Semiconductor device manufacturing: process – Making device or circuit emissive of nonelectrical signal – Including integrally formed optical element
Reexamination Certificate
2002-05-20
2003-04-01
Whitehead, Jr., Carl (Department: 2813)
Semiconductor device manufacturing: process
Making device or circuit emissive of nonelectrical signal
Including integrally formed optical element
Reexamination Certificate
active
06541295
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to whispering gallery mode resonators. More specifically, the present invention is a method of fabricating a whispering gallery mode resonator. CVD wafer fabrication is described in such patents as U.S. Pat. No. 4,661,199 Apr. 28, 1987, entitled: “METHOD TO INHIBIT AUOTDOPING IN EPITAXIAL LAYERS FROM HEAVILY DOPED SUBSTRATES IN CVD PROCESSING”
Method to inhibit audodoping in epitaxial layers from heavily doped substrates in chemical vapor deposition (CVD) processing, Looney, Gary W, which is disclosed herein by reference.
Silicon-based THz sources are based on intersub-banded transitions in SiGe alloy quantum wells on silicon substrates. The Whispering Gallery Mode Resonator structure for a unipolar quantum cascade THz laser is processed in SiGe alloys. The layer thickness is 3 micrometers for the active resonator disk, and 3-7 micrometers for the pedestal height and the disk diameter can range from 50 to 200 micrometers. Heavily doped Silicon layers and selective etching are now used to define the features of this device. This approach can be quite challenging because of the requirement of an extremely heavy doped layer to enhance the etch selectivity.
The above identified Looney patent shows that heavily doped substrates of silicon wafers are inhibited form contaminating by autodoping phenomenon lightly doped epitaxial growing films by providing a thick film of silicon on the susceptor for CVE processing in a radio frequency (RF) powered reactor. The susceptor film of silicon serves to provide a silicon seal to the rear surface of the substrate to prevent or at least inhibit outdiffusion of dopants that that can contaminate the epitaxial film. For example, substrates heavily doped with arsenic, phosphorus or boron at concentrations of 10
19
atoms/cc are inhibited from autodoping contaminating epitaxial films of silicon lightly doped with the same dopant at 10
14
atoms/cc.
In the production of certain semiconductor devices, an epitaxial layer of silicon on a substrate, such as a silicon wafer, is used as the starting material for the devices. The epitaxial layer of silicon is deposited upon the silicon wafer in a chemical vapor deposition (CVD) process wherein the wafer is supported on a silicon carbide-coated graphite susceptor and heated to a high temperature by energy derived from a radio frequency (RF) source. A volatile mixture of silicon is introduced and thermally decomposed or reacted with other gases or vapors at the surface of the wafer to yield silicon which deposits on the wafer surface. Various types of reactors utilizing such RF heated susceptors are well known in the art. One such susceptor utilized in a barrel reactor is described in U.S. Pat. No. 4,099,041, issued to S. Berkman et al on Jul. 4, 1978, entitled “Susceptor Structure for Heating Semiconductor Substrates”.
In recent applications of semiconductor devices, particularly those used for high power circuits, there has been a need to provide a precise and restricted range of resistivity values of the epitaxial layers grown on heavily doped substrates.
As mentioned above, silicon-based THz sources are based on intersub-banded transitions in SiGe alloy quantum wells on silicon substrates. The Whispering Gallery Mode Resonator structure for unipolar quantum cascade THz lasers in processed in SiGe alloys. The layer thickness is 3 micrometers for the active resonator disk, and 3-7 micrometers for the pedestal height and the disk diameter can range from 50 to 200 micrometers. Heavily doped silicon layers and selective etching are now used to define the features of this device. This approach can be quite challenging because of the requirement of an extremely heavy doped layer to enhance the etch selectivity.
Samples of current whispering gallery mode resonator technology are described in the following U.S. Patents which are incorporated herein by reference:
U.S. Pat. No. 5,834,981, Nov. 10, 1998, entitled “Whispering gallery mode dielectric resonator oscillator circuit,” Trier, Marc,
U.S. Pat. No. 5,652,556, Jul. 29, 1997, entitled “Whispering gallery-type dielectric resonator with increased resonant frequency spacing, improved temperature stability, and reduce microphny,” Flory, Curt Alan.
The present invention describes a novel process using the silicon oxide of a semiconductor on insulator (SOI) bonded silicon wafer as the etch medium which will be selectively removed to form the microdisk. SOI bonded silicon wafers are now being used in CMOS fabrication and have very low defect densities. When using KOH based etches, the oxide has essentially 100% selectivity with silicon, and normal silicon semiconductor fabrication procedures can be used to define the device, with precise control over all dimensions.
SUMMARY OF THE INVENTION
This disclosure describes a novel approach using the silicon oxide of an SOI bonded silicon wafer as the etch medium which will be selectively removed to form a microdisk for whispering gallery mode resonator. SOI bonded silicon wafers are now being used in CMOS fabrication and have very low defect densities. When using KOH based etches, the oxide has essentially 100% selectivity with silicon, and normal silicon semiconductor fabrication procedures can be used to define the device, with precise control over all dimensions.
The starting material for this process is a bonded silicon wafer with the appropriate thickness of separating silicon oxide and the appropriate thickness of superficial silicon. The thicknesses are chosen to give the desired operating characteristics of the device. First a masking oxide is formed and holes are opened in the masking oxide having the diameter needed for the pedestal. The holes are then opened down to the separating silicon oxide. If KOH is used then the etch will stop at the oxide automatically. After the silicon etch the oxide is opened to the silicon substrate.
Using CVD selective epitaxial (EPI) holes are then filled to the original surface of the superficial silicon, essentially forming the pedestal of the microdisk.
After stripping the masking oxide active regions of silicon and/or SiGe are formed at the appropriate thickness for the device, via CVD and/or molecular beam epitaxy (MBE). A new masking oxide is then deposited and a new mask level is aligned to the pedestals and defines the microdisk, moats are etched around the pedestal area having the diameter of the microdisc. These moats are etched down to the separating oxide. The oxide is then removed with an oxide etch which under cuts the microdisk and creates a cavity back to the pedestal.
REFERENCES:
patent: 4099041 (1978-07-01), Berkman et al.
patent: 4661199 (1987-04-01), Looney et al.
patent: 5343490 (1994-08-01), McCall
patent: 5561314 (1996-10-01), Ema et al.
patent: 5652556 (1997-07-01), Flory et al.
patent: 5834981 (1998-11-01), Trier et al.
Auton William G.
Jr. Carl Whitehead
The United States as represented by the Secretary of the Air For
Thompson Craig
LandOfFree
Method of fabricating a whispering gallery mode resonator... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of fabricating a whispering gallery mode resonator..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of fabricating a whispering gallery mode resonator... will most certainly appreciate the feedback.