Adhesive bonding and miscellaneous chemical manufacture – Differential fluid etching apparatus – With microwave gas energizing means
Reexamination Certificate
1999-06-30
2002-09-03
Goudreau, George (Department: 1763)
Adhesive bonding and miscellaneous chemical manufacture
Differential fluid etching apparatus
With microwave gas energizing means
C118S7230AN, C118S715000, C118S720000, C427S446000, C427S453000, C216S075000, C216S095000, C216S096000
Reexamination Certificate
active
06444083
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to semiconductor processing equipment and a method of improving corrosion resistance of such components.
2. Description of the Related Art
In the field of semiconductor processing, vacuum processing chambers are generally used for etching and chemical vapor deposition (CVD) of materials on substrates by supplying an etching or deposition gas to the vacuum chamber and application of an RF field to the gas to energize the gas into a plasma state. Examples of parallel plate, transformer coupled plasma (TCP™) which is also called inductively coupled plasma (ICP), and electron-cyclotron resonance (ECR) reactors and components thereof are disclosed in commonly owned U.S. Pat. Nos. 4,340,462; 4,948,458; 5,200,232 and 5,820,723. Because of the corrosive nature of the plasma environment in such reactors and the requirement for minimizing particle and/or heavy metal contamination, it is highly desirable for the components of such equipment to exhibit high corrosion resistance.
During processing of semiconductor substrates, the substrates are typically held in place within the vacuum chamber by substrate holders such as mechanical clamps and electrostatic clamps (ESC). Examples of such clamping systems and components thereof can be found in commonly owned U.S. Pat. Nos. 5,262,029 and 5,838,529. Process gas can be supplied to the chamber in various ways such as by gas nozzles, gas rings, gas distribution plates, etc. An example of a temperature controlled gas distribution plate for an inductively coupled plasma reactor and components thereof can be found in commonly owned U.S. Pat. No. 5,863,376. In addition to the plasma chamber equipment, other equipment used in processing semiconductor substrates include transport mechanisms, gas supply systems, liners, lift mechanisms, load locks, door mechanisms, robotic arms, fasteners, and the like. The components of such equipment are subject to a variety of corrosive conditions associated with semiconductor processing. Further, in view of the high purity requirements for processing semiconductor substrates such as silicon wafers and dielectric materials such as the glass substrates used for flat panel displays, components having improved corrosion resistance are highly desirable in such environments.
Aluminum and aluminum alloys are commonly used for walls, electrodes, substrate supports, fasteners and other components of plasma reactors. In order to prevent corrosion of the such metal components, various techniques have been proposed for coating the aluminum surface with various coatings. For instance, U.S. Pat. No. 5,641,375 discloses that aluminum chamber walls have been anodized to reduce plasma erosion and wear of the walls. The '375 patent states that eventually the anodized layer is sputtered or etched off and the chamber must be replaced. U.S. Pat. No. 5,895,586 states that a technique for forming a corrosion resistant film of Al
2
O
3
, AlC, TiN, TiC, AlN or the like on aluminum material can be found in Japanese Application Laid-Open No. 62-103379.
U.S. Pat. No. 5,680,013 states that a technique for flame spraying Al
2
O
3
on metal surfaces of an etching chamber is disclosed in U.S. Pat. No. 4,491,496. The '013 patent states that the differences in thermal expansion coefficients between aluminum and ceramic coatings such as aluminum oxide leads to cracking of the coatings due to thermal cycling and eventual failure of the coatings in corrosive environments. In order to protect the chamber walls, U.S. Pat. Nos. 5,366,585; 5,798,016; and 5,885,356 propose liner arrangements. For instance, the '016 patent discloses a liner of ceramics, aluminum, steel and/or quartz with aluminum being preferred for its ease of machinability and having a coating of aluminum oxide, Sc
2
O
3
or Y
2
O
3
, with Al
2
O
3
being preferred for coating aluminum to provide protection of the aluminum from plasma. The '585 patent discloses a free standing ceramic liner having a thickness of at least 0.005 inches and machined from solid alumina. The '585 patent also mentions use of ceramic layers which are deposited without consuming the underlying aluminum can be provided by flame sprayed or plasma sprayed aluminum oxide. The '356 patent discloses a ceramic liner of alumina and a ceramic shield of aluminum nitride for the wafer pedestal. U.S. Pat. No. 5,885,356 discloses ceramic liner materials for use in CVD chambers.
