. As telecommunications increasingly rely on optical signal transmission, these long wavelength lasers have become increasingly important.
Most optoelectronic components in the telecom wavelength range are grown on InP substrates. An InP substrate is preferred because the substrate easily lattice matches with high indium composition InGaAs films used in the fabrication of devices that emit 1.3-1.6 micron wavelength light. However, high substrate costs and low device yields makes InP-based optoelectronic devices rather expensive. Devices based on GaAs substrates would be much cheaper, but the difference in lattice constant normally prevents the growth of InGaAs with high In compositions (~50% indium mole fraction is preferred to achieve relevant telecom outputs) on GaAs substrate.
The bandgap in a semiconductor laser determines the frequency of light output by a semiconductor laser. Recently it has been demonstrated that by incorporating small amounts (fraction of a percent to a few percent) of nitrogen into the InGaAs film, the band gap of InGaAs alloys grown on GaAs substrate can be reduced thereby shifting the light emitted by the resulting devices to longer wavelengths. Indium Gallium Arsenide Nitride alloys have been found to be excellent semiconductor materials for fabricating the active region of VCSELS or other long-wavelength optoelectronic devices (e.g. edge-emitting laser, photodetectors or solar cells). Using elementary nitrogen as a group V source and a Molecular Beam Epitaxy (MBE) process, several groups have fabricated InGaAsN based lasers that output 1.3 micrometer wavelength light. See, M. Kondow et al., Jpn. J. Appl. Phys., Vol. 35, 1273 (1996) and M. Kondow, S. Natatsuka, T. Kitatani, Y. Yazawa, and M. Okai, Electron. Lett. 32, 2244 (1996). However, MBE is a slow growth technique and therefore not well suited to mass production of high volume optoelectronic devices such as VCSELs, egde-emitting lasers or solar cells.
Metal Organic Chemical Vapor Deposition (MOCVD) is a suitable technique for volume production of InGaAsN lasers. However, the high growth temperatures and surface chemistry of MOCVD results in inefficient incorporation of elemental nitrogen (N) in the InGaAsN material. To increase the incorporation efficiency of Nitrogen in the InGaAsN, the Nitrogen is typically introduced in a dimethylhydrazine (DMHy) form as described in J. Koch, F. Hohnsdorf, W. Stolz, Journal of Electronic Materials, Vol. 29, 165 (2000) and A. Ougazzaden et al., Appl. Phys. Lett. 70, 2861 (1997) which are hereby incorporated by reference. Large oversupplies of DMHy are used to achieve sufficient amounts of nitrogen in the InGaAsN structure.
The use of large quantities of DMHy as a nitrogen source has two major disadvantages. The first disadvantage is high cost. DMHy is expensive, current costs for 100 grams of DMHy is approximately $5000. A second disadvantage of using DMHy as a Nitrogen source is the relatively high impurity levels that often exist in commercially available DMHy. High impurity levels are possibly one reason why MOCVD grown InGaAsN films are often inferior to MBE grown films.
Thus a better source of Nitrogen for forming InGaAsN structures is needed.
REFERENCES:
patent: 6471769 (2002-10-01), Hashimoto et al.
patent: 2002/0034467 (2002-03-01), Otsuka et al.
Sato, et al., “Room Temperature Operation of GalnNAs/GalnP Double Heterostructure Laser Diodes Grown by Metalorganic Chemical Vapor Deposition”,Japan Journal of Applied Physics, May 1997, Part 1, No. 5A, pp. 2671-2675.
Ougazzaden et al., “Metal Organic Vapor Phase Epitaxy Growth of GaAsN on GaAs Using Dimethylhydrazine and Tertiarybutylarsine”,Applied Physics Letters, 70, (21) May 26, 1997, pp. 2861-2863.
Kneissl Michael A.
Treat David W.
Chen Kent
Mulpuri Savitri
Xerox Corporation
LandOfFree
Method and apparatus for MOCVD growth of compounds including... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method and apparatus for MOCVD growth of compounds including..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method and apparatus for MOCVD growth of compounds including... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3364719