Radiation imagery chemistry: process – composition – or product th – Imaging affecting physical property of radiation sensitive... – Radiation sensitive composition or product or process of making
Reexamination Certificate
2000-04-18
2001-09-25
Angebranndt, Martin (Department: 1756)
Radiation imagery chemistry: process, composition, or product th
Imaging affecting physical property of radiation sensitive...
Radiation sensitive composition or product or process of making
C369S288000, C369S275500, C369S275200, C428S064100
Reexamination Certificate
active
06294310
ABSTRACT:
The present invention relates to an optical information recording medium of recordable/erasable type utilizing a difference in reflectivity or a phase difference of reflected light resulting from a phase-change of the recording layer by irradiation of a laser beam.
Optical disks are classified into a read only memory (ROM) type and a recordable type (including a rewritable type). The read only memory type has already practically been used as a video disk, an audio disk or a disk memory for a large capacity computer.
Typical recordable type disks include disks of pit-forming/deformation type, organic dye type, magneto-optical type and phase-change type. For the pit-forming/deformation type, a recording layer made of e.g. a dye or a low melting point metal such as Te, is employed, and the recording layer is locally heated by irradiation with a laser beam to form pits or irregularities.
For the organic dye type, a recording layer made of a dye or a polymer containing a dye, is employed, so that the reflectivity (or the refractive index) changes between before and after the recording. This type is practically employed as an optical recording medium for recording CD format signals.
The magneto-optical type is designed to carry out recording or erasing by the direction of magnetization of the recording layer and to carry out retrieving by an magneto-optical effect.
On the other hand, the phase-change type is the one which utilizes a phenomenon that the reflectivity or the phase of reflected light changes between before and after the phase change, whereby retrieving is carried out by detecting the difference in the quantity of reflected light without requiring an external magnetic field. As compared with the magneto-optical type, the phase-change type requires no magnet, and the optical system is simple, whereby preparation of a driving system is easy, and such a phase-change type is advantageous also for downsizing and reduction of costs. Further, it has advantages such that recording and erasing can be carried out simply by modulating the power of a laser beam, and a one-beam overwriting operation is thereby possible wherein erasing and re-recording are carried out simultaneously by a single beam.
It is common to employ a thin film of a chalcogen type alloy as the material for the recording layer for such a phase-change recording system. For example, it has been attempted to use a thin film of an alloy of Ge—Te type, Ge—Sb—Te type, In—Sb—Te type, Ge—Sn—Te type or Ag—In—Sb—Te type.
In the one-beam overwriting phase-change recording, it is common to form recording bits by changing a recording layer in a crystalline state to an amorphous state and to carry out erasing by crystallizing the amorphous phase.
However, the recording layer is usually amorphous immediately after its formation. Accordingly, the entire recording layer is crystallized in a short period of time. This step is called initial crystallization or initialization. It is common to carry out the initialization by irradiating a rotating medium with a laser beam focused to have a diameter of from a few tens to a few hundreds &mgr;m.
With respect to the above-mentioned Ge—Sb—Te type ternary alloy, only a composition close to a GeTe—Sb
2
Te
3
pseudo-binary alloy has heretofore attracted an attention and has been practically developed, and a composition close to a Te
85
Ge
15
eutectic composition or a Sb
70
Te
30
eutectic composition has not been practically employed.
Namely, an alloy material close to the eutectic composition has been considered to be unsuitable as a recording layer for an overwritable optical recording medium, since it undergoes phase separation at the time of crystallization, and it has been impossible to crystallize it by heating for a short period of time of less than 100 nsec, although its amorphous-forming ability is high.
For example, even with a Ge—Sb—Te type ternary alloy, no practically crystallization speed has been obtained with a composition close to the Te
85
Ge
15
eutectic composition.
On the other hand, in the vicinity of the Sb
70
Te
30
eutectic composition, a binary alloy of Sb
u
Te
1−u
(0.58<u<075) is known to be useful for repeated recording and erasing as between the crystalline and amorphous states, although this is an extremely primitive method wherein only a change in reflectance was monitored (U.S. Pat. No. 5,015,548). Further, a study has been made on a compositional range having a third element, particularly Ge, added to Sb
70
Te
30
.
However, these methods have a problem that the productivity is low, since the initialization operation is difficult. Accordingly, there has been no practical progress since then with respect to a composition close to the Sb
70
Te
30
eutectic composition.
Accordingly, it has been considered that only a material in the vicinity of a readily initializable intermetallic composition or its pseudo binary alloy exhibits practical properties.
Irrespective of such a conventional belief, the present inventors have re-examined the crystallization/amorphous conversion properties of the medium having a composition in the vicinity of the eutectic composition, and as a result, have found that such a medium exhibits characteristics superior to a medium having a composition in the vicinity of the composition of the above-mentioned intermetallic compound, when the composition, the layer construction, the recording method, etc. are properly combined.
Namely, the present inventors have conducted a study from the viewpoint of the applicability to mark length recording using an optical disk evaluation machine suitable for high density recording.
As a result, it has been found that a recording layer comprising, as the main component, a SbTe alloy in the vicinity of the Sb
70
Te
30
eutectic composition has a difficulty only in the initial crystallization, and once it has been initially crystallized, subsequent recording and erasing can be carried out at an extremely high speed.
Further, it has been found that a GeSbTe ternary alloy and an InSbTe ternary alloy having Ge or In added thereto, exhibits excellent repetitive overwriting properties.
Especially in a combination with a certain specific recording pulse pattern, it has a merit such that deterioration during repetitive overwriting is less than the material in the vicinity of a BeTe—Sb
2
Te
3
pseudo-binary alloy or a material in the vicinity of an InGeTe—Sb
2
Te
2
pseudo-binary alloy, which is widely used for repetitive overwriting.
It has been also found that these ternary alloys based on Sb
70
Te
30
have higher crystallization temperatures than the Sb
70
Te
30
binary eutectic alloy and thus are excellent in archival stability.
However, these ternary alloys based on Sb
70
Te
30
had a problem that initialization was more difficult than the Sb
70
Te
30
binary eutectic alloy.
Further, the GeSbTe ternary alloy in the vicinity of the above SbTe eutectic composition had a problem that the recording pulse pattern dependency and the linear velocity dependency were large, and when an usual two level modulation pulse pattern was employed, normal overwriting was possible only within a narrow linear velocity range.
Namely, at a low linear velocity such as 2.8 m/s, recrystallization was so remarkable that formation of amorphous marks tended to be impaired. On the other hand, at a high linear velocity, the crystallization speed was inadequate, and erasing tended to be inadequate. Therefore, proper overwriting was possible only within a limited linear velocity range of 2.8 m/s±50%.
It is an object of the present invention to solve such problems involved in using a material having a composition in the vicinity of such a eutectic composition and to make the application of such a material to a high density optical recording medium possible.
In a first aspect, the present invention provides:
An optical information recording medium having a multilayer structure comprising at least a lower protective layer, a phase-change type optical recording layer, an upper protective layer and a reflective layer, on a s
Horie Michikazu
Ohno Takashi
Angebranndt Martin
Mitsubishi Chemical Corporation
Oblon & Spivak, McClelland, Maier & Neustadt P.C.
LandOfFree
Optical information recording medium and optical recording... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Optical information recording medium and optical recording..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Optical information recording medium and optical recording... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2496325