ABSTRACT:
TECHNICAL FIELD
The present invention relates generally to solder balls used in microelectronics and, more specifically, to a solder ball having surface properties enhanced by an ion-bombardment-induced sputtering process.
BACKGROUND OF THE INVENTION
In the manufacture of microelectronic devices, various microelectronic components are electrically joined together into circuits using metal alloy solders. Such solders are generally alloys of tin (Sn) and lead (Pb), but can comprise other metal components. The metal alloy solder is generally optimized for bulk properties that control the thermal behavior of the solder. For example, the melting temperature of Pb/Sn solder is controlled by adjusting the relative amounts of tin and lead in the solder. The minimum melting temperature of a Pb/Sn alloy is achieved when the ratio by weight of Pb to Sn in the solder is 37:63. This is called the eutectic composition.
A solder that is homogenous across its mass and optimized for bulk properties does not take into account the desirable surface properties of the solder. Therefore, solder compositions that are optimized for bulk behavior are not necessarily optimized in terms of surface properties. Such surface properties control wetting to metal surfaces, reactivity with organic materials such as fluxes, and the melting point of the surface layer. Such surface properties depend upon both the chemical composition of the solder and the physical characteristics of the surface. For instance, a rough surface may have more surface area for holding flux than a smooth surface.
For some applications, it is desirable to use bulk solder alloys at other than the eutectic composition. For example, Controlled Collapse Chip Connection (C4) solder balls, which are used to join Integrated Circuit (IC) chips to chip carriers, are typically Pb-rich in the range of 90% to 97% Pb. Because Pb-enriched solders have higher melting temperatures than solders closer to the eutectic composition, the solder joint formed by Pb-enriched solders between the chip and the chip carrier maintains its shape throughout subsequent assembly of the chip carrier (with chip attached) to another electrical component such as a printed circuit board. The Pb-enriched solders also require higher temperatures, however, to fuse them to metal surfaces such as copper pads on chip carriers. Thus, organic laminate chip carriers having copper joining pads may be exposed to undesirable high temperatures during joining processes.
A tradeoff results: without further treatment, the benefit of using a Pb-enriched metal alloy solder that maintains its shape at high temperatures is offset by the need for a high fusing temperature. Such high fusing temperatures can be avoided by applying a eutectic solder to the joining pads on the organic laminate chip carrier. To ensure proper fusing at every joint, however, the height of the applied eutectic solder layer must be controlled within very narrow limits, a requirement that is difficult to satisfy.
Another modification that retains high temperature stability while providing low temperature fusing comprises placement of an additional layer or cap of tin or other low melting point metal on the surface of the Pb-enriched solder, as described in U.S. Pat. Nos. 5,634,268 and 5,729,896 and assigned to the common assignee of the present invention. Such a cap enables the bulk solder to retain its desirable high-temperature resistance while providing a surface layer capable of fusing at low temperatures.
The present invention proposes a solder ball having an integral solder surface layer capable of fusing at low temperatures while maintaining the bulk solder properties.
SUMMARY OF THE INVENTION
The present invention provides a metal alloy solder ball comprising a first metal and a second metal, such as lead and tin respectively, and having a bulk ratio of the first metal to the second metal, the solder ball having enhanced surface properties. The process for enhancing the surface properties comprises exposing the solder ball to energized ions of a sputtering gas for an effective amount of time to form a surface gradient having a depth and a gradient ratio of the first metal to the second metal that is less than the bulk ratio. The gradient ratio increases along the surface gradient depth from a minimum at the outer surface.
It is to be understood that both the foregoing general description and the following detailed description are exemplary, but are not restrictive, of the invention.
REFERENCES:
patent: 4064030 (1977-12-01), Nakai et al.
patent: 4921157 (1990-05-01), Dishon et al.
patent: 5000819 (1991-03-01), Pedder et al.
patent: 5054421 (1991-10-01), Ito et al.
patent: 5108950 (1992-04-01), Wakabayashi et al.
patent: 5188280 (1993-02-01), Nakao et al.
patent: 5192582 (1993-03-01), Liedke et al.
patent: 5244144 (1993-09-01), Osame et al.
patent: 5735451 (1994-04-01), Mori et al.
patent: 5340411 (1994-08-01), Mergele et al.
patent: 5345056 (1994-09-01), Frei et al.
patent: 5476726 (1995-12-01), Harada et al.
patent: 5499754 (1996-03-01), Bobbio et al.
patent: 5516031 (1996-05-01), Nishikawa et al.
patent: 5878943 (1996-11-01), Nishikawa et al.
patent: 5609290 (1997-03-01), Bobbio et al.
patent: 5634268 (1997-06-01), Dalal et al.
patent: 5729896 (1998-03-01), Dalal et al.
patent: 6050481 (2000-04-01), Chapman et al.
patent: 6056831 (2000-05-01), Egitto et al.
patent: 6092714 (2000-07-01), Casey
patent: 6344234 (2002-02-01), Dalal et al.
patent: 07226400 (1995-08-01), None
“Ion Beam Joining Technique” by J.M.E. Harper, et al. J. Vac. Sci. Technol., 20(3), Mar. 1982.
“Thin Film Processes” by John L Vossen et al. Academic Press. 1978. pp. 14-19.
“Ion Milling to Remove Halo” by R.J. Herdzik et al. IBM Technical Disclosure Bulletin. vol. 23, No. 11, Apr. 1981. p. 4920.
“Ion Milling Technique to Reflow Solder Pads” by R.J. Herdzik et al. IBM Technical Disclosure Bulletin. Apr., 1981. pp. 4915-4916.
“Lift-Off Process For CrCuAu Metallurgy” by R.J. Herdzik et al. IBM Technical Disclosure Bulletin. vol. No. 1, Jun., 1979. pp. 84-85.
“Influence of Mask Materials on Ion-Etched Structures” by H. Dimigen et al. Journal of Vacuum Science Technology. vol. 13, No. 4, Aug., 1976, pp. 976-980.
Koopman et al., “Fluxless, no clean solder processing of components, printed wiring boards, and packages in air and nitrogen”, Proc. Surface Mount Int'l Conf., pp. 437-446.
Koopman et al., “Fluxless, no clean assembly of solder bumped flip chips,” IEEE, 1996 Elec. Components and Tech. Conf., pp. 552-558.
Coolbaugh et al., “Surface reactions of copper films in O2/CF4/N2 plasmas,” Surface and Interface Analysis, 15(2), pp. 119-124.
Nishikawa et al., “Fluxless Soldering Process Technology,” IEEE, 1994 Elec. Components and Tech. Conf. pp. 286-292.
Egitto Frank D.
Fey Edmond O.
Matienzo Luis J.
Questad David L.
Rai Rajinder S.
International Business Machines - Corporation
Ip Sikyin
Kaschak Ronald
RatnerPrestia
LandOfFree
Solder ball with chemically and mechanically enhanced... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Solder ball with chemically and mechanically enhanced..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Solder ball with chemically and mechanically enhanced... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3105715