Stock material or miscellaneous articles – Coated or structually defined flake – particle – cell – strand,... – Particulate matter
Reexamination Certificate
1998-12-18
2001-04-24
Le, Hoa T. (Department: 1773)
Stock material or miscellaneous articles
Coated or structually defined flake, particle, cell, strand,...
Particulate matter
C095S096000, C428S680000, C428S689000, C428S702000, C428S703000
Reexamination Certificate
active
06221492
ABSTRACT:
FIELD OF THE INVENTION
The invention relates to adsorbent particles which can be used in a process for separating by adsorption the constituents of a gas flow, such as air, preferably a process of the PSA type, and more particularly of the VSA type.
BACKGROUND OF THE INVENTION
It is known that the gases in air, such as in particular oxygen and nitrogen, are very important industrially.
At present, one of the non-cryogenic techniques used for producing these gases is the technique referred to as PSA (Pressure Swing Adsorption), which encompasses not only PSA processes proper, but also similar processes, such as VSA (Vacuum Swing Adsorption) or MPSA (Mixed Pressure Swing Adsorption) or TSA (Temperature Swing Adsorption) processes.
According to this PSA technique, when the gas mixture to be separated is, for example, air and the component to be recovered is oxygen, the oxygen is separated from the gas mixture using preferential adsorption of at least nitrogen on a material which preferentially adsorbs at least nitrogen and is subjected to cycles of given pressure in the separation zone.
The oxygen, which is adsorbed little or not at all, is recovered at the outlet of the separation zone; it has a purity, in general, of from 90% to 93%.
More generally, a PSA process for the non-cryogenic separation of a gas mixture comprising a first compound which is adsorbed preferentially on an adsorbent material, and a second compound which is less preferentially adsorbed on the adsorbent material than the first compound, with a view to producing the second compound, cyclically comprises at least:
a step of preferentially adsorbing at least the first compound on the adsorbent material, at an adsorption pressure referred to as the “high pressure”, with recovery of at least some of the second compound produced in this way;
a step of desorbing the first compound thus trapped by the adsorbent, at a desorption pressure which is lower than the adsorption pressure and is referred to as the “low pressure”;
a step of recompressing the separation zone comprising the adsorbent, by changing from the low pressure to the high pressure.
Conventionally, the adsorbent particles are placed in one or more adsorbers, so as to form one or more successive layers of adsorbent within each adsorber.
When an adsorber contains several layers or beds of adsorbent particles, these various beds may consist of particles of the same nature, for example beds of zeolite particles, or of different natures, for example a bed of alumina particles followed by one or more beds of zeolite particles.
Furthermore, the adsorbent beds may be placed horizontally within each adsorber, that is to say being stacked on one another, or vertically, that is to say being juxtaposed with one another according to the so-called radial technique.
Moreover, it is known that the separation efficiency for a gas mixture, such as air, depends on a number of parameters, in particular the high pressure, the low pressure, the type of adsorbent material used and its affinity for the compounds to be separated, the composition of the gas mixture to be separated, the adsorption temperature of the mixture to be separated, the size of the adsorbent particles, the composition of these particles and the temperature gradient set up inside the adsorbent bed.
At present, although it has not been possible to determine a general behavior law, knowing that it is very difficult to connect these various parameters with one another, it is also known that the nature and properties of the adsorbent used have an essential role in the overall efficiency of the process.
Currently, zeolites are the adsorbents most widely used in PSA processes, in particular VSA processes.
The zeolite particles used as aggregated adsorbent in PSA processes are synthesized in very fine powder form, which powder is then aggregated and formed into aggregated particles having a size of the order of from 0.4 mm to several millimeters.
The specific purpose of forming the adsorbent particles is to provide a particulate adsorbent whose geometrical characteristics are compatible with the constraints pertaining to, in particular, mechanical strength and adsorption kinetics which are inherent in the separation process employed.
The industrial fabrication of the adsorbent particles is carried out, for example, by aggregating the zeolite powder using a binder, for example a clay, such as kaolin, attapulgite, bentonite or the like.
There are currently two main forms of adsorbent particles, namely on the one hand cylindrically shaped extrudates and, on the other hand, spheres or beads obtained by accretion. In this regard, reference may in particular be made to the documents D. M. Ruthven,
Principles of adsorption and adsorption processes,
John Wiley & Sons, 1984, p.20, or D. W. Breck, Zeolite Molecular Sieves, John Wiley & Sons, 1974, p.745.
Adsorbents having particular shapes are furthermore also known, for example noncylindrical extruded adsorbents or honeycomb-structure extrudates.
In general, the extruded adsorbent particles known from the prior art are obtained by extruding a paste obtained by mixing zeolite, a binder and water, and optionally additives, such as pore-forming agents or extruding agents, then baking this paste at high temperature, in general at more than 500° C.
However, extruded adsorbents have several drawbacks, namely in particular that their angulated ends promote their attrition when they are being employed, and their very elongate cylindrical geometry facilitates their fracture. Nevertheless, they do in general have a good ratio of their external surface area to their internal volume, which is favorable for the adsorption kinetics.
Spherical adsorbent particles are obtained by accretion from pre-existent particles, called seeds, which are circulated in the presence of binder and zeolite powder while spraying with water, so as to obtain adsorbent spheres by a snowball effect, which adsorbent spheres are then baked at high temperature.
Spherical adsorbent particles of this type generally have good resistance to attrition and crushing, but have a low ratio of their external surface area to their internal volume, which is unfavorable for the adsorption kinetics.
Conventionally, the prior art considers the sphere to be a valid geometrical model for studying diffusion and adsorption phenomena, as mentioned in the document R. T. Yang,
Gas Separation by Adsorption Processes,
Butterworths, 1987, p.168.
Indeed, it can be stated that almost all studies on the diffusion of gases in aggregated zeolite particles are based on the model with spherical symmetry, see in particular D. M. Ruthven,
Principles of adsorption and adsorption processes,
p.235-273.
DESCRIPTION OF THE INVENTION
One object of the present invention is therefore to provide adsorbent particles having characteristics which are improved both from the adsorption kinetics viewpoint and from the mechanical and strength viewpoints.
Another object of the invention is to provide adsorbent particles which can be used in gas separation processes such as PSA processes.
Yet another object of the invention is to provide a process for separating gases, in particular a PSA or VSA process for separating gases from air, employing such adsorbent particles.
SUMMARY OF THE INVENTION
The invention therefore relates to aggregated adsorbent particles having a shape similar to an ellipsoid, the ellipsoid having a first axis (A—A) or main axis of length (a), a second axis (B—B) of length (b) and a third axis (C—C) of length (c), the first axis (A—A), second axis (B—B) and third axis (C—C) being perpendicular, with a>b≧c, the ratio (a/b) of the length (a) of the first axis (A—A) to the length (b) of the second axis (B—B) being such that: 1.05<a/b<2.50.
Depending on the case, the adsorbent particles of the invention may include one or more of the following characteristics:
they have a shape similar to an ellipsoid of revolution, that is to say b=c;
they are substantially free of sharp edges;
the ratio (a/b) is between 1.08 and 2, pref
Labasque Jacques
Moreau Serge
L'Air Liquide, Societe Anonyme pour l'Etude et Exploit
Le Hoa T.
Young & Thompson
LandOfFree
Ellipsoidal adsorbent particles and their use in a gas... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Ellipsoidal adsorbent particles and their use in a gas..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Ellipsoidal adsorbent particles and their use in a gas... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2522688