Adhesive bonding and miscellaneous chemical manufacture – Delaminating processes adapted for specified product – Delaminating in preparation for post processing recycling step
Patent
1986-08-12
1987-09-01
Powell, William A.
Adhesive bonding and miscellaneous chemical manufacture
Delaminating processes adapted for specified product
Delaminating in preparation for post processing recycling step
134 2, 156647, 156663, 156667, 156903, 252 795, 252 791, B44C 122, C03C 1500, C03C 2506
Patent
active
046907270
ABSTRACT:
Increased optical transmission is provided for a body of optically transparent polycrystalline alumina by coating at least one major surface of said alumina body with a solid glaze coating and subsequently melting said coating at elevated temperatures to dissolve the surface alumina grains in physical content therewith to provide a smoother surface when the coating residue has been removed. More particularly, a solid glaze coating is first deposited on said major surface of the alumina body and the coated alumina body thereafter heated to sufficiently elevated temperatures for the glaze liquification whereupon surface alumina grains in physical contact therewith are dissolved in a manner which reduces the high spots on the individual surface alumina grains without materially introducing low spots at the grain boundaries and wherein the individual alumina surface grains have been preferentially etched in certain of the crystalline axis directions. The present glaze material comprises an alkali metal borate other than lithium borate having an alkali metal oxide to boron oxide weight ratio in the range from about 1:2 up to 1:4 and which is deposited on the major surface of said alumina body as a liquid suspension.
REFERENCES:
patent: 3935495 (1976-01-01), Scott et al.
patent: 4150317 (1979-04-01), Laska et al.
patent: 4285732 (1981-08-01), Charles et al.
McVey Charles I.
Scott Curtis E.
General Electric Company
Jacob Fred
McDevitt J. F.
Powell William A.
Schlamp Philip L.
LandOfFree
Glaze polishing polycrystalline alumina material does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Glaze polishing polycrystalline alumina material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Glaze polishing polycrystalline alumina material will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1263631