Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Compositions to be polymerized by wave energy wherein said...
Reexamination Certificate
2001-01-29
2003-01-28
Seidleck, James J. (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Compositions to be polymerized by wave energy wherein said...
C522S150000, C522S182000, C522S178000, C522S113000, C522S114000, C522S121000, C523S105000, C523S111000, C526S317100, C526S314000, C526S319000, C526S320000, C526S321000, C526S323100, C526S931000
Reexamination Certificate
active
06512022
ABSTRACT:
DESCRIPTION
The invention relates to structured polyacrylates crosslinked by selective UV irradiation, to their use, and to a process for preparing them.
In the field of pressure-sensitive adhesive (PSA) compositions, ongoing technological developments in the coating technique mean that there is a progressive need for new developments. Within the industry, hotmelt processes with solventless coating technology are of increasing importance in the preparation of PSA compositions, since the environmental regulations are becoming ever greater and the prices of solvents continue to rise. The consequence of this is that solvents are to be eliminated as far as possible from the manufacturing process for PSA tapes. The associated introduction of the hotmelt technology is imposing ever greater requirements on the adhesive compositions. Acrylic PSA compositions in particular are the subject of very intensive investigations aimed at improvements. For high-level industrial applications, polyacrylates are preferred on account of their transparency and weathering stability. In addition to these advantages, however, these acrylic PSA compositions must also meet stringent requirements in respect of shear strength and bond strength. This profile of requirements is met by polyacrylates of high molecular weight and high polarity with subsequent efficient crosslinking. These high shear strength, polar PSA compositions possess the disadvantage, however, that they are unsuited to the hotmelt extrusion process, because high application temperatures are necessary and because, furthermore, the molecular weight of the polymer is reduced by shearing in the extruder. This damage significantly lowers the level of the adhesive properties. The bond strength and the tack are generally low, since owing to the polar fractions in the adhesive compositions the glass transition temperature is relatively high. The shear strengths of the hotmelt-coated acrylic PSA compositions, in particular, fall distinctly in comparison to the original, solvent-coated PSA composition. At the present time, therefore, different concepts aimed at reducing the flow viscosity and thereby facilitating extrusion coating of these PSA compositions are being investigated.
The industry is pursuing a variety of concepts for achieving this objective. One possibility is the highly efficient crosslinking of a low-viscosity, nonpolar acrylic adhesive composition only when it is on the backing. Acrylates containing electron donating groups are copolymerized and, during crosslinking by UV or EBC (EBC: electron beam curing), they stabilize free radicals that are formed. Examples are tertiary amine monomers [WO96/35725], tertiary butylacrylamide monomer [U.S. Pat. No. 5,194,455], and the tetrahydrofurfuryl acrylates cited and used in EP 0 343 467 B1. A further efficient crosslinking concept is the copolymerization of UV photoinitiators into the polyacrylate chain. For example, benzoin acrylate has been used as a comonomer and the crosslinking has been conducted on the backing using UV light [DE 27 43 979 A1]. In U.S. Pat. No. 5,073,611, on the other hand, benzophenone and acetophenone were used as copolymerizable monomers.
An entirely new method has come from chip manufacture. By adding a photocationic initiator and carrying out irradiation with UV light, polymers containing ester functions are deprotected and free carboxylic acids or hydroxyl functions are generated. This method has been described in U.S. Pat. No. 4,491,628. More recent developments deal with the change in the UV light wavelength to 193 nm [U.S. Pat. No. 5,910,392] and with improving the resolution [U.S. Pat. Nos. 5,861,231; 4,968,581; 4,883,740; 4,810,613; 4,491,628].
It is an object of the invention to provide a polyacrylate whose intermediates in the course of processing feature a low viscosity and thus great ease of processing in the hotmelt process, and which is converted only after processing, e.g., in a hotmelt process, into a composition of high shear strength. Through an appropriate choice of the reaction parameters during the conversion reaction, the intention is that it should be possible to adjust the physical properties of the polymer. The reaction causing the conversion should be able to be conducted when the polymer composition is already present in its ultimate form: for example, applied as an adhesive composition on a backing.
By the introduction of surface structures into the acrylic PSA compositions (introduction of polar alongside nonpolar regions) during UV irradiation, the intention is to obtain an additional improvement in the adhesive properties of the acrylic PSA compositions, a particular intention being to improve the bond strength and the tack in respect of the uniform polyacrylate mixtures. The aim of the invention is therefore to produce hard segments by the UV-initiated deprotection reaction of tert-butyl acrylate to give the free carboxylic acid by means of selective UV irradiation through a mask.
This object is achieved by means of a polyacrylate in accordance with the main claim. The subclaims relate to advantageous developments of the invention and to a process for preparing the polyacrylate, and also to its use.
The invention accordingly provides structured polyacrylates preparable by crosslinking, induced by UV irradiation, of a polymer mixture comprising the following components:
a) polyacrylate copolymers of the following monomers
a1) acrylic acid and/or acrylic esters of the following formula
CH
2
=CH(R
1
)(COOR
2
),
where R
1
=H or CH
3
and R
2
is an alkyl chain having 1-20 carbon atoms, at 70-99% by weight, based on component (a),
a2) olefinically unsaturated monomers containing functional groups, at 0-15% by weight, based on component (a),
a3)tert-butyl acrylate, at 1-15% by weight, based on component (a), and
b) a photocationic initiator at 0.01-25% by weight, based on the overall polymer mixture, the structuring of the polyacrylates comprising the presence in the polyacrylates of regions of high crosslinking alongside regions of low crosslinking and/or noncrosslinked regions.
It is particularly advantageous if component (a1) is present at 85-89% by weight, based on component (a), and/or component (a2) is present at 4-6% by weight, based on component (a), and/or component (a3) is present at 7-9% by weight, based on component (a).
It is very advantageous to use a polymer mixture in which up to 3% by weight, based on the overall polymer mixture, of
c) a difunctional or polyfunctional crosslinker is added.
Crosslinkers which can be used here are all difunctional or polyfunctional compounds whose functional groups are able to enter into a linking reaction with the polyacrylates, especially addition polymerization, polycondensation or polyaddition reactions. Preferably, these reactions will take place on a carboxyl group. Particularly suitable crosslinkers are epoxides or isocyanates containing at least two functional groups, although all other compounds which react with carboxyl groups are also suitable. It is also possible to use metal chelate compounds for this purpose.
A process for preparing structured polyacrylates by structured crosslinking of polyacrylate mixtures comprises irradiating the base polymer mixture with ultraviolet light in such a way that only certain regions of the polymer mixture are exposed to the UV radiation.
The preparation process may in particular be conducted such that the base polymer mixture is irradiated with ultraviolet light through a perforated mask in such a way that only certain regions of the polymer mixture are exposed to the UV radiation.
Alternatively, the structuring of the polymer mixture for curing may be achieved by using, rather than the perforated mask, a film whose two-dimensional extent has regions of different UV light permeability, so that certain regions of the polymer mixture are exposed to different intensities of the UV radiation.
The invention further provides for the use of the polyacrylate as a pressure-sensitive adhesiv
Husemann Marc
Zöllner Stephan
McClendon Sanza L.
Norris McLauglin & Marcus
Seidleck James J.
tesa AG
LandOfFree
Structured UV-crosslinked acrylic pressure-sensitive... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Structured UV-crosslinked acrylic pressure-sensitive..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Structured UV-crosslinked acrylic pressure-sensitive... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3063954