Active solid-state devices (e.g. – transistors – solid-state diode – Field effect device – Having insulated electrode
Reexamination Certificate
2000-12-21
2002-01-01
Lee, Eddie (Department: 2815)
Active solid-state devices (e.g., transistors, solid-state diode
Field effect device
Having insulated electrode
C257S298000, C257S052000, C257S295000, C257S532000, C257S300000, C438S396000
Reexamination Certificate
active
06335551
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to a thin film capacitor and a method of forming the same, and more particularly to a thin film capacitor having an improved bottom electrode to be used in a semiconductor integrated circuit.
A high temperature oxygen atmosphere is necessary to form a high dielectric constant thin film such as SrTiO
3
or (Ba, Sr)TiO
3
which shows several hundreds dielectric constant at room temperature. Such the high dielectric constant thin film is deposited on a bottom electrode of a stable electrically conductive oxide such as RuO
2.
In 1994, International Electron Devices Meeting Technical Digest, pp. 831-834, it is disclosed that a polycrystalline RuO
2
thin film is deposited by a reactive sputtering method on a TiN thin film serving as a diffusion barrier layer for subsequent patterning the laminations of the TiN thin film and the polycrystalline RuO
2
thin film to define an RuO
2
/TiN storage electrode before an SrTiO
3
thin dielectric thin film is deposited on the RuO
2
/TiN storage electrode by a chemical vapor deposition method.
In 1995, International Electron devices Meeting Technical Digest pp. 119-122, it is disclosed that an Ru thin film is deposited on a TiN diffusion barrier layer before a polycrystalline RuO
2
thin film is deposited by a reactive sputtering method on the Ru thin film to form a RuO
2
/Ru/TiN storage electrode.
FIG. 1
is a fragmentary cross sectional elevation view illustrative of a conventional thin film capacitor having a bottom electrode of an electrically conductive oxide. A TiN diffusion barrier layer
11
is provided on a substrate
9
. A polycrystalline conductive oxide bottom electrode
24
is provided on the TiN diffusion barrier layer
11
. A dielectric film
25
is provided on the polycrystalline conductive oxide bottom electrode
24
. A top electrode
26
is provided on the dielectric film
25
.
The polycrystalline conductive oxide bottom electrode
24
has a pillar-shaped or particle-shaped crystal structure with a size of several tens nanometers, for which reason a surface of the polycrystalline conductive oxide bottom electrode
24
also has an roughness of the same size as the crystal structure. Particularly, this problem with the surface roughness of the bottom electrode is significant when the polycrystalline conductive layer serving as the diffusion barrier layer is provided on the substrate and the polycrystalline conductive oxide layer serving as the bottom electrode is provided on the diffusion barrier layer. A field concentration may appear at convex portions of the surface of the bottom electrode. The dielectric film is unlikely to be deposited within concave portions of the surface of the bottom electrode, whereby voids are likely to be formed at the concave portions of the surface of the bottom electrode. For those reasons, a leakage of current may be caused and a breakdown voltage may be reduced.
In Japanese laid-open patent publication No. 2-46756, it is disclosed that a polycrystalline silicon film is subjected to an ion-implantation of As in order to amorphize a surface region of the polycrystalline silicon film before a dielectric film is formed on the amorphized surface region of the polycrystalline silicon film.
FIG. 2
is a fragmentary cross sectional elevation view illustrative of a conventional thin film capacitor having a bottom electrode having an amorphized surface region. A silicon oxide film
102
is provided on a silicon substrate
101
. A bottom electrode
103
is formed on a selected region of the silicon oxide film
102
, wherein the bottom electrode
103
comprises an undoped polycrystalline silicon film and a surface region which comprises an amorphous layer
08
. silicon nitride film
104
is provided which extends on the amorphous layer
108
and unselected regions of the silicon oxide film
102
. A silicon oxide film
105
is provided on the silicon nitride film
104
. A polycrystalline silicon top electrode
106
is provided on the silicon oxide film
105
.
FIGS. 3A through 3E
are fragmentary cross sectional elevation views illustrative of a conventional method of forming the above conventional thin film capacitor having the bottom electrode having the amorphized surface region.
With reference to
FIG. 3A
, a silicon oxide film
102
is formed on a silicon substrate
101
. An undoped polycrystalline silicon film is deposited by a chemical vapor deposition method on the silicon oxide film
102
for subsequent patterning the undoped polycrystalline silicon film.
With reference to
FIG. 3B
, the patterned undoped polycrystalline silicon film is then subjected to an ion-implantation of an impurity such as As to amorphize a surface region of the patterned undoped polycrystalline silicon film, thereby forming an amorphous silicon layer
108
. As a result, a bottom electrode
103
comprising the undoped polycrystalline silicon film and the amorphous silicon layer
108
is formed on a selected region of the silicon oxide film
102
.
With reference to
FIG. 3C
, a silicon nitride film
104
is formed which extends on the amorphous layer
108
and unselected regions of the silicon oxide film
102
.
With reference to
FIG. 3D
, a silicon oxide film
105
is formed on the silicon nitride film
104
.
With reference to
FIG. 3E
, a polycrystalline silicon top electrode
106
is formed on the silicon oxide film
105
.
The dielectric of the capacitor includes the silicon oxide film which has a small dielectric constant. This silicon oxide film reduces an effective capacitance, whereby it is difficult to obtain desired characteristics of the thin film capacitor. Further, the ion-implantation of As for forming the amorphous layer
108
is labored and time-consuming process.
In the above circumstances, it had been required to develop a novel thin film capacitor free from the above problems and a novel method of forming the same.
SUMMARY OF THE INVENTION
Accordingly, it is an object of the present invention to provide a novel thin film capacitor having an improved bottom electrode free from the above problems.
It is a further object of the present invention to provide a novel thin film capacitor having an improved bottom electrode capable of suppressing a leakage of current.
It is a still further object of the present invention to provide a novel thin film capacitor having an improved bottom electrode capable of preventing a drop of the breakdown voltage.
It is yet a further object of the present invention to provide a novel thin film capacitor having an improved bottom electrode having a smooth surface free of a remarkable roughness.
It is a further more object of the present invention to provide an improved bottom electrode for a thin film capacitor, wherein the improved bottom electrode has a smooth surface free of a remarkable roughness for suppressing a leakage of current and preventing a drop of the breakdown voltage.
It is still more object of the present invention to provide a method of forming a novel thin film capacitor having an improved bottom electrode free from the above problems.
It is moreover object of the present invention to provide a method of forming a novel thin film capacitor having an improved bottom electrode capable of suppressing a leakage of current.
It is another object of the present invention to provide a method of forming a novel thin film capacitor having an improved bottom electrode capable of preventing a drop of the breakdown voltage.
It is still another object of the present invention to provide a method of forming a novel thin film capacitor having an improved bottom electrode having a smooth surface free of a remarkable roughness.
It is yet another object of the present invention to provide a method of forming an improved bottom electrode for a thin film capacitor, wherein the improved bottom electrode has a smooth surface free of a remarkable roughness for suppressing a leakage of current and preventing a drop of the breakdown voltage.
The present invention provides a storage electrode of a capacitor. The storage electrode i
Lee Eddie
Lee Eugene
NEC Corporation
Young & Thompson
LandOfFree
Thin film capacitor having an improved bottom electrode and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Thin film capacitor having an improved bottom electrode and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thin film capacitor having an improved bottom electrode and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2835610