Coating processes – Direct application of electrical – magnetic – wave – or... – Pretreatment of substrate or post-treatment of coated substrate
Reexamination Certificate
1998-02-25
2001-01-09
Padgett, Marianne (Department: 1762)
Coating processes
Direct application of electrical, magnetic, wave, or...
Pretreatment of substrate or post-treatment of coated substrate
C427S533000, C427S534000, C427S252000, C427S253000
Reexamination Certificate
active
06171661
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention is directed toward the field of manufacturing integrated circuits.
2. Description of the Related Art
Presently, aluminum is widely employed in integrated circuits as an interconnect, such as plugs and wires. However, higher device densities, faster operating frequencies, and larger die sizes have created a need for a metal with lower resistivity than aluminum to be used in interconnect structures. The lower resistivity of copper makes it an attractive candidate for replacing aluminum.
One challenge in employing copper instead of aluminum is the fact that copper dry etching is not presently feasible. A polishing process, such as chemical mechanical polishing, is used to remove undesirable portions of a deposited layer of copper. The need to use chemical mechanical polishing presents a challenge, because copper has poor adhesion to materials that are presently being used as diffusion barriers beneath the copper. The polishing of copper that is deposited over a diffusion barrier can therefore result in portions of the copper being undesirably peeled away from the surface of the diffusion barrier. This can render an integrated circuit defective.
When depositing copper, it is desirable to employ chemical vapor deposition (“CVD”), as opposed physical vapor deposition, because CVD provides for a more conformal layer of copper. However, the chemical vapor deposition of copper presents a further challenge. The challenge arises from a byproduct that is produced during the deposition of the copper.
In one instance, the chemical vapor deposition of copper is achieved by using a precursor known as Cupraselect, which has the formula Cu(hfac)L. The L represents a Lewis base compound, such as vinyltrimethylsilane (“VTMS”). The (hfac) represents hexafluoroacetylacetonato, and Cu represents copper. During the CVD of copper using the Cu(hfac)L precursor, the precursor is vaporized and flowed into a deposition chamber containing a wafer. In the chamber, the precursor is infused with thermal energy at the wafer's surface, and the following reaction results:
2 Cu(hfac)L→Cu+Cu(hfac)
2
+2L (Eqn. 1)
The resulting copper (Cu) deposits on the upper surface of the wafer, along with the Cu(hfac)
2
byproduct. The gaseous Lewis base byproduct (2L) is purged from the chamber. The presence of the byproduct as well as other contaminants on the wafer's surface reduces the adhesion of the copper to an underlying diffusion barrier, such as tantalum nitride.
In order to improve the adhesion of copper to an underlying diffusion barrier, the process for depositing copper has been divided into two steps. During a first step, physical vapor deposition (PVD) is performed to deposit a seed layer of copper. In PVD, a copper target is placed above a substrate onto which the copper is to be deposited. An argon gas is introduced into the environment between the copper target and the substrate. The argon gas is then excited through the use of a radio frequency (“RF”) signal to create a plasma containing ions.
The ions from the plasma strike the copper target, thereby dislodging particles of the copper which deposit on the substrate. These copper particles are generally ionized and thus are highly energetic. Such energetic copper ions adhere well to the barrier layers. The substrate is biased so that a voltage gradient forms between the target and the substrate, thereby causing the copper ions to accelerate along the gradient and bombard the substrate. As a result of the bombardment, the copper particles strongly adhere to the surface of the substrate. Secondly, this PVD process provides a clean interface between the copper seed layer and the barrier layer.
Once the seed layer of copper is deposited using PVD, a bulk layer of copper is deposited. The bulk layer is deposited by either standard chemical vapor deposition or electrical plating. The bulk layer of copper adheres relatively well to the copper seed layer.
However, the use of the PVD process results in poor step coverage, which is unacceptable for devices that have small features. Further, the PVD process cannot be accomplished in the same chamber as either chemical vapor deposition or electrical plating. The need to have both a PVD chamber and either a CVD or electrical plating chamber increases integrated circuit manufacturing costs.
Accordingly, it is desirable to provide for the conformal chemical vapor deposition of copper onto a diffusion barrier, so that the adhesion between the copper and underlying diffusion barrier is improved. It is also desirable for such a deposition to be performed in a single chamber (in situ). It is further desirable to decrease the production of contaminant byproducts during the deposition of copper, so that the deposition can be performed faster and with a smaller amount of precursor.
