Method of making porous biodegradable polymers

Details Method of making porous biodegradable polymers Method of making porous biodegradable polymers

2001-09-04

2004-01-06

Kuhns, Allan R. (Department: 1732)

Plastic and nonmetallic article shaping or treating: processes

Pore forming in situ

By mechanically introducing gas into material

C264S053000, C521S084100, C521S094000, C521S097000

Reexamination Certificate

active

06673286

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates in general to a method of making porous materials. More particularly, it relates to a method of making porous biodegradable polymers.
2. Description of the Related Arts
Polymeric materials which are both porous and biodegradable are useful in a variety of pharmaceutical applications, such as controlled-release drug delivery systems and surgical implantation. Four major techniques are employed in making porous biodegradable materials: (1) solvent casting/salts leaching; (2) freeze drying (phase separation); (3) emulsion freeze drying; and (4) gas foaming. The first three techniques require excessive quantities of solvent, complicated process, and the operating time is undesirably long. In the last technique, gas forming, a biodegradable polymer is brought into contact with a high-pressure fluid such as CO
2
or N
2
, followed by reducing the pressure in a sharp step to generate void spaces inside a bulk polymer. However, polymers which contain protein structures and hydrogen bonds such as gelatin and collagen are hydrophilic, and it is not easy for the hydrophobic fluid (such as CO
2
) to permeate into these polymer matrices. Therefore, in the current state of the art, the gas foaming technique cannot produce hydrophilic porous materials effectively.
World Patent Application No. WO91/09079 issued to D. P., Roberto et al., discloses a method of preparing a biodegradable porous matrix, which comprises contacting a biodegradable polymer with supercritical carbon dioxide in a chamber and subsequently reducing the pressure in the chamber in a sharp step. A porous spongy material such as poly(glycolic acid) (PGA) or poly(lactide glycolide acid) (PLGA) carrying an active ingredient can be obtained.
As described in
J. Biomed. Mater. Res.,
42, 396 (1998) issued to Harris et al., the supercritical CO
2
foaming technique cannot directly lead to opened-cell morphology. A method combining supercritical CO
2
foaming and leaching techniques is therefore proposed in this article to achieve open-celled biodegradable materials. This method is limited, however, to water-insoluble polymers such as PLGA.
J. Controlled Release,
66, 177-185 (2000) issued to Hill et al., discloses a method in which a PLGA polymer support comprising a protein is prepared by forming an emulsion of PLGA and the protein, placing the emulsion in a high pressure chamber, and then reducing the pressure in the chamber in a sharp step.
J. Biomed. Mater. Res.,
14, 511 (1980) issued to Dagalakis et al., discloses a method of drying porous collagen by supercritical CO
2
, in which the solvent in a collagen solution is first replaced by ethanol, and the ethanol is then removed by supercritical CO
2
extraction. This method requires excessive quantities of solvent and ethanol, and therefore is economically disadvantageous.
SUMMARY OF THE INVENTION
An object of the invention is to provide a method of making porous biodegradable polymers, by which hydrophilic polymers can be foamed in an effective and controllable manner.
To obtain the above object, the present method is characterized by adopting solvent in supercritical fluid processing to help the hydrophobic supercritical fluid to penetrate into hydrophilic polymer, and finally dissolve into the polymer.
The method according to the invention comprises the steps of: (a) placing a biodegradable polymer and a solvent in a chamber; (b) adding a supercritical fluid to the chamber and maintaining the chamber at a predetermined temperature for a sufficient period of time to allow the supercritical fluid to dissolve into the biodegradable polymer with the help of the solvent; (c) venting the supercritical fluid and the solvent by reducing the pressure in the chamber, thereby obtaining the porous biodegradable polymer; and optionally (d) promptly heating the porous biodegradable polymer to increase the porosity thereof.
With the present method, the use of excessive organic solvent can be avoided and the operating time can be reduced. Further, the pore size and morphology of the porous material can be controlled by adjusting the operating pressure and temperature.
DETAILED DESCRIPTION OF THE INVENTION
By supercritical fluid is meant a gas or liquid above its critical point. At the critical point, physical properties of the liquid and gaseous states, in particular the densities, are identical. The temperature and pressure values at the critical point may be termed the critical conditions and are constant for a given fluid. Any supercritical fluid, including carbon dioxide, lower hydrocarbons (hydrocarbons that contain 1 to 8 carbon atoms), refrigerant, nitrogen, and ammonia, may be used in the method of the present invention. Carbon dioxide (CO
2
), at a pressure of at least 7376 kPa and a temperature of at least 31.1° C., is a preferred example.
In operation, the biodegradable polymer is placed in a high pressure chamber or any appropriate device, along with a solvent. After setting the operating temperature, fluid from a cylinder is passed through a pump, which raises the pressure, and then fed into the chamber where it is heated above its critical temperature. Given sufficient time, the supercritical fluid will dissolve into the polymer with the help of the solvent. Thereafter, the pressure inside the chamber is reduced in a sharp step. The sharp pressure reduction contributes towards achieving the desired porosity in the material obtained, and the solvent dissolved in the supercritical fluid can be removed at the same time.
The present method is particularly suited for preparing hydrophilic porous polymers such as gelatin or collagen, but may be used to make hydrophobic porous polymers.
To help hydrophobic fluid (such as CO
2
) dissolve into the hydrophilic polymer, as a key aspect of the invention, a suitable solvent is placed in the high pressure chamber in addition to the biodegradable polymer. The solvent used herein should be able to dissolve the biodegradable polymer to form a single phase, so that it can help the supercritical fluid to dissolve into the polymer. For hydrophilic biodegradable polymers, suitable solvents include diluted acidic solutions, diluted basic solutions, neutral (slat) solutions, solvents that are miscible with water (such as alcohols), or mixtures thereof. The amount of the solvent can be adjusted to modify the porosity of the porous biodegradable polymer. The greater the amount of solvent employed, the higher the porosity of the resulting product, but the longer the time needed for drying the product.
After placing the solvent and the polymer in the chamber, a supercritical fluid is fed into the chamber through a high pressure pump. The chamber is maintained at a predetermined temperature for a sufficient time to allow the supercritical fluid to permeate the biodegradable polymer with the help of the solvent, and finally dissolve the polymer. Thus, a single-phase fluid is formed with the polymer-solvent mixture. The operating time and temperature can also be adjusted to modify the product porosity. The higher the operating temperature of the chamber or the longer the operating time, the higher the porosity achieved. When carbon dioxide is employed as the supercritical fluid, the operating temperature is preferably between about 40° to 150° C., the operating time is preferably between about 5 minutes and 6 hours, and the pressure inside the chamber must be greater than ambient pressure, at about 101.325 kPa (1 atmosphere).
Once this process is complete, the pressure inside the chamber is reduced to a value below the critical pressure of the fluid in a sharp step, typically in a period from 0.1 to 10 seconds. In one embodiment of the invention, the pressure in the chamber is reduced to ambient pressure in the sharp step. The sharp pressure reduction contributes towards achieving the desired porosity in the material obtained, and the solvent dissolved in the supercritical fluid can be removed thereby. However, if the resulting product is found to be moist, it may be des

Affiliated with

Also associated with

Rating

Method of making porous biodegradable polymers does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method of making porous biodegradable polymers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of making porous biodegradable polymers will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3203826