Semiconductor device manufacturing: process – Formation of electrically isolated lateral semiconductive... – Total dielectric isolation
Reexamination Certificate
2001-11-01
2003-04-22
Dang, Trung (Department: 2823)
Semiconductor device manufacturing: process
Formation of electrically isolated lateral semiconductive...
Total dielectric isolation
C438S404000, C438S295000, C438S517000
Reexamination Certificate
active
06551898
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates generally to silicon-on-insulator structures, and more specifically to processing a polarizable layer in the buried oxide of silicon-on-insulator substrates for the fabrication of non-volatile memory.
2. Discussion of the Background
There are various types of commercial non-volatile memory that have been fabricated on bulk silicon, but no commercial non-volatile memories have been fabricated on SOI substrates that utilize a polarizable layer in the buried oxide in their operation.
Two known techniques for forming the buried oxide layer in SOI substrates are the implantation of oxygen ions in the separation-by-implantation-of-oxygen process (SIMOX) and the method of first growing a thermal oxide and then bonding. The difficulty is that the buried oxide formed using either of these commercial processes are non-polarizable.
The test for the polarizability of the buried oxide is (1) the fabrication of point-contact transistors, (2) measurement of the transistor characteristics, (3) application of a positive poling voltage to the back-gate or drain above the operating voltage and (4) remeasurement of the transistor characteristics. The procedure is then repeated, where a negative poling voltage of the same magnitude is applied to the back-gate or drain. Any significant reproducible hysteresis in the transistor characteristics indicates that the buried oxide has been polarized. These measurements were performed on a wide range of commercially available SOI substrates, and demonstrate that the buried oxides of these substrates are non-polarizable.
In the SIMOX process, a thin layer of a monocrystalline silicon substrate is separated from the bulk of the substrate by implanting oxygen ions into the substrate to form a buried dielectric layer. The SIMOX process provides a heterostructure in which a buried silicon dioxide layer serves as a highly effective insulator for surface layer electronic devices.
In the SIMOX process, oxygen ions are implanted into silicon, after which the material is annealed to form the buried silicon dioxide layer or BOX region. The annealing phase redistributes the oxygen ions such that the silicon/silicon dioxide boundaries become smoother and more abrupt, thus forming a sharp and well-defined BOX region.
One important criterion for SIMOX wafers is the defect density, which should be minimized in order to produce high quality wafers. Defect density can be defined in terms of the departure from perfect crystallinity in the silicon layer that is separated from the bulk substrate by the buried oxide layer. In general, as the oxygen ions are implanted into the wafer to produce the buried SiO
2
layer, atomic silicon is displaced. Additionally, excess silicon atoms from the growing BOX region can alter the crystal structure of the top silicon layer resulting in a variety of point and extended defects, such as threading dislocations and stacking faults, during the ion implantation and/or annealing processes. These defects degrade the quality and reliability of devices. e.g., transistors, that are subsequently formed in the upper silicon layer.
It is known that, in the SIMOX substrate, structure and quality of the buried oxide layer formed under the top silicon layer by implanting the oxygen ions into the single-crystal silicon substrate depend on an ion implanting quantity (dose of ions), so that the dose of oxygen ions as 10
17
-10
18
/cm
2
is required in order to form the buried oxide layer having the abrupt interface. But, there is the disadvantage of producing crystal defects in the top single-crystal silicon layer when the dose of ions is increased, and observing the relation of a crystal dislocation density and the dose of ions, when the dose of ions reaches over 1.0×10
18
/cm
2
, the dislocation density is increased and crystal quality of the top silicon layer where device elements are formed is inferior. When the dose of ions is controlled within the range between 0.5×10
18
/cm
2
and less than 1.0×10
18
/cm
2
in order not to produce the crystal defect, a breakdown electric field of the buried oxide layer is smaller and the breakdown voltage is decreased. Consequently, as a condition capable of obtaining the high breakdown electric field of the buried oxide layer and of achieving the low dislocation density in the top silicon layer, at an acceleration energy of 150-200 keV, for example, the ion implantation has been practiced by setting the dose of ions at around 0.4×10
18
/cm
2
(J. Mater. Res., Vol. 8, No. 3, 1993 pp. 524-534).
If a polarizable layer is formed in the buried oxide, then the polarizable layer/buried oxide combination can be used for the fabrication of non-volatile memory.
SUMMARY OF THE INVENTION
Accordingly, it is one object of the present invention to provide a novel process for creating a polarizable buried oxide in SOI substrates.
It is another object of this invention to provide a process for creating a polarizable buried oxide in SOI substrates by the implantation of ions.
It is another object of this invention to provide a process for creating a polarizable buried oxide in SOI substrates by the implantation of silicon ions into the buried oxide.
It is another object of this invention to provide a process for creating a polarizable buried oxide in SOI substrates by the channeling and implantation of ions such that damage effects to the top silicon region are reduced.
These and other objects, which will become apparent during the following detailed description, have been achieved by the inventors' discovery that a polarizable buried oxide layer in a SOI substrate may by prepared by:
externally heating the silicon-on-insulator substrate;
implanting ions into the buried oxide layer; and
annealing the silicon-on-insulator substrate.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention provides a process for forming a polarizable layer in a buried oxide layer of a silicon-on-insulator substrate for the fabrication of non-volatile memory, the process comprising:
externally heating the silicon-on-insulator substrate;
implanting ions into the buried oxide layer; and
annealing the silicon-on-insulator substrate.
A typical SOI includes a silicon substrate, an active silicon layer, and a buried oxide layer sandwiched between the active silicon layer and the silicon substrate. Generally, the buried oxide layer rests directly on and physically contacts the silicon substrate. Also, the active silicon layer generally rests on and physically contacts the buried oxide layer. The buried oxide layer electrically isolates the active silicon layer from the silicon substrate.
During the implantation stage, the dose of the implanted ion should be as high as can be obtained without damaging the active Si layer to such an extent that a subsequent anneal will not essentially rectify the damage.
Channeling of the ions during the implantation stage may minimize the damage to the active Si layer. Channeling, however, is not required according to the present invention.
The depth of the implant is determined by the energy. The implant energy required to obtain the desired implantation profile in the buried oxide layer will vary depending upon the implanted species, the thickness of the active Si layer and the angle of implantation. Other factors, such as the density of the buried oxide layer may also effect the required implantation energy. Thus, the energy required to obtain the desired implantation profile in the BOX is best determined empirically for each situation, using the knowledge of those skilled in the art of ion implantation. Typically, the peak implant concentration is 5 to 50 nm from the top silicon/buried oxide interface. Most typically, the peak implant concentration is about 20 nm from the top silicon/buried oxide interface.
Typically, the step of externally heating the substrate is carried out at temperatures of 25 degrees Celsius to 300 degrees Celsius.
Typically, the step of implanting is carried out such as to s
Hughes Harold L.
Lawrence Reed K.
McMarr Patrick J.
Dang Trung
Hunnius Stephen T.
Karasek John J.
The United States of America as represented by the Secretary of
LandOfFree
Creation of a polarizable layer in the buried oxide of... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Creation of a polarizable layer in the buried oxide of..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Creation of a polarizable layer in the buried oxide of... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3049712