SUMMARY OF THE INVENTION
In accordance with the present invention, a layer of material, such as copper, is formed on the surface of a wafer with improved adhesion. In forming the layer of copper, a copper seed layer is first deposited on a surface of the wafer. Once the seed layer is deposited, the copper is bombarded (annealed) with ions to improve the adhesion of the copper to the surface of the wafer.
More specifically, ions in a plasma of an inert gas bombard the copper to provide the improved adhesion, which results in the copper being “mounted” on the surface of the wafer. This mounting increases the adhesion of the copper to the wafer's surface. Additionally, such bombardment flattens the copper grains to improve charge mobility. The plasma is generated in one embodiment of the present invention using an inert gas, such as argon. Alternatively, hydrogen can be employed along with an inert gas to generate a plasma for bombarding the copper as well as providing for contaminant removal. The addition of the hydrogen provides for the removal of copper deposition byproducts such as carbon, oxygen, fluorine and the like, thereby enhancing the adhesion of the copper to the barrier layer.
REFERENCES:
patent: Re. 35614 (1997-09-01), Norman et al.
patent: 4256780 (1981-03-01), Gaerttner et al.
patent: 4673587 (1987-06-01), Kamigaito et al.
patent: 4965090 (1990-10-01), G{umlaut over (a)}rtner et al.
patent: 5096737 (1992-03-01), Baum et al.
patent: 5395642 (1995-03-01), Hamerich et al.
patent: 5449799 (1995-09-01), Terfloth et al.
patent: 5480684 (1996-01-01), Sandhu
patent: 5561082 (1996-10-01), Matsuo et al.
patent: 5576071 (1996-11-01), Sandhu
patent: 5654245 (1997-08-01), Allen
patent: 5736192 (1998-04-01), Okamoto
patent: 5789027 (1998-08-01), Watkins et al.
patent: 5891349 (1999-04-01), Tobe et al.
patent: 5953634 (1999-09-01), Kajita et al.
patent: 6083568 (2000-07-01), Sandhu
patent: 0 461 032 A1 (1991-12-01), None
patent: 0 776 991 A1 (1997-06-01), None
M. Bai, X. Zhang, “Ion Beam Mixing Modification of Sputter-Deposied Molybdenum Films on Si3N4Ceramics”,Thin Solid Films, vol. 249, No. 2, Sep. 15, 1994.
A.E. Berkowitz, R.E. Benenson, R.L. Fleischer, L. Wielunski, W. A. Lanford, “Ion-Beam-Enhanced Adhesion of Au Films on Si and SiO2”,Nuclear Inst.&Methods in Physics Research, vol. B07/8, No. 1, Part 2, Mar. 1, 1985, pages.
G. Cheng, S. Xu, D. Ye, “Adhesion Modification in (Cu, Nb, Ti)/SiO2Pairs by Argon Ion Bombardment”, Nuclear Instruments and Methods in Physics Research B 135 (1998) pp. 545-549. No month.
D. Manger, G. Braeckelmann, S-C Seo, S. Baesor, S. Nijsten, T. Happ, K. Kumar, A. Kaloyeros, “Microstructure Effects in MOCVD Copper for ULSI Metallization”, VMIC Conference, Jun. 10-12, 1997. p.107-109.
C. Marcadal, E. Richard, J. Torres, J. Palleau, R. Madar, “CVD Process for Copper Interconnection”, Proceeding 1996 13th VMIC (1996) 174. No Month pp. 1-5 & Figures 1-7 & Table 1.
A. Jain,K-M. Chi,T.T. Kodas,M.J. Hampden-Smith,“Chemical Vapor Deposition of Copper from Hexafluoroacetylacetonato Copper (I) Vinyltrimethylsilane”,J. of Electrochemical Soc.,vol. 140,No. 5,May 1993,pp. 1434-1438.
Chang Mei
Chen Ling
Mak Alfred
Zheng Bo
Applied Materials Inc.
Padgett Marianne
Thomason Moser & Patterson
LandOfFree
Deposition of copper with increased adhesion does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Deposition of copper with increased adhesion, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Deposition of copper with increased adhesion will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2557531