Semiconductor device manufacturing: process – Making field effect device having pair of active regions... – On insulating substrate or layer
Reexamination Certificate
1998-10-02
2002-01-01
Zarabian, Amir (Department: 2824)
Semiconductor device manufacturing: process
Making field effect device having pair of active regions...
On insulating substrate or layer
C438S159000, C438S486000, C438S487000
Reexamination Certificate
active
06335232
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method of manufacturing a thin film transistor suitable for applications such as a switching device for displaying a pixel in a display panel of an active matrix type.
2. Description of the Related Art
FIG. 1
is a cross sectional view showing a structure of a thin film transistor of a bottom gate type.
This thin film transistor is formed as follows.
On a surface of an insulating transparent substrate
1
, a gate electrode
2
of high melting point metal (refractory metal) such as tungsten or chromium is provided. The gate electrode
2
has a tapered shape with its width gradually increasing toward the transparent substrate
1
. On the transparent substrate
1
on which the gate electrode
2
is located, a silicon oxide film
4
is deposited, with a silicon nitride film
3
interposed therebetween. The silicon nitride film
3
prevents penetration of impurities contained in the substrate
1
into an active region which will be described below, and the silicon oxide film
4
acts as a gate insulating film. A polycrystalline silicon film
5
is deposited on the silicon oxide film
4
crossing over the gate electrode
2
. The polycrystalline silicon film
5
functions as an active region of the thin film transistor.
A stopper
6
of insulating material such as silicon oxide is disposed on the polycrystalline silicon film
5
. The region of the film
5
covered with the stopper acts as a channel region
5
c
, while the remaining regions of the polycrystalline silicon film
5
act as a source region
5
s
and a drain region
5
d
. A silicon oxide film
7
and a silicon nitride film
8
are deposited on the polycrystalline silicon film
5
including the stopper
6
formed thereon. These silicon oxide and nitride films
7
and
8
, respectively, are interlayer insulating films protecting the polycrystalline silicon film
5
including the source and drain regions
5
s
and
5
d.
Contact holes
9
are formed at prescribed positions of the silicon oxide and nitride films
7
and
8
located on the source and drain regions
5
s
and
5
d
. At the contact hole
9
portions, a source electrode
10
s
and a drain electrode
10
d
are disposed connected to the source and drain regions
5
s
and
5
d
, respectively. An acrylic resin layer
11
transparent to visible light is deposited on the silicon nitride film
8
where source and drain electrodes
10
s
and
10
d
are formed. The acrylic resin layer
11
fills in the recesses created by the gate electrode
2
and the stopper
6
, to thereby planarize the surface.
A contact hole
12
is formed in the portion of the acrylic resin layer
11
located on the source electrode
10
s
. A transparent electrode
13
of indium tin oxide (ITO) or the like connected to the source electrode
10
s
through the contact hole
12
is formed spreading over the acrylic resin layer
11
. This transparent electrode
13
forms a pixel electrode in the application of a liquid crystal display panel.
A plurality of the above-described thin film transistors and pixel electrodes are arranged in a matrix on the transparent substrate
1
. These transistors respond to a scan control signal applied to the gate electrode
2
to provide image data received at the drain electrode
10
d
to the pixel electrodes.
The polycrystalline silicon film
5
is preferably formed to have a grain size large enough to function as an active region of the thin film transistor. One of the commonly-known methods for forming the polycrystalline silicon film with a large grain is a laser annealing method utilizing an excimer laser. According to this laser annealing method, amorphous silicon is deposited on the silicon oxide film
4
serving as a gate insulating film, and is irradiated by an excimer laser, so that silicon is melted and then crystallized. Since a use of the laser annealing method can eliminate the need for processing the transparent substrate
1
at a high temperature, a low-melting point glass substrate can be employed as the transparent substrate
1
.
The amorphous silicon film, which will be turned into the polycrystalline silicon film
5
, is formed by plasma CVD performed at a low temperature. As a result, hydrogen contained in silane which is used as reaction gas remains in the film. If the amorphous silicon film is melted by laser irradiation with a large amount of hydrogen remaining in the film, hydrogen is suddenly expelled from the film, resulting in a rough film surface. Consequently, operation characteristics of a transistor having such a polycrystalline silicon film as an active region will be deteriorated.
SUMMARY OF THE INVENTION
Therefore, an object of the present invention is to avoid creation of a rough film surface during crystallization of an amorphous silicon film.
A method of manufacturing a thin film transistor according to the present invention includes a first step of depositing a refractory metal film on a main surface of a substrate and etching the film to a prescribed pattern to form a gate electrode, a second step of depositing a gate insulating film on the substrate to cover the gate electrode, a third step of depositing a semiconductor film on the gate insulating film, and a fourth step of depositing an interlayer insulating film on the semiconductor film. The above third step includes a step of depositing an amorphous silicon film on the gate insulating film, heating the amorphous silicon film at 430±20° C. to expel hydrogen contained therein, and melting the amorphous silicon film to crystallize.
Another method of manufacturing a thin film transistor according to the present invention includes a first step of depositing a semiconductor film on a main surface of a substrate, a second step of depositing a gate insulating film on the semiconductor film, a third step of depositing an electrically conductive film on the gate insulating film and etching the electrically conductive film to a prescribed pattern crossing over the semiconductor film to form a gate electrode, and a fourth step of depositing an interlayer insulating film on the semiconductor film to cover the gate electrode. The first step includes a step of depositing an amorphous silicon film on the main surface of said substrate, heating the silicon film at 430±20° C. to expel hydrogen contained therein, and melting the amorphous silicon film to crystallize it.
In the above method of manufacturing a thin film transistor according to the present invention, the above third or first step of heating the amorphous silicon film is carried out in an inert gas atmosphere. Gas such as nitrogen gas can be used as the inert gas.
In the above heating step of the present invention, for example, prior to heating, the substrate is placed in a preparation chamber disposed adjacent to a heat treatment chamber, gas in the heat treatment and preparation chambers are replaced by the inert gas, and the substrate is relocated from the preparation chamber to the heat treatment chamber.
Further, according to the present invention, the step of heating the amorphous silicon layer is carried out for one hour or longer.
The step of heating the amorphous silicon film according to the present invention allows reduction in hydrogen concentration of the amorphous silicon film formed on the gate insulating film to 1 atomic % or lower.
By thus performing heat treatment of the amorphous silicon film, hydrogen remaining in the film when it is formed can be gradually expelled out of the film. Performing heat treatment for a given period of time allows reduction in hydrogen in the amorphous silicon film to a prescribed value or lower, preventing a large amount of hydrogen from being suddenly emitted from the film when the amorphous silicon film is melted.
Therefore, the present invention can avoid roughness at the surface of the film which otherwise results from sudden generation of hydrogen when the amorphous silicon film is melted.
Since heat treatment for eliminating hydrogen is carried out in an nitrogen atmosphere, it
Nakanishi Shiro
Ohori Mitsutaka
Cantor & Colburn LLP
Lebentritt Michael S.
Sanyo Electric Co,. Ltd.
Zarabian Amir
LandOfFree
Method of manufacturing a thin film transistor does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of manufacturing a thin film transistor, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of manufacturing a thin film transistor will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2869379