Various coatings have been proposed for metal components of semiconductor processing equipment. For instance, U.S. Pat. No. 5,879,523 discloses a sputtering chamber wherein a thermally sprayed coating of Al
2
O
3
is applied to a metal such as stainless steel or aluminum with an optional NiAl
x
bond coating therebetween. U.S. Pat. Nos. 5,522,932 and 5,891,53 disclose a rhodium coating for metal components of an apparatus used for plasma processing of substrates with an optional nickel coating therebetween. U.S. Pat. No. 5,680,013 discloses non-bonded ceramic protection for metal surfaces in a plasma processing chamber, the preferred ceramic material being sintered AlN with less preferred materials including aluminum oxide, magnesium fluoride, and magnesium oxide. U.S. Pat. No. 5,904,778 discloses a SiC CVD coating on free standing SiC for use as a chamber wall, chamber roof, or collar around the wafer.
With regard to plasma reactor components such as showerhead gas distribution systems, various proposals have been made with respect to the materials of the showerheads. For instance, commonly owned U.S. Pat. No. 5,569,356 discloses a showerhead of silicon, graphite, or silicon carbide. U.S. Pat. No. 5,494,713 discloses forming an alumite film on an aluminum electrode and a silicon coating film such as silicon oxide or silicon nitride over the alumite film. The '713 patent states that the thickness of the silicon coating film should be 10 &mgr;m or less, preferably about 5 &mgr;m, since the aluminum coating film, the alumite coating film and the silicon coating film have different coefficients of linear expansion and cracks are easily generated when the thickness of the silicon coating film is too thick. A thickness below 5 &mgr;m, however, is stated to be unfavorable since the protection of the aluminum substrate is insufficient. U.S. Pat. No. 4,534,516 discloses an upper showerhead electrode of stainless steel, aluminum, copper or the like. U.S. Pat. No. 4,612,077 discloses a showerhead electrode of magnesium. U.S. Pat. No. 5,888,907 discloses a showerhead electrode of amorphous carbon, SiC or Al. U.S. Pat. Nos. 5,006,220 and 5,022,979 disclose a showerhead electrode either made entirely of SiC or a base of carbon coated with SiC deposited by CVD to provide a surface layer of highly pure SiC.
In view of the need for high purity and corrosion resistance for components of semiconductor processing equipment, there is a need in the art for improvements in materials and/or coatings used for such components. Moreover, with regard to the chamber materials, any materials which can increase the service life of a plasma reactor chamber and thus reduce the down time of the apparatus, would be beneficial in reducing the cost of processing the semiconductor wafers.
SUMMARY OF THE INVENTION
According to a first aspect of the invention a process for providing a corrosion resistant coating on a metal surface of a semiconductor processing equipment component is provided. The process includes: (a) depositing a phosphorus nickel plating on a metal surface of the component; and (b) depositing a ceramic coating on the phosphorus nickel plating so as to form an outer corrosion resistant surface. The metal surface can be anodized or unanodized aluminum, stainless steel, a refractory metal such as molybdenum or other metal or alloy used in plasma chambers. The ceramic coating can be alumina, SiC, AlN, Si
3
N
4
, BC or other plasma compatible ceramic material.
According to a second aspect of the invention, a metal component is provided. The component includes
Chang Chris
Steger Robert
Burns Doane , Swecker, Mathis LLP
Goudreau George
Lam Research Corporation
LandOfFree
Corrosion resistant component of semiconductor processing... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Corrosion resistant component of semiconductor processing..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Corrosion resistant component of semiconductor processing... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2886349