Glass fiber forming compositions

Compositions: ceramic – Ceramic compositions – Glass compositions – compositions containing glass other than...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C501S036000, C501S070000

Reexamination Certificate

active

06818575

ABSTRACT:

The present invention relates to glass compositions for making glass fibers, and more particular to glass compositions having lowered liquidus and forming temperatures.
The most common glass composition for making continuous glass fiber strands for textiles and glass fiber reinforcements is “E” glass. The requirements as to what type of composition constitutes an E-glass composition are included in ASTM D578-98. An advantage of using E-glass is that its liquidus temperature is well below its forming temperature, i.e. typically greater than 56° C. (100° F.) and generally between 83 to 111° C. (150 to 200° F.). As used herein, the terms “forming temperature”, “T
FORM
” and “log 3 forming temperature” mean the temperature of the glass at which the viscosity of the glass is log 3, or 1000 poise, and the terms “liquidus temperature” and “T
LIQ
” mean the temperature at which solid phase (crystals) and liquid phase (melt) are in equilibrium. The difference between T
FORM
and T
LIQ
, referred to herein as “delta T” or “&Dgr;T”, is a common measure of the crystallization potential of a given melt composition. In the glass fiber forming industry, &Dgr;T is typically maintained at a temperature of at least 50° C. (90° F.) in order to prevent devitrification of the molten glass during a glass fiber forming operation, and in particular in the bushing area.
Boron and fluorine containing glass were developed to meet these operating conditions. More specifically, the boron and fluorine were included in the glass batch materials to act as fluxes during the glass melting operation. In particular, E-glass can include up to 10 wt % B
2
O
3
and up to 1.0 fluoride (see ASTM D 578-00 §4.2). However, these materials are volatilized during melting and boron and fluorine emissions are released to the atmosphere. Since boron and fluorine are considered pollutants, these emissions are closely controlled by environmental regulations, which in turn requires careful control of the furnace operations and the use of expensive pollution control equipment. In response to this, low boron and/or low fluorine E-glasses were developed. As used herein, “low boron” means that the glass composition is no greater than 5 weight percent (wt %) boron, and includes boron-free glass, and “low fluorine” means that the glass composition is no greater than 0.30 wt % fluorine, and includes fluorine-free glass.
For additional information concerning glass compositions and methods for fiberizing the glass composition, see K. Loewenstein,
The Manufacturing Technology of Continuous Glass Fibres
, (3d Ed. 1993) at pages 30-44, 47-60, 115-122 and 126-135, and F. T. Wallenberger (editor),
Advanced Inorganic Fibers: Processes, Structures, Properties, Applications
, (2000) at pages 81-102 and 129-168, which are hereby incorporated by reference.
Because the actual glass fiber forming operation is conducted at high temperatures, there is high energy usage associated with its production, along with associated high energy costs. In addition, the high temperatures accelerate the degradation of the refractory used in the glass melting furnace, as well as the bushings used to form the fibers. The bushings include precious metals that cannot be recovered from the glass as the bushings corrode. It would be advantageous to produce the glass fibers at the lowest possible forming and liquidus temperatures so as to reduce the energy usage and costs and thermal load on the furnace refractory and bushings, while at the same time provide the &Dgr;T required to ensure an uninterrupted glass fiber forming operation. Reducing the forming and liquidus temperatures of the glass compositions can also result in environmental benefits, such as but not limited to, a reduction in the amount of fuel required to generate the energy necessary for the fiber forming operation, as well as a reduction in the flue gas temperature. In addition, it would be advantageous if the glass compositions are low fluorine and/or low boron compositions so as to reduce or eliminate the environmental pollutants associated with these materials.
The present invention provides a low boron content glass fiber forming composition that has a forming temperature of no greater than 1240° C. (2262° F.), a &Dgr;T of at least 50° C. (90° F.), and a ratio of SiO
2
to RO (i.e. CaO+MgO) of no greater than 2.35. In one nonlimiting embodiment of the present invention, the glass composition has a silica content of no greater than 59 weight percent. In another nonlimiting embodiment of the invention, the glass composition is boron-free.


REFERENCES:
patent: 3600205 (1971-08-01), Breton
patent: 3847626 (1974-11-01), Erickson
patent: 3847627 (1974-11-01), Harsch
patent: 3876481 (1975-04-01), Erickson et al.
patent: 3929497 (1975-12-01), Clark-Monks
patent: 4026715 (1977-05-01), Erickson et al.
patent: 4066466 (1978-01-01), Neely, Jr.
patent: 4166747 (1979-09-01), Neely, Jr.
patent: 4199364 (1980-04-01), Neely
patent: 4542106 (1985-09-01), Sproull
patent: 4628038 (1986-12-01), Weirauch, Jr.
patent: 4882302 (1989-11-01), Horiuchi et al.
patent: 5789329 (1998-08-01), Eastes et al.
patent: 5843854 (1998-12-01), Karppinen et al.
patent: 5962354 (1999-10-01), Fyles et al.
patent: 6136735 (2000-10-01), Gallo et al.
patent: 6686304 (2004-02-01), Wallenberger
patent: 2692248 (1992-06-01), None
patent: 2768144 (1997-09-01), None
patent: 520247 (1940-04-01), None
patent: 1391384 (1975-04-01), None
patent: 10-203845 (1998-08-01), None
patent: 10-231142 (1998-09-01), None
patent: 10-231143 (1998-09-01), None
patent: 2027687 (1995-01-01), None
patent: WO96/39362 (1996-12-01), None
patent: 96/39362 (1996-12-01), None
patent: 98/01932 (1999-02-01), None
patent: WO99/12858 (1999-03-01), None
patent: WO 00/73231 (2000-12-01), None
The Manufacturing Technology of Continuous Glass Fibres, by Loewenstein (3rdEd 1993) pp. 30-44, 47-60, 85-107, 115-122, 126-135.
Advanced Inorganic Fibers: Processes, Structures, Properties, Applications, by Wallenberger et al. (2000); pp. 81-102; 129-168.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Glass fiber forming compositions does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Glass fiber forming compositions, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Glass fiber forming compositions will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3345841

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.