Crucible for crystal pulling and method of manufacturing same

Single-crystal – oriented-crystal – and epitaxy growth processes; – Apparatus

Patent

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

117900, C30B 3500

Patent

active

061360945

DESCRIPTION:

BRIEF SUMMARY
TECHNICAL FIELD

The present invention relates to a crucible applied to a single crystal pulling apparatus for pulling single crystals of silicon, gallium or their compounds and to a producing method thereof. More particularly, the present invention relates to a crucible made of carbon fiber reinforced carbon composite material and to a method of producing a single crystal pulling crucible of carbon fiber reinforced carbon composite material by filament windings.


BACKGROUND ART

The present invention relates to a single crystal pulling crucible applied to an apparatus for pulling semiconductor single crystals by the Czochralski process (the CZ process) and to a producing method thereof.
For producing single crystals of silicon by the CZ process, a quartz crucible for silicon to be fused in the inside thereof and a carbon crucible for receiving the quartz crucible therein and supporting the same from outside have been used hitherto.
In use, the quartz crucible is subjected to the heat of fused silicon to be softened and thus is put into the state of its outside surface being closely contacting with the inner surface of the carbon crucible. If the quartz crucible is cooled in this state, a large stress will be generated in the carbon crucible having a larger coefficient of thermal expansion than the quartz crucible.
Proposals have been made that a single crystal pulling crucible be made of carbon fiber reinforced carbon composite material or C/C composite material having a mechanical strength to withstand the stress and a coefficient of thermal expansion relatively close to that of the quartz crucible, and to easily correspond with increase of size.
Japanese Utility Model Publication No. Hei 3 (1991)-43250 proposed that the crucible comprising a drum portion and a bottom portion be made of the C/C composite material at the drum portion only or over the entirety thereof. It also proposed that the filament windings be used as the producing method to mold the crucible by carbon fibers impregnated with matrix precursor is being helically wound on a crucible-like mandrel.
However, it is hard to wind the carbon fibers helically on the bottom portion having a curved form like a bowl, without any slip caused. This results in the insufficient winding of the bottom portion, and as such could not allow the bottom portion to have a sufficient strength.
Experiments show that the stress is most concentrated on an area extending from the drum portion to the bottom portion, and in the light of the difficulties in making the entire crucible by using the C/C composite material by the filament windings, the modification was proposed that only a boundary portion between the drum portion and the bottom portion be made of the C/C composite material. However, this modified method also uses the filament windings of carbon fibers impregnated with matrix precursors being wound on a crucible-like mandrel by using a parallel winding or a helical winding, in molding the crucible. Although it is easier to produce only the boundary portion between the drum portion and the bottom portion by using the C/C composite material than to produce the entirety of the drum portion and the bottom portion by using the C/C composite material, since the boundary portion between the drum portion and the bottom portion also has a curved part, it was still hard to effect the parallel winding or the helical winding at such a curved part, without any slip caused. As a result of this, those conventional methods have not succeeded in proposing the single crystal pulling crucibles of the C/C composite material having a sufficient strength not only at the drum portion but also at the bottom portion.
Also, the crucible-like mandrel used in the filament windings has the form of a shaft being extended through both ends of the bottom portion and the drum portion at the center thereof. Because of this, even when the entirety of the drum portion and bottom portion is produced by using the C/C composite material, the hole will inevitably remain at the center of the b

REFERENCES:
patent: 5858486 (1999-01-01), Metter et al.
patent: 5954875 (1999-09-01), Kato et al.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Crucible for crystal pulling and method of manufacturing same does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Crucible for crystal pulling and method of manufacturing same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Crucible for crystal pulling and method of manufacturing same will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-1959602

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.