Semiconductor device manufacturing: process – Formation of electrically isolated lateral semiconductive... – Total dielectric isolation
Reexamination Certificate
2001-05-21
2003-08-05
Lebentritt, Michael S. (Department: 2824)
Semiconductor device manufacturing: process
Formation of electrically isolated lateral semiconductive...
Total dielectric isolation
C438S404000, C438S408000, C438S423000, C438S459000, C438S517000
Reexamination Certificate
active
06602757
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to silicon-on-insulator (SOI) substrates for use in the semiconductor industry for fabricating integrated circuits (ICs), and more particularly to a method for improving the thickness uniformity of the top superficial Si-containing layer of a SOI substrate. The SOI substrate may be a preformed SOI substrate or a SOI substrate that is prepared in-situ.
BACKGROUND OF THE INVENTION
Silicon-on-insulator (SOI) thickness and thickness uniformity requirements for future generation of complementary metal oxide semiconductor (CMOS) devices and circuits are becoming highly demanding. Typically, SOI thickness targets are from about 100 to about 2500 Å with a thickness uniformity of about ±2% over a 200 mm Si wafer. This is because the threshold voltage, V
t
, of today's generation of CMOS devices can be strongly dependent on the SOI thickness, especially in the low thickness range.
Thickness uniformity of present commercially available SOIs made either by conventional SIMOX or bonding is quite inadequate to meet the required thickness control targets. A typically SOI substrate of the prior art is shown, for example, in FIG.
1
. Specifically, the SOI substrate shown in
FIG. 1
comprises bottom Si-containing substrate
10
, buried oxide (BOX) region
12
formed on the bottom Si-containing substrate, and superficial Si-containing layer
14
having a surface with roughness variation. Note that the area above the dotted line represents the thickness non-uniformity in the superficial Si-containing layer that is formed from conventional SIMOX and bonding processes. Due to this non-uniformity, the thickness in layer
14
may vary randomly across the SOI substrate.
Ideally, it would be beneficial if the superficial Si-containing layer has thickness uniformity across the entire length of the SOI substrate. In the prior art, it is known to control thickness uniformity of a SOI substrate by thinning in hydrogen, chemical mechanical polishing (CMP), or low temperature oxidation (at temperatures below about 1100° C.). The aforementioned prior art approaches to achieve thickness uniformity do not demonstrate sufficient thickness control needed with today's generation of CMOS devices.
Thus, there is a need for developing a method in which thickness uniformity can be readily achieved utilizing processing steps that do not adversely affect the SOI substrate. Moreover, a method is required which demonstrates sufficient thickness control to permit the use of SOI substrates with today's and future generation of CMOS devices.
SUMMARY OF THE INVENTION
One object of the present invention is to provide a method of improving the thickness uniformity of a SOI (preformed or in-situ) substrate.
Another object of the present invention is to provide a method of forming a SOI substrate having a SOI thickness of less than about 1000 Å.
Another object of the present invention is to provide a method of improving the thickness uniformity of SIMOX or bonded SOI substrates.
A yet further object of the present invention is to provide a method of improving the thickness uniformity of a SOI substrate that employs processing steps that do not adversely affect the SOI substrate.
A still further object of the present invention is to provide a method for achieving thickness uniformity of a SOI substrate which demonstrates sufficient thickness control to permit the SOI substrates to be used in fabricating high-performance semiconductor devices and circuits.
An even further object of the present invention is to provide a method of improving the thickness uniformity in a self-adjusting manner by using an internal thermal oxidation (ITOX) mechanism.
These and other objects and advantages are achieved in the present invention by subjecting a SOI substrate having thickness non-uniformity to high-temperature oxidation step. During the high-temperature oxidation the following two phenomena are believed to be taking place which aid in improving the thickness uniformity of the SOI substrate: (i) surface oxidation of the superficial Si-containing layer (i.e., the Si-containing layer present atop the buried oxide (BOX) region); and (ii) internal thermal oxidation (ITOX), i.e., diffusion of oxygen via the superficial Si-containing layer into the interface that exists between the BOX and the superficial Si-containing layer.
Regions of the SOI substrate which have thicker Si get less ITOX, but more surface oxidation creating a thicker surface oxide (and hence thinner superficial Si-containing layer). However, regions of the SOI substrate which are thinner get more ITOX and have thinner surface oxide (and hence a thicker superficial Si-containing layer). This mechanism continues to self-adjust the SOI substrate thickness with oxidation time to improve the SOI thickness uniformity. The same mechanism improves the surface roughness. It has been observed that the closer the oxidizing surface is to the BOX, the more uniform the superficial Si-containing layer
14
becomes.
A first method of the invention which is employed with a preformed SOI substrate (SIMOX or bonded) comprises the steps of: subjecting a preformed SOI substrate having thickness non-uniformity to a high-temperature oxidation process that is capable of improving the thickness uniformity of said SOI substrate, wherein said high-temperature oxidation is carried out at a temperature of about 1000° C. or above, preferably 1250° C. or above and in an oxygen-containing ambient that promotes surface oxide growth and internal thermal oxidation.
In accordance with the present invention, the preformed SOI substrates employed in the present invention include SOI substrates that are formed by conventional SIMOX or bonding techniques. Included within this definition are unpatterned or patterned SOI substrates that have a single or multiple buried oxide regions formed therein.
A second method of the present invention is directed to an in-situ process of preparing a SOI substrate wherein the inventive high-temperature oxidation step is used as a soak cycle prior to annealing. Specifically, the second method of the present invention comprises the steps of:
(a) implanting oxygen ions into a surface of a Si-containing substrate, said implanted oxygen ions having a sufficient concentration to form a buried oxide region in said Si-containing substrate;
(b) soaking said Si-containing substrate containing implanted oxygen ions in an oxygen-containing ambient at a temperature of about 1000° C. or above, preferably 1100° C. or greater for a time period of about 0.5 hours or greater; and
(c) annealing said soaked Si-containing substrate containing said implanted oxygen ions under conditions that are capable of forming a SOI substrate having said buried oxide region which electrically isolates a superficial Si-containing layer from a bottom Si-containing layer, said SOI substrate having thickness uniformity.
In a third method of the present invention, the high-temperature oxidation step is used in a conventional SIMOX process following the annealing step. When this aspect is employed, a SIMOX process is provided that comprises the steps of:
(a) implanting oxygen ions into a surface of a Si-containing substrate, said implanted oxygen ions having a sufficient concentration to form a buried oxide region in said Si-containing substrate;
(b) annealing said Si-containing substrate containing said implanted oxygen ions under conditions that are capable of forming a SOI substrate having said buried oxide region which electrically isolates a superficial Si-containing layer from a bottom Si-containing layer, said SOI substrate having thickness non-uniformity; and
(c) subjecting said SOI substrate having thickness non-uniformity to a high-temperature oxidation process that is capable of improving the thickness uniformity of said SOI substrate, wherein said high-temperature oxidation is carried out at a temperature of about 1000° C. or above, preferably 1250° C. or above, and in an oxygen-containing ambient that promotes surface oxid
Hovel Harold J.
Sadana Devendra K.
Lebentritt Michael S.
Scully Scott Murphy & Presser
Trepp Robert M.
LandOfFree
Self-adjusting thickness uniformity in SOI by... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Self-adjusting thickness uniformity in SOI by..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Self-adjusting thickness uniformity in SOI by... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3090874