Paper making and fiber liberation – Processes and products – Non-fiber additive
Reexamination Certificate
2001-11-13
2004-08-31
Chin, Peter (Department: 1731)
Paper making and fiber liberation
Processes and products
Non-fiber additive
C162S181400, C162S181500, C162S181600
Reexamination Certificate
active
06783631
ABSTRACT:
BACKGROUND OF THE INVENTION
This invention relates to a decorative paper which contains a pigment mixture of titanium dioxide and talc and the decorative coating materials obtained therefrom.
Decorative coating materials, so-called decorative sheets or decorative paper [paper impregnated with synthetic resin] is preferably used for surface coating in production of furniture and in completion of interiors. Decorative sheets are understood to be printed or unprinted sheets of paper impregnated with a synthetic resin and optionally treated at the surface. Decorative sheets are glued or bonded to a backing board.
Depending on the type of impregnation process, a distinction is made between decorative sheets with a thoroughly impregnated paper core and decorative sheets based on a preimpregnate, in which the paper is impregnated only partially online in the papermaking machine. Molded laminated materials (high-pressure laminates) are laminates produced by pressing several impregnated layered papers. The structure of these molded laminated materials consists in general of a transparent layer (overlay) which produces an extremely high surface stability, a decorative paper impregnated with a synthetic resin and one or more kraft papers impregnated with a phenolic resin. Molded fiber board and particle board as well as plywood can be used as the substrate for this.
In the laminates (low-pressure laminates) produced by the short-cycle method, the decorative paper impregnated with synthetic resin is pressed directly with a substrate, e.g., a particle board using a low pressure. The decorative paper used in the coating materials mentioned above is white or colored and may be with or without an additional imprint.
Special requirements are made of so-called decorative base paper such as high opacity for a better coverage of the substrate, uniform formation and grammage of the sheet for uniform resin uptake, high light stability, high purity and uniformity of the color for good reproducibility of the pattern to be printed, high wet strength for a smooth impregnation operation, suitable absorbency to achieve the required degree of resin saturation and dry strength which are important in re-rolling operations in the papermaking machine and in printing in the printing machine.
Decorative base paper is generally made of high-white sulfate pulp, mainly from hardwood pulp, up to 45% pigments and fillers and wet strength, retention agents and fixing agents. Decorative base paper differs from the usual paper in that it has a much higher filler content and there is none of the internal sizing or surface sizing which is usual in paper with the known sizing agents such as alkyl ketene dimers.
Opacity is one of the most important properties of decorative base paper. This characterizes the coverage with respect to the substrate.
A high opacity of the decorative base paper is also achieved by adding white pigments. Titanium dioxide is usually used as the white pigment. This pigment guarantees a high opacity and a good brightness and whiteness of the decorative base paper. However, the high price of titanium dioxide is a disadvantage.
Replacing some or all of the titanium dioxide with other white pigments has a negative effect on these properties. Matching of opacity can be achieved only by increasing the pigment content. However, the pigment content cannot be increased to an unlimited extent, because in this case, negative effects on the physical properties such as retention of the pulp suspension, strength, light-fastness and resin uptake can be expected.
SUMMARY OF THE INVENTION
The object of this invention is to make available an inexpensive decorative paper with a high opacity while at the same time having a reduced titanium dioxide content.
This object is achieved by a decorative base paper for decorative coating materials, wherein said decorative base paper contains a pigment mixture of a titanium dioxide and talc. The talc used according to this invention has a very narrow particle size distribution with a D50 of less than about 3 &mgr;m. This means that 50 wt % of the talc particles have a diameter of less than about 3 &mgr;m. Talc with a particle size distribution D50 of less than about 2 &mgr;m is especially preferred.
According to a further embodiment a decorative paper or decorative sheet is provided that includes the aforementioned decorative base paper.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The specific surface area of the talc used according to this invention is greater than about 30,000 m
2
/kg, or according to an especially preferred embodiment it is greater than about 40,000 m
2
/kg. On the other hand, the specific surface area of traditional types of talc is in the range of 8,000 to 16,000 m
2
/kg. The specific surface area was determined according to DIN 66,126.
The amount of talc in the pigment mixture is preferably 0.1 to 25 wt %, based on the total pigment content.
The titanium dioxide preset in the pigment mixture used in the decorative base paper according to this invention may be a titanium dioxide conventionally used in decorative paper. Such titanium dioxides are available commercially and may be used in the rutile or anatase modification. Such titanium dioxides of the rutile type are especially preferred.
Other fillers such as zinc sulfide, calcium carbonate, kaolin or mixtures thereof may be used.
The amount of filler in the decorative base paper may be up to 55 wt %, in particular 11 to 50 wt % or 20 to 45 wt %, based on the weight of the paper. The weight of the decorative base paper according to this invention may be in the range of 30 to 300 g/m
2
and is usually 40 to 200 g/m
2
. The weight is selected as a function of the specific application.
Softwood pulp (long-fiber pulp) or hardwood pulp (short-fiber pulp) may be used as the cellulose pulp for producing the decorative bulk paper according to this invention. It is also possible to use cotton fibers or mixtures of the types of cellulose mentioned above. For example, a mixture of softwood pulp and hardwood pulp in a ratio of 10:90 to 90:10 or mixtures of softwood pulp and hardwood pulp in a ratio of 30:70 to 70:30 are especially preferred. The pulp may have a degree of beating of 20 to 60 SR according to Schopper-Riegler.
The cellulose pulp mixture preferably has a cationically modified cellulose fiber content of at least 5 wt %, based on the weight of the cellulose mixture. A content of 10 to 50 wt %, in particular 10 to 20 wt % of the cationically modified cellulose in the cellulose pulp mixture has proven to be especially advantageous.
Cationically modified cellulose pulps are known from the journal
Das Papier
, volume 12 (1980), pp. 575-579, for example.
In a special embodiment of this invention, the cationically modified cellulose contained in the paper pulp has an effective cationic charge of 20 to 300 mmol/kg pulp, determined according to the internal method no. 4 of the Technical University of Darmstadt. Cellulose pulp fibers with a charge density of 30 to 100 mmol/kg are preferred. The term “effective cationic charge” is understood to refer to a charge density which has been balanced with the charge density of the non-cationized cellulose pulp. The charge density of the cellulose pulp depends on the amount of cationic agent to be used. The amount of cationizing agent may be 0.005 to 200 g/kg cellulose pulp.
The cationic modification of the cellulose pulp fibers may be accomplished through reaction of the fibers with epichlorohydrin resin and a tertiary amine or by reaction with quaternary ammonium chlorides such as chlorohydroxypropyl-trimethyl-ammonium chloride or glycidyltrimethyl-ammonium chloride.
In a preferred embodiment of this invention, cellulose pulp fibers that have been cationically modified by an addition reaction of quaternary ammonium compounds having glycidyl functional groups with hydroxyl groups of cellulose are used.
The decorative bulk paper according to this invention may contain wet strength agents such as polyamide/polyamine-epichlorohydrin resin, other polyamine d
Chin Peter
Cook Alex McFarron Manzo Cummings & Mehler, Ltd.
Technocell Dekor GmbH & Co. KG
LandOfFree
Decorative paper with a high opacity does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Decorative paper with a high opacity, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Decorative paper with a high opacity will most certainly appreciate the feedback.