ABSTRACT:
FIELD OF THE INVENTION
This invention relates generally to spin valves. More particularly, it relates to the coupling field of spin valves.
BACKGROUND ART
A spin valve or a magnetoresistive (MR) sensor detects magnetic field signals through the resistance changes of a read element, fabricated of a magnetic material, as a function of the strength and direction of magnetic flux being sensed by the read element. The conventional MR sensor operates on the basis of the anisotropic magnetoresistive (AMR) effect in which a component of the read element resistance varies as the square of the cosine of the angle between the magnetization in the read element and the direction of the flow of sense current through the read element. Such a MR sensor can be used to read data from a magnetic medium. An external magnetic field from the magnetic medium (the signal field) causes a change in the direction of magnetization in the read element, which in turn causes a change in resistance (&Dgr;R/R) in the read element and a corresponding change in the sensed current or voltage.
A spin valve has been identified in which the resistance between two uncoupled ferromagnetic layers varies as the cosine of the angle between the magnetizations of the two layers and is independent of the direction of current flow.
An external magnetic field causes a variation in the relative orientation of the magnetization of neighboring ferromagnetic layers in a spin valve. This in turn causes a change in the spin-dependent scattering of conduction electrons and thus the electrical resistance of the spin valve. The resistance of the spin valve thus changes as the relative alignment of the magnetizations of the ferromagnetic layers changes.
Typically, a conventional simple spin valve comprises a ferromagnetic free layer, a spacer layer, and a single-layer pinned ferromagnetic layer, which is exchange-coupled with an anti-ferromagnetic (AF) layer. In an anti-parallel (AP) pinned spin valve, the single-layer pinned ferromagnetic layer is replaced by a laminated structure comprising at least two ferromagnetic pinned sublayers separated by one or more thin non-ferromagnetic anti-coupling sublayers.
In general, the larger the value of &Dgr;R/R and the smaller coupling the field H
f
, the better the performance of the spin valve. The &Dgr;R/R value of a spin valve conventionally increases as the thickness of the spacer layer decreases due to reduced shunting of the sense current in the spacer layer of the spin valve. For example, a spin valve with a copper spacer layer having a thickness of 28 Å will achieve a &Dgr;R/R of about 5%. If the thickness of copper spacer layer is reduced to 20 Å, a &Dgr;R/R of 8% will be obtained. However, the ferromagnetic coupling field H
f
also increases as the thickness of the spacer layer decreases. In addition, the ferromagnetic coupling field of conventional spin valves is unstable upon annealing cycles. For example, the ferromagnetic coupling field of spin valves changes from about +5 Oe at the beginning of the annealing process to +20 Oe after annealing cycles.
An article entitled “Oxygen as a Surfactant in the Growth of Giant Magnetoresistance Spin Valve” published Dec. 15, 1997 by Journal of Applied Physic to Egelhoff et al. discloses a method for increasing the giant magnetoresistance &Dgr;R/R of Co/Cu spin valves with use of oxygen. In this method, oxygen is introduced in an ultrahigh vacuum deposition chamber with an oxygen partial pressure of 5×10
−9
Torr during deposition of the spin valve layers, or the top copper surface is exposed to the oxygen to achieve an oxygen coverage, after which growth of the sample is completed. The oxygen acts as a surfactant during film growth to suppress defects and to create a surface that scatters electrons more specularly. Oxygen coverage decreases the ferromagnetic coupling between magnetic layers, and decreases the sheet resistance of spin valves.
Unfortunately, this technique requires a very small oxygen partial pressure window around 5×10
−9
Torr, since when the oxygen partial pressure is increased to only 10
−8
Torr, all GMR (&Dgr;R/R) gain due to oxygen is lost, and at oxygen pressures higher than this, the fall-off in GMR is rapid. This very small oxygen partial pressure is very difficult to achieve or to maintain in a large manufacturing type system. Also, oxygen exposure of only one surface of the copper spacer layer does not optimize the ferromagnetic coupling field. Furthermore, the use of oxygen for all spin valve layer depositions may result in oxidation of Mn in anti-ferromagnetic materials, such as FeMn, PtMn, IrMn, PdPtMn and NiMn, and thus kills the spin valve effect. Therefore this technique can not be applied for spin valve deposition.
In addition, adsorbing oxygen only on the copper surface does not improve the GMR, and produces only a positive coupling field. Furthermore, this technique results in decrease in sheet resistance, which reduces the overall signal. Finally, the prior art oxygen treatment does not show stabilization of the ferromagnetic coupling field upon hard bake annealing cycles.
There is a need, therefore, for an improved method of making spin valves that overcomes the above difficulties.
OBJECTS AND ADVANTAGES
Accordingly, it is a primary object of the present invention to provide spin valves with low and stable coupling field H
f
.
It is a further object of the invention to provide spin valves with high magnetoresistive ratio &Dgr;R/R.
It is another object of the invention to develop a process of making spin valves with oxygen partial pressure levels that can be used in manufacturing systems.
It is another object of the invention to develop a process of making spin valves achieving negative coupling fields in production processes.
It is a further object of the invention to develop a process of making spin valves, which does not result in reduction in sheet resistance.
It is another object of the invention to develop a process of making spin valves, which can be used with metallic anti-ferromagnetic materials or in addition to oxide anti-ferromagnetic materials.
It is an additional object of the invention to provide a method of making spin valves having above properties, which can be applied for bottom and top spin valves.
SUMMARY
These objects and advantages are attained by spin valves having a first surface of one ferromagnetic layer and a second surface of a spacer layer, treated with oxygen.
According to a first embodiment of the present invention, a simple spin valve includes a ferromagnetic layer having a first surface, such as a ferromagnetic free layer, and a spacer layer having a second surface. One or more of the first and second surfaces has been treated with oxygen after deposition of the corresponding layer and oxygen treatment has been shut off before depositing a subsequent layer. Treatment with oxygen herein refers to exposing a surface of a layer of material to oxygen after the layer has been deposited. Physisorbed oxygen on these surfaces limits the intermixing between the layers and reduces the surface roughness of these surfaces. As a result, the coupling field is reduced. The obtained coupling field is around −10 Oe for about 20 Å copper, and the coupling field is stable upon hard bake annealing cycles at 232° C. for 11 hours or at 270° C. for 6 hours. Furthermore, the magnetoresistive ratio &Dgr;R/R is enhanced from about 6% to about 9%.
According to a second embodiment of the present invention, a bottom AP-pinned spin valve includes a first surface of a ferromagnetic layer, which is an AP-pinned sublayer, and a second surface of a spacer layer, treated with oxygen. The effect of oxygen surface treatment in AP-pinned spin valves is similar to the effect of oxygen surface treatment in simple spin valve as described in the first embodiment.
A method of making spin valves having surfaces treated with oxygen is described in a third embodiment of the present invention. An ion beam sputtering technique may be used to make the spi
Lumen Intellectual Property Services
Ometz David L.
LandOfFree
Method to achieve low and stable ferromagnetic coupling field does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method to achieve low and stable ferromagnetic coupling field, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method to achieve low and stable ferromagnetic coupling field will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3177476