Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
From carboxylic acid or derivative thereof
528283, 528286, 528309, C08G 6314
Patent
active
042085276
ABSTRACT:
In a process for preparing high molecular weight poly-(ethylene terephthalate) in two stages, comprising, in the first stage, reacting a dialkyl ester of terephthalic acid with ethylene glycol in the presence of 35 to 290 ppm of manganese, in the form of a manganese-II salt effective as a catalyst, together with 6 to 95 ppm of cobalt, in the form of a cobalt-II salt effective as a catalyst, at a temperature of 170.degree. to 220.degree. C. to give a low molecular weight precondensate; then adding 45 to 140 ppm of phosphorus in the form of a phosphorus compound effective to minimize discoloration of the product poly-(ethylene terephthalate) due to said transesterification catalysts; and, in the second stage, effecting complete condensation of the precondensate thus obtained, in the presence of catalysts at a temperature of 270.degree.-290.degree. C. and under low pressure, to give high molecular weight poly-(ethylene terephthalate),
REFERENCES:
patent: 3962189 (1976-08-01), Russin et al.
patent: 4010145 (1977-03-01), Russin et al.
patent: 4119614 (1978-10-01), King et al.
patent: 4128533 (1978-12-01), Kohler et al.
patent: 4128534 (1978-12-01), Kohler et al.
patent: 4133800 (1979-01-01), Taubinger et al.
Burzin Klaus
Feinauer Roland
Horlbeck Gernot
Chemische Werke Huls Aktiengesellschaft
Phynes Lucille M.
LandOfFree
Process for the manufacture of high molecular weight poly-(ethyl does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for the manufacture of high molecular weight poly-(ethyl, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the manufacture of high molecular weight poly-(ethyl will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-475992