Semiconductor device manufacturing: process – Coating with electrically or thermally conductive material – To form ohmic contact to semiconductive material
Reexamination Certificate
1999-09-07
2001-02-06
Booth, Richard (Department: 2812)
Semiconductor device manufacturing: process
Coating with electrically or thermally conductive material
To form ohmic contact to semiconductive material
C438S631000, C438S633000, C438S638000, C438S643000
Reexamination Certificate
active
06184138
ABSTRACT:
BACKGROUND OF THE INVENTION
(1) Field of the Invention
The invention relates to the fabrication of integrated circuit devices, and more particularly, to a method for reducing dishing and erosion effects in the copper surface of copper dual damascene structures.
(2) Description of the Prior Art
In the formation of semiconductor integrated circuits, it is common practice to form interconnect metal line structures on a number of different levels within the structure and interconnecting the various levels of wiring with contact or via openings. The first or lowest level of interconnect wires is typically formed as a first step in the process after which a second or overlying level of interconnect wires is deposited over the first level. The first level of interconnect wires is typically in contact with active regions in a semiconductor substrate but is not limited to such contact. The first level of interconnect can for instance also be in contact with a conductor that leads to other devices that form part of a larger, multi-chip structure. The two levels of metal wires are connected by openings between the two layers that are filled with metal where the openings between the two layers are lines up with and match contact points in one or both of the levels of metal lines.
Previously used techniques to form multi-levels of wiring apply the technique of first forming the interconnect level metal in a first plane followed by forming the overlying level of interconnect wire in a second plane. This structure typically starts with the surface of a semiconductor substrate into which active devices have been created. These active devices can include bipolar transistors, MOSFET devices, doped regions that interconnect with other regions of the device while provisions may also have been provided to make interconnects with I/O terminals in the periphery of the device. The surface into which the pattern of interconnect lines of the first plane is formed may also be an insulation layer deposited over the surface of the substrate or a layer of oxide may first have been formed on the surface of the substrate. After the layer, into which the pattern of interconnecting wires has to be created, has been defined, the interconnecting pattern itself needs to be defined. This is done using conventional photolithographic techniques whereby the openings are made (in the layer) above the points that need to be contacted in the substrate. The openings, once created, may by lined with layers of material to enhance metal adhesion (to the sidewalls of the opening), the glue layer, or to prevent diffusion of materials into and from the substrate in subsequent processing steps, the barrier layer. For the barrier layer, a variety of materials can be used such as Ti/Tin:W (titanium/titanium nitride:tungsten), titanium-tungsten/titanium or titanium-tungsten nitride/titanium or titanium nitride or titanium nitride/titanium, silicon nitride (Si
3
N
4
), tungsten, tantalum, niobium, molybdenum. The final phase in creating the first level of interconnect lines is to fill the created openings with metal, typically aluminum, tungsten or copper, dependent on the particular application and requirements and restrictions imposed by such parameters as line width, aspect ratio of the opening, required planarity of the surface of the deposited metal and others.
This process of line formation in overlying layers on metal can be repeated in essentially the same manner as just highlighted for the first layer of interconnecting wires. This process of forming sequential layers of interconnecting levels of wire is in many instances prone to problems and limitations. Copper has in recent times found more application in the use of metal wires due to its low resistivity, high electromigration resistance and stress voiding resistance. Copper however exhibits the disadvantage of high diffusivity in common insulating materials such as silicon dioxide and oxygen-containing polymers. This leads to, for instance, the diffusion of copper into polyimide during high temperature processing of the polyimide resulting in severe erosion of the copper and the polyimide due to the copper combining with oxygen in the polyimide. The erosion may result in loss of adhesion, delamination, voids, and ultimately a catastrophic failure of the component. The copper that is used in an interconnect may diffuse into the silicon dioxide layer causing the dielectric strength to become conductive and also decreasing the dielectric strength of the silicon dioxide layer. A copper diffusion barrier is therefore often required; silicon nitride is often applied as a diffusion barrier to copper. Silicon nitride however has a dielectric constant that is high compared to silicon dioxide thereby limiting the use of silicon nitride in encapsulating copper interconnect lines.
In addition, due to the fact that copper is very difficult to process by RIE, the CMP method may need to be used where copper is used as a wiring material. To polish copper at a high rate without scratching in accordance with the buried wiring formation, the copper etch rate must be raised by increasing the amount of the component responsible for copper etching contained in the polishing slurry. If the component is used in an increased amount, the etching will occur isotropically. Consequently, buried copper is etched away, causing dishing in the wiring. It is, when forming interconnect lines using copper, desirable to use methods that do not depend on patterning the copper lines using a chemical etching process since etching of copper is very difficult and is a process that is only recently being further investigated. The use of copper as a metal for interconnect wiring is further hindered by copper's susceptibility to oxidation. Conventional photoresist processing cannot be used when the copper is to be patterned into various wire shapes because the photoresist needs to be removed at the end of the process by heating it in a highly oxidized environment, such as an oxygen plasma, thereby converting it to an easily removed ash.
Two widely used approaches in creating metal interconnects is the use of the damascene and the dual damascene structures. The application of the Damascene process continues to gain wider acceptance, most notably in the process of copper metalization due to the difficulty of copper dry etch where the Damascene plug penetrates deep in very small, sub-half micron, Ultra Large Scale integrated devices. Recent applications have successfully used copper as a conducting metal line, most notably in the construct of CMOS 6-layer copper metal devices.
In the formation of a damascene structure, a metal plug is first formed in a surface; this surface in most instances is the surface of a semiconductor substrate. A layer of Intra Level Dielectric (ILD) is deposited (using for instance Plasma Enhanced CVD technology with SiO
2
as a dielectric) over the surface into which trenches for metal lines are formed (using for instance Reactive Ion Etching technology).
The trenches overlay the metal plug and are filled with metal (using for instance either the CVD or a metal flow process). Planarization of this metal to the top surface of the layer of ILD completes the damascene structure. Some early damascene structures have been achieved using Reactive Ion Etching (RIE) for the process of planarization but Chemical Mechanical Planarization (CMP) is used exclusively today.
An extension of the damascene process is the dual damascene process whereby an insulating or dielectric material, such as silicon oxide, is patterned with several thousand openings for the conductive lines and vias, which are filled at the same time with metal. Damascene is an interconnection fabrication process in which grooves are formed in an insulating layer and filled with metal to form the conductive lines. Dual damascene is a multi-level interconnection process in which, in-addition to forming the grooves of single damascene, conductive via openings also are formed. One of the dual damascene approaches uses a dielectric
Gupta Subhash
Ho Paul Kwok Keung
Zhou Mei Sheng
Booth Richard
Chartered Semiconductor Manufacturing Ltd.
Nguyen Ha Tran
Pike Rosemary L. S.
Saile George O.
LandOfFree
Method to create a controllable and reproducible dual copper... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method to create a controllable and reproducible dual copper..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method to create a controllable and reproducible dual copper... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2562212