Semiconductor device manufacturing: process – Coating of substrate containing semiconductor region or of... – Insulative material deposited upon semiconductive substrate
Reexamination Certificate
1998-06-10
2001-02-20
Baxter, Janet (Department: 1752)
Semiconductor device manufacturing: process
Coating of substrate containing semiconductor region or of...
Insulative material deposited upon semiconductive substrate
C438S782000, C427S240000, C427S346000, C118S320000, C430S270100
Reexamination Certificate
active
06191053
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to an improved method and apparatus for coating semiconductor substrates with organic photoresist polymers. In particular, this invention relates to an improved method and apparatus for coating semiconductor substrates which provides a more uniform photoresist layer and is much more efficient than are current methods in the use of expensive photoresist solutions.
BACKGROUND OF THE INVENTION
The manufacture of integrated circuits involves the transfer of geometric shapes on a mask to the surface of a semiconductor wafer. Thereafter, the semiconductor wafer corresponding to the geometric shapes, or corresponding to the areas between the geometric shapes, is etched away. The transfer of the shapes from the mask to the semiconductor wafer typically involves a lithographic process. This includes applying a solution of a pre-polymer solution to the semiconductor wafer, the pre-polymer being selected to form a radiation-sensitive polymer which reacts when exposed to ultraviolet light, electron beams, x-rays, or ion beams, for example. The solvent in the pre-polymer solution is removed by evaporation, and the resulting polymer film is then baked. The film is exposed to radiation, for example, ultraviolet light, through a photomask supporting the desired geometric patterns. The images in the photosensitive material are then developed by soaking the wafer in a developing solution. The exposed or unexposed areas are removed in the developing process, depending on the nature of the radiation-sensitive material. Thereafter, the wafer is placed in an etching environment which etches away the areas not protected by the radiation-sensitive material. Due to their resistance to the etching process, the radiation sensitive-materials are also known as photoresists, and the term photoresist is used hereinafter to denote the radiation-sensitive polymers and their pre-polymers.
The photoresist film thickness required depends on the desired resolution, defect protection, and step coverage. Thicker films provide better adhesion, greater protection for reactive ion erosion, and improved defect protection. However, thicker films also result in lower resolution because they take longer to expose and develop. Photoresist film thicknesses used in current semiconductor manufacturing may be typically 0.5 to 4 &mgr;m thick.
Thickness uniformity of the photoresist layer is an important criterion in the manufacture of integrated circuits. When the radiation is focused through the mask onto the coating, variations in thickness of the coating prevent the precise focus over the entire surface of the wafer which is required to obtain the sharpness necessary to ensure satisfactory reproduction of the geometric patterns on the semiconductor wafer for advanced circuits with line width dimensions approaching 0.25 &mgr;m line widths and smaller over a surface. Photoresist film thickness uniformity is required to maintain good transfer of the mask pattern to the photoresist. Uniformity is important to maintain a constant exposure level across the surface of the wafer. Nonuniformities cause position overlay errors when optical steppers attempt to sense alignment marks beneath the photoresist film. Nonuniformities also change the reflectivity of a photoresist deposited over an oxide.
The small critical dimensions of microelectronic devices require photoresist coating thickness typically to be uniform to within 10 Å (3&sgr;). As the critical dimension decreases further, even better uniformities will be required.
The high cost of the photoresist pre-polymer solutions makes it desirable to devise methods of improving the efficiency of the coating process so as to minimize the amount of the polymer solution required to coat a substrate.
Methods which have been used or proposed for coating wafers include dip coating, meniscus coating, spray coating, patch coating, bubble coating, chemical vapor deposition, and spin coating. Only a few of these methods produce photoresist films with the thicknesses and uniformities required for semiconductor production. Of these methods, only spin coating has a production rate fast enough to meet the demands of chip manufacturers. One major shortcoming of spin coating, however, is that it can waste as much as 90%, or more, of the photoresist applied to the wafer surface.
About one million gallons of photoresist are consumed each year at a cost of several hundred million dollars. As the critical dimension of semiconductor devices becomes smaller, new deep UV photoresists will be used. These new photoresists can cost five or more times the cost of the i-line photoresists used currently. Therefore, a new coating method is needed which wastes less photoresist while producing uniform, defect-free coatings at a rate comparable to that of spin coating.
OBJECTS AND SUMMARY OF THE INVENTION
One object of this invention is to provide an improved wafer coating process and apparatus which provide greater coating uniformity across the entire surface of the wafer.
Another object of the invention is to provide an improved wafer coating process and apparatus which provide coating uniformity with less waste and more efficient use of the photoresist.
In a first aspect the invention provides a method of applying a coating of photoresist to a circular semiconductor wafer, the wafer having a top surface, a center, and an outer edge, the method comprising extruding a ribbon of photoresist, the ribbon having a width bounded by outer and inner sides, the ribbon extruded in a spiral pattern which covers the entire top surface of the wafer.
In a second aspect, the invention provides a method of applying a coating of photoresist to a circular semiconductor wafer, the wafer having a top surface, a center, a diameter, and an outer edge, the method comprising the steps of mounting the wafer on a chuck, the top surface of the wafer aligned horizontally and oriented upward; positioning an extrusion head adjacent to the outer edge of the wafer and above the top surface of the wafer, the extrusion head configured to extrude photoresist out an extrusion slot, the extrusion slot having a length bounded by a first end and a second end, the extrusion head positioned with the extrusion slot aligned radially with respect to the wafer, the first end of the extrusion slot located adjacent to the outer edge of the wafer, and the second end of the extrusion slot outside the outer edge of the wafer; rotating the wafer about its center; extruding a ribbon of photoresist from the extrusion slot, the ribbon having a width bounded by outer and inner sides, the width of the ribbon substantially equal to the length of the slot; and, while extruding photoresist from the extrusion slot, and maintaining the extrusion slot aligned radially with respect to the wafer, moving the extrusion head radially inward from the outer edge of the wafer toward the center of the wafer until the photoresist covers the entire top surface of the wafer.
In a third aspect, the invention provides a method of applying a coating of photoresist to a circular semiconductor wafer, the wafer having a top surface, a center, a diameter, and an outer edge, the method comprising the steps of mounting the wafer on a chuck; positioning an extrusion head at the center of the wafer and above the top surface of the wafer, the extrusion head configured to extrude photoresist out an extrusion slot, the extrusion slot having a length bounded by a first end and a second end, the extrusion head positioned with the extrusion slot aligned radially with respect to the wafer, the second end of the extrusion slot located at the center of the wafer and the first end of the extrusion slot located between the center of the wafer and the outer edge of the wafer; rotating the wafer about its center; extruding a ribbon of photoresist from the extrusion slot, the ribbon having a width substantially equal to the length of the slot; and, while extruding photoresist from the extrusion slot, and maintaining the extrusion slot aligned radially with respe
Chun Jung-Hoon
Derksen James
Han Sangjun
Baxter Janet
Gilmore Barbara
Silicon Valley Group Inc.
Wilson Sonsini Goodrich & Rosati
LandOfFree
High efficiency photoresist coating does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High efficiency photoresist coating, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High efficiency photoresist coating will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2590720