Paper making and fiber liberation
Processes and products
Multi-layer waterlaid webs or sheets
C162S125000, C162S127000, C162S129000, C162S132000, C523S201000, C524S460000, C525S330200, C525S327800, C525S902000, C526S080000, C526S201000, C604S365000, C604S367000, C604S381000, C604S378000
Reexamination Certificate
active
06425978
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to a latex binder for treating nonwoven fibers and a method of manufacture of a personal hygiene article including the latex binder. More particularly, the present invention relates to a latex binder for treating nonwoven fibers to make a nonwoven fabric that is particularly suitable for use as a permeable sublayer of a personal hygiene article.
BACKGROUND OF THE INVENTION
A nonwoven fabric is a web or continuous sheet of fibers laid down mechanically. The fibers may be deposited in a random manner or oriented in one direction. Most widely used fibers include cellulosics, polyamides, polyesters, polypropylene and polyethylene. The spun fibers, which may be drawn, are laid down directly onto a belt by carding, airlaying or wet-laying. The sheet is then bonded together with a latex binder and subsequently treated in an oven or a calendar to complete the bonding process.
Commonly used lattices for nonwoven fabrics are those prepared from polymers of butadiene-styrene, butadiene-acrylonitrile, vinyl acetate, acrylic monomers such as methyl acrylate, ethyl acrylate, methyl methacrylate and the like. It will be appreciated that to be useful as a nonwoven fabric in many applications, such as a permeable sublayer of a personal hygiene article, the latex binder should possess several desired physical properties. The desired physical properties include adequate tensile strength, a high modulus or stiffness under certain conditions, and good textile qualities such as tenacity, handle and the like.
It is an object of the present invention to provide a nonwoven fabric having a high modulus. It is another object of the present invention to provide a nonwoven fabric having desired physical properties. Yet another object of the present invention is to provide a nonwoven fabric of chemically bonded fibers that is simple and economical to manufacture.
SUMMARY OF THE INVENTION
Briefly, the present invention relates to a latex that is particularly suitable for utilization as a binder for nonwoven applications. The latex is prepared by a process including the steps of:
(1) polymerizing a monomer mixture comprising styrene, itaconic acid, surfactant and water soluble free radical initiator to form a seed;
(2) sequentially adding equal increments of a monomer mixture of styrene, butadiene and acrylic acid to the seed under emulsion polymerization conditions to form a styrene-butadiene-acrylic acid copolymer; and then
(3) neutralizing the styrene-butadiene-acrylic acid copolymer to a pH of about 4.5 to 7 to form the latex.
The latex is particularly suitable to treat nonwoven fibers to form a permeable sublayer of a personal hygiene article. The permeable sublayer is typically interposed between a topsheet layer and a backsheet layer typically used to form the personal hygiene article.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention relates to a latex suitable for utilization as a binder to chemically bond fibers and form a nonwoven fabric. The nonwoven fabric is particularly suitable for use as a permeable sublayer of a personal hygiene article of a type well known in the art. Examples of personal hygiene articles include diapers, feminine hygiene articles and the like.
The permeable sublayer of the personal hygiene article is a web or mat comprised of randomly arranged nonwoven fibers having an open structure and high loft. The web may be formed by carding when the fibers are of such a character, by virtue of their length and flexibility, as to be capable of carding. During carding the crimped fibers are placed on a moving support and then treated with a latex binder as described herein.
The fibers may include natural textile fibers such as jute, sisal, ramie, hemp, and cotton as well as many artificial organic textile fibers or filaments including rayon, those of cellulose esters such as cellulose acetate, vinyl resin fibers such as those of polyvinyl chloride, copolymers of vinyl chloride with vinyl acetate, vinylidene chloride or acrylonitrile, copolymers of acrylonitrile with vinyl chloride, vinyl acetate, methacrylonitrile, vinyl pyridine, polymers and copolymers of olefins such as ethylene and propylene, also condensation polymers such as polyamides or nylon types, polyesters such as ethylene glycol terephthalate polymers and the like.
The fibers may be of one composition or mixtures of fibers in a given web. The preferred fibers include polyolefins, especially polyesters, poly(ethylene terephthalate), and acrylics, polyamides, polypropylene. The polyolefin fibers include polypropylene, polyethylene, polybutene and their copolymers. The polyester fibers include any long chain synthetic polymer composed of at least 85% by weight of an ester of a dihydric alcohol and terephthalic acid such as polyethylene terephthalate, and, in addition liquid crystal polyesters, thermotropic polyesters and the like. The acrylic fibers include any fiber forming substance containing a long chain synthetic polymer composed of at least 85% by weight acrylonitrile units —CH
2
CH(CN)—. It will be appreciated that other types of fibers may also be employed in accordance with the teachings of the present invention. For example, high modulus fibers more commonly known as graphite fibers made from rayon, polyacrylonitrile or petroleum pitch may also be used.
The fibers may be of most any suitable size and randomly arranged to most any suitable thickness depending upon the desired end use of the nonwoven fabric. The fibers are typically of a length of about 0.25 to 2 inches and typically about 1.2-15 denier. The fibers may be laid in an overlapping, intersecting random arrangement to a thickness of about 0.25 inches or less to form a mat of fibers. The fibers may be arranged by most any convenient known manner such as by wet laying, air-laying or carding.
The fabric of the present invention is made by forming a mat of randomly arranged fibers. After the fibers are randomly arranged as desired, a latex binder is applied to the fibers. The latex binder is applied in an effective amount which will result in the fabric having sufficient strength and cohesiveness for the intended end use application. As well known in the art, the latex binder may be applied to the layer of randomly arranged fibers in a spaced, intermittent pattern of binder sites, or uniformly applied throughout the layer of fibers. It will be further appreciated that the exact amount of the latex binder employed depends, in part, upon factors such as the type of fiber, weight of fibrous layer, nature of latex binder and the like. For example, end uses which require a stronger fabric may utilize more binder. A typical content of latex binder applied on a fiber mat is about 15-40 wt %. It is preferred that the minimum amount of latex binder be applied to obtain the desired required physical properties of the nonwoven fabric such as tensile, hand and the like as well known in the art.
The latex is then cured using methods well known in the art such as by application of heat or radiation. The term “cured” refers to the latex being cross-linked to increase the tensile strength properties. The curing of the treated fibers is affected at a temperature above the glass transition temperature of the binder.
To obtain a sufficient thickness for the end use intended a plurality of webs may also be superimposed upon one another to achieve a sufficient thickness. The webs may be superimposed by alternating layers of carded webs disposed with their fiber orientation directions disposed at angles such as 60 degrees or 90 degrees with respect to intervening layers.
The latex binder utilized in accordance with the present invention may be prepared by well-known conventional emulsion polymerization techniques using one or more ethylenically unsaturated monomers and a polymeric surfactant as herein disclosed and additional conventional additives such as free-radical initiators, optional chain transfer agents, chelating agents and the like can be utilized as set forth in U.S. Pat. No. 5,166,259 to Schmeing and
Diehl David F.
McBain Carla Dittman
Egwim K C
Meenan Larry R.
Omnova Solutions Inc.
Rywalski Robert F.
Wu David W.
LandOfFree
Latex binder for nonwoven fibers and article made therewith does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Latex binder for nonwoven fibers and article made therewith, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Latex binder for nonwoven fibers and article made therewith will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2874865